Andriawan, Reno (2018) Pengaruh Wire Feed, Feed Rate Dan Besar Arus Listrik Terhadap Recast Dan Kekerasan Pada Baja Aisi 1045 Menggunakan Wire Edm Pengaruh Wire Feed, Feed Rate Dan Besar Arus Listrik Terhadap Recast Dan Kekerasan Pada Baja Aisi 1045 Menggunakan Wire Edm. Sarjana thesis, Universitas Brawijaya.
Abstract
Electric Discharge Machine merupakan teknologi pemotongan logam non konvensional yang menggunakan energi panas pada proses pemotongannya (thermal cutting processes). Proses EDM adalah proses pengerjaan material oleh sejumlah loncatan bunga api listrik (spark) yang terjadi pada celah di antara katoda (elektroda) dengan anoda (benda kerja). Loncatan bunga api tersebut terjadi secara periodik terhadap waktu. Pada proses permesinan digunakan cairan deionized yang disebut dengan cairan dielektrik yang berada diantara elektroda dan benda kerja. Pergerakan aliran elektron yang menumbuk bagian permukaan benda kerja menyebabkan percikan bunga api yang semakin besar, sehingga terjadi peningkatan temperatur. Dalam kondisi ini akan terjadi pengerosian benda kerja yang akan merubah hasil pemotongan dan berdampak pada kekerasan serta kepresisian hasil pemotongan benda kerja. Oleh karena itu peneliti ini bertujuan untuk mengetahui pengaruh wire feed, feed rate dan arus listrik terhadap recast serta kekerasan baja aisi 1045 pada proses wire EDM. Adapun variabel bebas yang di gunakan adalah variasi dari wire feed 5mm/menit, 7 mm/menit, dan 10 mm/menit dengan arus listrik 5 A, 7 A, 9 A dan feed rate 4,5 mm/s, 6 mm/s dan 9 mm/s. Adapun variabel terikat yang digunakan yaitu recast serta kekerasan pada roda gigi. Hasil dari penelitian ini menunjukkan bahwa semakin meningkat nilai variasi wire feed, feed rate dan arus listrik yang diberikan maka nilai tebal recast serta kekerasan pada roda gigi semakin meningkat. Nilai kekerasan tertinggi didapatkan dari variasi arus 9 ampere dengan feed rate 9 mm/menit dengan ketebalan recast 34 μm nilai kekerasan 342 VHN. Hal ini menunjukan bahwa semakin tinggi nilai arus maka kekerasan lapisan recast yang terbentuk semakin keras. Hal ini dikarenakan dengan semakin tinggi nilai arus mengakibatkan naiknya jumlah energy yang di gunakan untuk memotong benda kerja sehingga jumlah panas yang terjadi dipermukaan semakin tinggi. Hal ini mengakibatkan lapisan material yang mengalami fase austenite semakin besar. Selanjutnya dengan pendinginan cepat dari cairan dielektrik menyebabkan terjadinya transformasi dari austenite menjadi martensit yang semakin banyak. Sehingga mengakibatkan lapisan recast semakin keras.
English Abstract
Electric discharge technology machine is metal cutting non conventional use energy heat on the slaughtering process thermal (cutting processes) .The process of edm is construction materials by a number of a jumper sparks electricity (spark) what happened to crack in between the cathode (electrodes) to anode (workpiece). A jumper sparks there has been periodically against time. At process permesinan used of liquids deionized called with a liquid dielektrik who are among the electrodes and workpiece. The flow of electrons hitting the surface part workpiece causing a spark sparks bigger, so increased temperature. In this condition will happen in erosion objects the working change the results of cutting and give the impact in hardness and precision the results of cutting a workpiece.Hence research aims to understand the influence of wire feeds, feeds rate and electric current to recast and violence steel aisi 1045 to the process wire edm. As for variable free in use is a variant on wire feeds 5mm / minute, 7 mm/minutes, and 10 mm/minutes with an electric current 5 a, 7 a, 9 a and feeds rate 4.5 mm/s, 6 mm/s and 9 mm/s. as for variable bound used namely recast and hardness on a gear wheel.The result of the research indicated that increase value variation wire feeds, feeds rate and a given electrical current this value thick recast and violence on a gear wheel increase. The value of hardness highest was obtained from variations of current 9 ampere with feed rate 9 mm / minutes with a girth recast 34 μm the value of 342 VHN of hardness. This showed that the higher the test scores a current so violence a layer of recast formed getting louder. It was because the with the higher the test scores a current of resulting in increasing number of energy that is in use to cut a workpiece so that the amount of heat that occurred at the surface the higher. This has resulted in a layer of material that experienced the greater the phase of austenite. Next to the rapid cooling of from a liquid of dielectrics causing the occurrence of the transformation of austenite be marten of growing up. So as to lead to a layer of recast getting louder.
| Item Type: | Thesis (Sarjana) |
|---|---|
| Identification Number: | SKR/FT/2018/174/051801637 |
| Uncontrolled Keywords: | Arus listrik, Feed Rate, Recast, Wire EDM , Wire feed dan Kekerasan, Feed rate, Electric current, Hardness, Recast, Wire EDM and Wire feed |
| Subjects: | 600 Technology (Applied sciences) > 621 Applied physics > 621.3 Electrical, magnetic, optical, communications, computer engineering; electronics, lighting > 621.31 Generations, modification, storage, transmission of electric power |
| Divisions: | Fakultas Teknik > Teknik Mesin |
| Depositing User: | Nur Cholis |
| Date Deposited: | 23 Mar 2018 07:07 |
| Last Modified: | 19 Oct 2021 23:00 |
| URI: | http://repository.ub.ac.id/id/eprint/8907 |
Preview |
Text
013 DAFTAR PUSTAKA fix.pdf Download (14kB) | Preview |
Preview |
Text
BAGIAN DEPAN.pdf Download (849kB) | Preview |
Preview |
Text
09 BAB 2 reno.pdf Download (1MB) | Preview |
Preview |
Text
08 BAB 1 reno.pdf Download (102kB) | Preview |
Preview |
Text
10 BAB 3 reno fix.pdf Download (529kB) | Preview |
Preview |
Text
10 BAB 3 reno.pdf Download (529kB) | Preview |
Preview |
Text
11 BAB 4 reno.pdf Download (530kB) | Preview |
Preview |
Text
12 BAB 5 reno fix.pdf Download (90kB) | Preview |
Preview |
Text
014 LAMPIRAN fix.pdf Download (896kB) | Preview |
Actions (login required)
 |
View Item |