Febriyani, Agnesya Ayu (2017) Pengaruh Perlakuan Plasma Nitrogen Pada Permukaan Interlayer Polistiren Terhadap Fungsionalitas Lapisan Stearic Acid Yang Dideposisikan Di Atas Quartz Crystal Microbalance (Qcm). Sarjana thesis, Universitas Brawijaya.
Abstract
Telah dilakukan perlakuan plasma nitrogen terhadap permukaan polistiren dengan variasi pelarut yaitu kloroform, THF, toluen dan xylene yang kemudian dideposisi dengan lapisan tipis stearic acid (SA). Tujuan dari penelitian ini adalah untuk mengetahui pengaruh plasma nitrogen pada fungsionalitas lapisan stearic acid yang dideposisikan di atas QCM terhadap nilai kekasaran, tingkat kebasahan serta kemampuannya dalam immobilisasi protein Bovine Serum Albumin (BSA). Lapisan tipis polistiren dideposisikan dengan menggunakan metode spin coating kemudian dilakukan perlakuan plasma nitrogen selama 2 menit, daya 40 Watt, laju alir gas 20mL/min dan tekanan 0,3 Torr. Kemudian dideposisikan dengan lapisan tipis stearic acid (SA) dengan metode evaporasi vakum selama 60 sekon dan massa 0,01 gram. Sampel dikarakterisasi menggunakan mikroskop optik, TMS-1200 Polytech, sudut kontak dan seperangkat alat immobilisasi. Hasil karakterisasi menunjukkan perbedaan morfologi sampel yang diberi perlakuan plasma. Terjadi peningkatan nilai kekasaran dan sudut kontak permukaan stearic acid pada sampel dengan perlakuan plasma nitrogen. Peningkatan nilai kekasaran paling besar terjadi pada variasi pelarut xylene, dan pada nilai sudut kontak yang terukur sebesar 1020. Dan hasil immobilisasi terbaik dimiliki oleh sampel dengan nilai kekasaran permukaan yang rendah.
English Abstract
Nitrogen plasma treatment on polystyrene surface with different types of solvent namely chloroform, THF, toluene and xylene that deposition with a thin film of stearic acid (SA). The purpose of this research is to know the effect of nitrogen plasma treatment on the functionality of stearic acid surface deposition on QCM about the roughness, the wettability and the ability in the immobilization of Bovine Serum Albumin (BSA) protein. A thin film of polystyrene deposition using spin coating then nitrogen plasma treatment had done for 2 minutes, power 40 Watt, gas flow rate 20 ml/min and pressure 0.3 Torr. Then deposition of stearic acid (SA) thin film with vacuum evaporation method for 60 seconds of deposition and a mass of 0.01 gram. The samples are characterized using an optical microscope, TMS-1200 Polytech, contact angle and an immobilization tool. The result of the characterization show the difference between the morphology of the sample who were given nitrogen plasma treatment. An increase in the value of roughness and the contact angle surface of stearic acid on nitrogen plasma treatment samples. The increase in the value of most of roughness variation solvent xylene, and on the value of the contact angle is measured of 1020. Best immobilization owned by the sampel with low surface roughness value.
| Item Type: | Thesis (Sarjana) |
|---|---|
| Identification Number: | SKR/FMIPA/2017/364/051709705 |
| Uncontrolled Keywords: | polistiren, stearic acid, evaporasi, plasma, kekasaran, tingkat kebasahan, immobilisasi, Bovine Serum Albumin |
| Subjects: | 500 Natural sciences and mathematics > 530 Physics > 530.4 States of matter |
| Divisions: | Fakultas Matematika dan Ilmu Pengetahuan Alam > Fisika |
| Depositing User: | Nur Cholis |
| Date Deposited: | 30 Oct 2017 01:57 |
| Last Modified: | 23 Nov 2021 02:16 |
| URI: | http://repository.ub.ac.id/id/eprint/4521 |
Preview |
Text
skripsi.pdf Download (1MB) | Preview |
Actions (login required)
 |
View Item |