Fahrizal, Akhmad Fandi (2018) Pengaruh Arah Putaran Tool Terhadap Sifat Mekanik Hasil Sambungan Aluminium Double Side Friction Stir Welding. Sarjana thesis, Universitas Brawijaya.
Abstract
Friction Stir Welding pertama kali dikenalkan oleh The Welding Institute (TWI) pada tahun 1991 di Inggris. Friction Stir Welding merupakan metode pengelasan tanpa melelehkan material (solid-state welding) yang menggunakan tool non-consumable yang berputar sesuai kecepatan spindle dan bergerak melintasi garis pengelasan sesuai dengan feedrate sehingga terjadi penempaan pada pusat lasan. Friction stir welding (FSW) mulai banyak dikembangkan karena dapat menyambungkan material yang kemampuan lasnya rendah (welding ability) seperti aluminium yang memiliki strength weight of rasio lebih bagus dari baja tetapi welding ability rendah dikarenakan kemampuan menghantarkan panas yang baik sehingga panas yang timbul pada proses pengelasan kurang terfokus pada daerah pengelasan. Seiring dengan berkembangannya waktu, FSW berinovasi menjadi Double Side Friction Stir Welding yang digunakan untuk material tebal yang tidak memungkinkan tool untuk melakukan penetrasi kedalam material dan menurukan resiko kegagalan pada tool itu sendiri. DFSW bisa diterapkan dengan menggunakan mesin Double Tool Friction Stir Welding untuk pengelasan sisi ganda simultan, dan juga bisa pada mesin Milling untuk pengelasan sisi ganda non-simultan. Pada penelitian ini menggunakan sambungan butt joint dengan material aluminium dan parameter permesinan dengan kecepatan spindle 1452 rpm dengan feedrate 42 mm/min yang divariasikan dengan arah putaran tool (clockwise – clockwise) dan (clockwise – counter clockwise) yang dikombinasikan dengan panjang tool 2.5 mm, 3.5 mm, 4.5 mm, 5.5 mm dan 6.5 mm. Dari penelitian didapatkan kekuatan tarik hasil sambungan tertinggi didapat dengan menggunakan variasi beda arah putaran tool dengan panjang tool 6.5 mm dengan kekuatan tarik rata – rata sebesar 57.17 MPa. Dan untuk nilai distribusi kekerasannya tertinggi berada pada daerah advancing side dengan panjang tool 6,5 mm dengan arah putaran tool yang berbeda yaitu 90.3 Vicker’s microhardness .
English Abstract
Friction Stir Welding (FSW) first introduced by TWI in 1991 in England. FSW is the welding method without melting the material (solid state welding) who used the non-consumable tool which rotates according to the spindle speed and move across the welding line matching with the federate so that forging occurs at the welding center FSW began to be much developed because it can connect the material who has a poor welding ability such as aluminium which has the strength weight of rasio better than steel however the welding ability is poor because of the ability to deliver the heat was good so the arising heat in the welding process is less focused in the welding area. Along with the development of time, FSW innovates to Double Side Friction Stir Welding who used for thick material that does not allow tool of penetrate into the material and decrease the risk of failure of the tool itself. DFSW can be applied using Double Tool Friction Stir Welding Machine to Simultaneous double-side welding and also on milling universal for non-simultaneos double-sided welding in this research using a butt joint with aluminium material and machining parameters with spindle speed 1452 rpm with federate 42mm/min which is varied with the direction of the tool rotation (clockwice-clockwice) and (clockwice-counter clockwice) which combined with length of tool 2.5mm, 3.5mm, 4.5mm, 5.5mm and 6.5mm with an average tensile strength 57.17 Mpa and for value of the hardness distribution the highest value in the advancing side area with the tool length 6.5mm by using clockwice-counter clockwice is 90.3 vicker’s microhardness.
| Item Type: | Thesis (Sarjana) |
|---|---|
| Identification Number: | SKR/FT/2018/1150/051900100 |
| Uncontrolled Keywords: | Friction Stir Welding, Double Side Friction Stir Welding, Arah Putaran Tool, Sifat Mekanik. Friction Stir Welding, Double Side Friction Stir Welding, Tool Round Direction, Mechanical Properties. |
| Subjects: | 600 Technology (Applied sciences) > 671 Metalworking Processes and primary metal products > 671.5 Joining and cutting of metals > 671.52 Welding |
| Divisions: | Fakultas Teknik > Teknik Mesin |
| Depositing User: | Budi Wahyono Wahyono |
| Date Deposited: | 15 Apr 2019 03:25 |
| Last Modified: | 05 Jul 2022 02:39 |
| URI: | http://repository.ub.ac.id/id/eprint/162736 |
Preview |
Text
Akhmad Fandi Fahrizal.pdf Download (5MB) | Preview |
Actions (login required)
 |
View Item |