Pengaruh Komposisi Fly Ash Terhadap Kuat Tekan Beton Porous Dengan Variasi Komposisi Agregat Kasar Daur Ulang (RCA)

Suseno, Kartika Candra (2017) Pengaruh Komposisi Fly Ash Terhadap Kuat Tekan Beton Porous Dengan Variasi Komposisi Agregat Kasar Daur Ulang (RCA). Sarjana thesis, Universitas Brawijaya.

Abstract

Beton porous adalah beton yang memiliki kemampuan dapat ditembus air dengan mudah atau disebut juga sifat porositas tinggi. Bahan penyusun beton porous terdiri dari campuran semen, air, agregat kasar, dan sedikit agregat halus atau tanpa menggunakan agregat halus. Pada penelitian ini tidak menggunakan agregat halus dan agregat kasar yang digunakan memiliki gradasi seragam. Beton porous memiliki kelemahan yaitu memiliki kuat tekan lebih rendah dibandingkan dengan beton normal. Pemanfaatan fly ash dalam pembuatan beton porous diharapkan mampu meningkatkan kualitas beton porous dari segi kekuatan sedangkan pemanfaatan RCA untuk mengurangi pemanfaatan agregat kasar alam. Kelebihan beton porous adalah mampu menyerap limpasan air permukaan berlebih dengan mudah sehingga dapat meningkatkan kandungan air tanah dan dapat diterapkan pada jenis perkerasan yang menerima beban ringan seperti taman. Pada penelitian ini dilaksanakan pengujian kuat tekan pada beton porous menggunakan benda uji silinder diameter 15 cm dan tinggi 30 cm. Kombinasi campuran yang digunakan yaitu fly ash sebesar 0%, 15%, 25% terhadap semen PPC dan agregat kasar daur ulang (RCA) sebesar 0%, 25%, 50%, 75%, 100%. Jenis fly ash yang digunakan adalah kelas C. Fly ash kelas ini memiliki sifat pozzolan dan cementitious ketika bercampur dengan pasta air semen. Semen yang digunakan adalah Portland Pozzoland Cement (PPC) yang lebih memiliki sifat pozolan. Pengujian beton porous menggunakan alat uji compression testing machine (CTM) yang bertujuan untuk mengetahui hubungan kuat tekan beton porous terhadap komposisi optimal kombinasi fly ash dan agregat kasar daur ulang (RCA). Hasil dari penelitian dari pengujian kuat tekan terhadap beton porous adalah kuat tekan tertinggi diperoleh pada komposisi fly ash 25% dan agregat kasar daur ulang (RCA) 0% dengan nilai sebesar 13,621 MPa. Hubungan antara komposisi fly ash dan agregat kasar daur ulang (RCA) terhadap kuat tekan menunjukkan hasil yang beragam serta pola grafik yang saling silang.

English Abstract

Porous concrete is a concrete that designed to have high porosity forming pores in the concrete and makes water passing through the pores easily. Porous concrete materials are cement, water, coarse aggregate, and small amount of fine aggregate or without using it. Fine aggregate was not used in the experiment while the gradation of coarse aggregates was uniform graded. Porous concrete has some weakness, the compression strength porous concrete is smaller than the normal concrete. Utilization of fly ash for porous concrete is expected to improve the quality of porous concrete in terms of strength meanwhile utilization of RCA to reduce natural coarse aggregate utilization. The benefit of porous concrete is the ability to drain water easily and improve groundwater quantity and can be applied in light load pavement such as parks. In this research cylinder samples with diameter 15 cm and height 30 cm was used. Variations design for this research were combinations of fly ash 0%, 15%, 25% to replace cement PPC and 0%, 25%, 50%, 75%, 100% recycled coarse aggregates (RCA). Class C fly ash was used in this experiment. Class C fly ash is a type of fly ash that has pozzoland and cementitious properties when mixed with cement paste. Pozzolan Portland Cement (PPC) which has pozzoland properties was used in this experiment. Compression testing machine (CTM) was used to investigated the relationship between compression strength porous concrete and the optimum composition of fly ash comSbinations and recycled coarse aggregates (RCA). The porous concrete compression strength research resulted highest compression strength was obtained on the mixed of fly ash composition 25% and 0% recycled coarse aggregate (RCA) with compression strength value was 13,621 MPa. The relationship between the composition of the fly ash and recycled coarse aggregate (RCA) on the compression strength has showed variation results and insignificant trend.

Item Type:	Thesis (Sarjana)
Identification Number:	SKR/FT/2017/503/051705918
Uncontrolled Keywords:	beton porous, fly ash, agregat kasar daur ulang, kuat tekan, komposisi
Subjects:	600 Technology (Applied sciences) > 624 Civil engineering > 624.1 Structural engineering and underground construction > 624.18 Materials > 624.183 Masonry, cermic, allied materials > 624.183 4 Concrete
Divisions:	Fakultas Teknik > Teknik Sipil
Depositing User:	Budi Wahyono Wahyono
Date Deposited:	03 Aug 2017 03:22
Last Modified:	15 Nov 2024 07:05
URI:	http://repository.ub.ac.id/id/eprint/998

Text SKRIPSI - KARTIKA CANDRA SUSENO -135060101111004.pdf Download (8MB)

Actions (login required)

View Item