Yulfiana, Tien (2019) Pengaruh Konsentrasi Garam Prekursor dan Jenis Pelarut terhadap Sintesis Nanokomposit Seng Oksida - Perak (ZnO-Ag) Menggunakan Metode Microwave dengan Bioreduktor Minyak Cengkeh (Syzygium aromaticum L.) dan Uji Aktivitas Antibakterinya terhadap Staphylococcus aureus. Sarjana thesis, Universitas Brawijaya.
Abstract
Sintesis nanokomposit ZnO-Ag menggunakan paparan gelombang mikro dan bioreduktor minyak cengkeh serta uji aktivitas antibakterinya terhadap Staphylococcus aureus telah dilakukan. Proses sintesis dilakukan dengan memvariasikan konsentrasi garam prekursor dan pelarut. Variasi konsentrasi garam prekursor yang digunakan adalah 30:3:0,3 mM untuk Zn(Ac)2.2H2O dan 10:1:0,1 mM untuk AgNO3 dengan jenis pelarut etanol, aseton, dan n-heksana. Produk hasil sintesis dianalisis menggunakan XRD dan SEM-EDS. Hasil XRD dilengkapi dengan intrepetasi data menggunakan software High score plus. Hasil karakterisasi menggunakan XRD menunjukkan bahwa konsentrasi garam prekursor dan jenis pelarut mempengaruhi ukuran kristalit partikel dan intensitas sudut difraksi yang dihasilkan. Semakin besar konsentrasi garam prekursor, maka ukuran kristalit dan intensitas sudut difraksi semakin besar. Semakin polar jenis pelarut, interaksi paparan gelombang mikro semakin besar, sehingga intensitas sudut difraksi tinggi dan ukuran kristalit partikel lebih kecil yaitu sekitar 8,32-82,18 nm. Hasil terbaik pada konsentrasi 3:1 mM dan jenis pelarut etanol menunjukkan terbentuknya masing-masing puncak kristalit Ag, ZnO, dan Zn(OH)2. Hasil SEM-EDS menunjukkan morfologi berupa logam Ag yang tersebar pada permukaan ZnO dengan %massa Zn (45.35%) dan O (36,95%) lebih besar dibandingkan Ag (17,69%). Hasil uji antibakteri nanokomposit terhadap Staphylococcus aureus menunjukkan terdapatnya zona hambatan sebesar 13,8 mm.
English Abstract
The synthesis of ZnO-Ag nanocomposite using microwave exposure, clove oil as bioreductor and its antibacterial activity test against Staphylococcus aureus were carried out. The synthesis is carried out by varying the concentration of salt precursor and type of solvent. The variation of the precursor salt concentration was 30: 3: 0,3 mM for Zn(Ac)2.2H2O and 10: 1: 0,1 mM for AgNO3 with ethanol, acetone, and n-hexane as a solvent. The products were analyzed using XRD and SEM-EDS. XRD results are equipped with data interpretation using the High score plus software. The results showed that the concentration of precursor salt and type of solvent affected the size of particle crystallite and the intensity of the diffraction angle. The greater the concentration of the precursor salt, the greater the size of the crystallite and the intensity of the diffraction angle. At the more polar type of solvent, the interaction of microwave exposure is greater so that the intensity of diffraction angles is high and the crystallite size of particles is smaller, which is around 8,32-82,18 nm. The best result obtained at 3: 1 mM with ethanol solvent showed the formation of each peak crystallite Ag, ZnO, and Zn(OH)2. The result of SEM-EDS showed that ZnO-Ag nanocomposite consisted of metal Ag which spread on the surface of ZnO with a %mass of Zn (45,35%) and O (36,95%) greater than Ag (17,69%). Antibacterial activity test on Staphylococcus aureus toward nanocomposite showed an inhibition zone of 13,8 mm.
Other obstract
-
| Item Type: | Thesis (Sarjana) |
|---|---|
| Identification Number: | SKR/MIPA/2019/448/052001603 |
| Uncontrolled Keywords: | Nanokomposit Seng Oksida-Perak, Minyak cengkeh, gelombang mikro, XRD, SEM-EDS, Uji Antibakteri. Zinc Oxide-Silver nanocomposite, clove oil, microwave, XRD, SEM-EDS, antibacterial |
| Subjects: | 500 Natural sciences and mathematics > 553 Economic geology > 553.6 Other economic materials > 553.63 Salts |
| Divisions: | Fakultas Matematika dan Ilmu Pengetahuan Alam > Kimia |
| Depositing User: | Budi Wahyono Wahyono |
| Date Deposited: | 20 Jul 2020 23:43 |
| Last Modified: | 31 Jul 2020 07:02 |
| URI: | http://repository.ub.ac.id/id/eprint/179344 |
Actions (login required)
 |
View Item |