Pengaruh Variasi Fraksi Serat Kawat Loket Lapis PVC terhadap Kuat Tekan, Kuat Tarik Belah dan Modulus Elastisitas Beton Silinder (Fiber Concrete),

Suwanda, Rizky Anas (2017) Pengaruh Variasi Fraksi Serat Kawat Loket Lapis PVC terhadap Kuat Tekan, Kuat Tarik Belah dan Modulus Elastisitas Beton Silinder (Fiber Concrete),. Sarjana thesis, Universitas Brawijaya.

Abstract

Beton di desain dengan kemampuan dapat memikul beban tekan, tetapi sangat lemah dalam menerima gaya tarik. Kuat tarik yang kecil menyebabkan beton bersifat getas dan dapat menyebabkan keruntuhan mendadak. Penggunaan tulangan baja pada beton bertujuan untuk menahan gaya tarik, tetapi bukan berarti beton tidak mengalami keruntuhan tarik. Retak melintang halus masih sering muncul. Dengan penambahan serat kawat loket lapis PVC yang merupakan bahan lokal, diharapkan dapat memperbaiki kelemahan beton. Variasi fraksi atau presentase serat kawat yang ditambahkan ke dalam campuran beton adalah sebesar 0.5%, 1% dan 1.5% dari volume beton silinder. Selain untuk mengetahui pengaruh serat kawat loket lapis PVC pada campuran beton terhadap kuat tarik, peneliti juga menganalisa pengaruh serat kawat loket lapis PVC terhadap kuat tekan dan modulus elastisitas beton. Pengujian dilakukan pada beton yang telah berumur 28 hari. Pengujian kuat tarik belah dan kuat tekan menggunakan compression machine, sedangkan uji modulus elastisitas menggunakan extensometer. Hasil pengujian kuat tarik belah menunjukkan bahwa nilai kuat tarik maksimum diperoleh pada fraksi serat kawat 1% dengan nilai sebesar ft = 2.439 MPa (meningkat 0.57% dari beton normal), yang artinya kondisi optimum terdapat pada fraksi 1%. Sedangkan hasil pengujian kuat tekan menunjukkan bahwa nilai kuat tekan maksimum diperoleh pada fraksi kawat 1.5% dengan nilai sebesar f’c = 31.68 MPa (menurun 3.7% dari beton normal), yang artinya kuat tekan meningkat seiring dengan bertambahnya fraksi serat, namun jika dibandingkan dengan beton normal, kuat tekan beton serat menurun. Begitu pula dengan hasil uji modulus elastisitas yang menunjukkan bahwa nilai modulus elastisitas maksimum diperoleh pada fraksi kawat 1.5% (menurun 19.4% dari beton normal).

English Abstract

Concrete is designed with the ability to endure compressive strength, however it is very weak if given a tensile force. The weak of concrete’s tensile strength causes it can be brittle and sudden collapse occurs. The use of reinforcing steel on concrete intended to endure tensile strength, but that doesn’t mean the concrete is not collapse. Small transverse cracks still appear frequently. With addition of PVC coated welded wire mesh fiber which is a local material, is expected to improve the concrete weakness. Variations in fraction or percentage of wire fiber added to the concrete mixture are 0.5%, 1% and 1.5% of the concrete volume. In addition to knowing the influence of PVC coated welded wire mesh fiber on concrete mixture to tensile strength, the researchers also analyzed the effect of PVC coated welded wire mesh fiber on compressive strength and modulus elasticity of concrete. Tests were performed on 28-day-old concrete. Tensile strength testing and compressive strength using compression machine, while modulus elasticity test using extensometer. The tensile strength test results showed that the maximum tensile strength was obtained at the wire fraction of 1% with ft = 2,439 MPa (increased by 0.57% from the normal concrete), which means the optimum condition is at 1% fraction. While the compressive strength test results show that the maximum compressive strength is obtained at the wire fraction of 1.5% with f'c = 31.68 MPa (decreased by 3.7% from the normal concrete), which means the compressive strength increases with increasing fiber fraction, but when compared with the normal concrete, compressive strength of concrete fiber decreased. Similarly, the modulus elasticity test results show that the maximum modulus elasticity is obtained at the wire fraction of 1.5% (decreased by 19.4% from the normal concrete).

Item Type:	Thesis (Sarjana)
Identification Number:	SKR/FT/2017/477/051705528
Uncontrolled Keywords:	serat kawat, kawat loket lapis PVC, kuat tarik, kuat tekan, modulus elastisitas
Subjects:	600 Technology (Applied sciences) > 624 Civil engineering > 624.1 Structural engineering and underground construction > 624.18 Materials > 624.183 Masonry, cermic, allied materials > 624.183 4 Concrete
Divisions:	Fakultas Teknik > Teknik Sipil
Depositing User:	Budi Wahyono Wahyono
Date Deposited:	28 Jul 2017 07:50
Last Modified:	15 Nov 2024 02:55
URI:	http://repository.ub.ac.id/id/eprint/796

Text SKRIPSI Rizky Anas Suwanda - 135060101111063.pdf Download (8MB)

Actions (login required)

View Item