Pengaruh Semen Ground Granulated Blast Furnance Slag (GGBFS) Pada Komposisi Semen Terhadap Kuat Tarik Belah Beton Mutu Tinggi,

Fahrudin, Rizqi and Lilya Susanti, ST., MT. and Indra Waluyohadi, ST., MT., M.Sc (2021) Pengaruh Semen Ground Granulated Blast Furnance Slag (GGBFS) Pada Komposisi Semen Terhadap Kuat Tarik Belah Beton Mutu Tinggi,. Sarjana thesis, Universitas Brawijaya.

Abstract

Saat ini produksi semen meningkat seiring dengan meningkatnya industry konstruksi. Sangat sulit untuk menggantikan semen sebagai bahan utama pembuatan beton. Hal tersebut dapat diminimalisir dengan penggunaan bahan pengganti semen seperti silica fume dan granulated blast furnance slag (ggbfs). Penelitian ini bertujuan untuk mengetahui pengaruh GGBFS terhadap kuat tarik belah beton mutu tinggi tanpa tambahan serta menggunakan tambahan silica fume pada proporsi semen. Bahan yang digunakan dalam penelitian ini antara lain; semen Portland, GGBFS, silica fume, agregat, air, dan superplasticizer. GGBFS yang digunakan dengan variasi 25%, 45%, 55%, dan 65%. Sedangkan silica fume yang digunakan dengan variasi 10% dan 0%. Hasil penelitian ini menunjukkan bahwa pada beton umur 7 hari, dengan nilai kuat tarik belah beton terbesar adalah kadar silika fume 0% yaitu 16,86 MPa dan pada kadar silika fume 10% yaitu 17,37 MPa . Pada umur 14 hari dengan nilai kuat tarik belah beton terbesar adalah kadar silika fume 0% yaitu 16,12 MPa dan pada kadar silika fume 10% yaitu 20,25 MPa. Pada umur 28 hari dengan nilai kuat tarik belah beton terbesar adalah kadar silika fume 0% yaitu 16,69 MPa dan pada kadar silika fume 10% yaitu 24,72 MPa. Pada umur 56 hari dengan nilai kuat tarik belah beton terbesar adalah kadar silika fume 0% yaitu 19,85MPa dan pada kadar silika fume 10% yaitu 20,53 MPa. Pada umur 90 hari dengan nilai kuat tarik belah beton terbesar adalah kadar silika fume 0% yaitu 22,22 MPa dan pada kadar silika fume 10% yaitu 21,27 MPa. Hasil tersebut merupakan hasil nilai kuat tarik belah tertinggi pada masing-masing umur dan variasi silika fume

English Abstract

Currently, cement production is increasing along with the increase in the construction industry. It is very difficult to replace cement as the main ingredient for making concrete. This can be minimized by using cement substitutes such as silica fume and granulated blast furnace slag (ggbfs). This study aims to determine the effect of GGBFS on the split tensile strength of high-strength concrete without additional use of silica fume in the proportion of cement. The materials used in this study include; Portland cement, GGBFS, silica fume, aggregate, water, and superplasticizer. GGBFS is used with variations of 25%, 45%, 55%, and 65%. Meanwhile, silica fume is used with variations of 10% and 0%. The results of this study indicate that in 7-day-old concrete, the greatest value of split tensile strength of concrete is 0% silica fume content of 16.86 MPa and 10% silica fume content of 17.37 MPa. At the age of 14 days with the greatest value of the split tensile strength of concrete is 0% silica fume content, which is 16.12 MPa and at 10% silica fume content, which is 20.25 MPa. At the age of 28 days with the greatest value of the split tensile strength of concrete is 0% silica fume content, which is 16.69 MPa and at 10% silica fume content, which is 24.72 MPa. At the age of 56 days with the greatest value of the split tensile strength of concrete is 0% silica fume content, which is 19.85 MPa and at 10% silica fume content, which is 20.53 MPa. At the age of 90 days with the greatest value of the split tensile strength of concrete is 0% silica fume content, which is 22.22 MPa and at 10% silica fume content, which is 21.27 MPa. These results are the results of the highest split tensile strength values for each age and variation of silica fume.

Other obstract

-

Item Type:	Thesis (Sarjana)
Identification Number:	0521070239
Uncontrolled Keywords:	Kata Kunci : Beton, GGBFS, semen, silika fume
Subjects:	600 Technology (Applied sciences) > 624 Civil engineering
Divisions:	Fakultas Teknik > Teknik Sipil
Depositing User:	yulia Chasanah
Date Deposited:	07 Feb 2022 02:58
Last Modified:	27 Sep 2024 01:41
URI:	http://repository.ub.ac.id/id/eprint/189410

Text Rizqi Fahrudin.pdf Download (2MB)

Actions (login required)

View Item