Pengaruh Plasma Nitrogen Pada Permukan Interlayer Polistirena Terhadap Fungsionalitas Zinc-Pthalocyanine (Znpc) Yang Dideposisikan Di Atas Quartz Crystal Microbalance (Qcm)

Sukowati, Sri Ageng (2017) Pengaruh Plasma Nitrogen Pada Permukan Interlayer Polistirena Terhadap Fungsionalitas Zinc-Pthalocyanine (Znpc) Yang Dideposisikan Di Atas Quartz Crystal Microbalance (Qcm). Sarjana thesis, Universitas Brawijaya.

Abstract

Pada penelitian ini dilakukan deposisi lapisan Zinc-Pthalocyanine (ZnPc) di atas interlayer polistiren (PS) yang telah dimodifikasi menggunakan teknik plasma nitrogen. Interlayer PS dideposisikan di atas QCM menggunakan teknik spin coating. PS dilarutkan pada empat variasi pelarut, yaitu kloroform (CHCl3), THF (C3H3), toluene (C6H4(CH3)2), dan xilen (C4H8O). Tujuan dari penelitian ini adalah untuk mengetahui fungsionalisasi lapisan ZnPc yang telah dimodifikasi, dengan mengukur nilai ketebalan lapisan, kekasaran, sudut kontak, pengamatan morfologi, dan kemampuannya dalam mengimmobilisasi biomolekul BSA. Plasma nitrogen dipaparkan pada permukaan PS dengan menggunakan parameter daya 40W, tekanan 0,3 Torr, laju alir 20 mL/min, dan waktu 2 min. Parameter plasma yang digunakan mampu menurunkan kekasaran dan sudut kontak permukaan PS. ZnPc dideposisikan dengan menggunakan teknik evaporasi termal dengan parameter waktu vakum 1 jam, tegangan 0,8 V, arus 28A, jarak 3 cm, massa ZnPc 0,005g, dan waktu deposisi 5 menit. Interlayer PS yang dipapar menggunakan plasma nitrogen mampu memodifikasi lapisan ZnPc yang terbentuk. Fungsionalitas lapisan mengalami peningkatan pada seluruh jenis karakterisasi. Peningkatan ketebalan ZnPc yang terbentuk berkisar 22%-295%, dengan peningkatan kekasaran, sudut kontak, dan kemampuan immobilisasi berturut-turut sebesar 10-31nm, 5-11,5o, dan -50%-749%. Peningkatan tertinggi kemampuan immobilisasi lapisan ZnPc diperoleh pada PS pelarut xilen.

English Abstract

Zinc-Pthalocyanine (ZnPc) was deposited on top of polystyrene (PS) interlayer that has been modified using nitrogen plasma treatment. PS was dissolved on various solvents, that are chloroform (CHCl3), THF (C3H3), toluene (C6H4(CH3)2), and xylene (C4H8O). PS was deposited using spin coating method. The aim of the research is to understand the functionalization of ZnPc modified layer, by measuring layer thickness, roughness, contact angle, immobilization ability and morphology obesrvation. Nitrogen plasma was exposed on top PS surface using power 40W, pressure 0.3 Torr, flow rate 20 mL/min, and 2 min time exposure. Nitrogen plasma was effectively reduce the roughness and contact angle of PS surface with range 42-53nm and 32-450. ZnPc was deposited using termal evaporation method using an hour vacuum time, voltage 0.8 V, current 28A, substrat distance 3 cm, ZnPc mass 0.005 g, and 5 minutes deposition time. Ps interlayer that exposured by nitrogen plasma treatment proved can increasing the functionalization of ZnPc film. The functionality of ZnPc layers increased in all of the types of characterization. ZnPc layer thickness increase at range between 22%-295%, followed by the increase of roughness, contact angle , and the immobilization ability in range between 10-31nm, 5-11o, dan -50%-749% respectively.

Item Type: Thesis (Sarjana)
Identification Number: SKR/FMIPA/2017/364/051709704
Uncontrolled Keywords: Zinc-Pthalocyanine (ZnPc), evaporasi termal, plasma nitrogen, polistiren, pelarut
Subjects: 500 Natural sciences and mathematics > 530 Physics
Divisions: Fakultas Matematika dan Ilmu Pengetahuan Alam > Fisika
Depositing User: Nur Cholis
Date Deposited: 30 Oct 2017 01:52
Last Modified: 23 Nov 2021 02:18
URI: http://repository.ub.ac.id/id/eprint/4519
[thumbnail of BAB III.pdf]
Preview
Text
BAB III.pdf

Download (96kB) | Preview
[thumbnail of BAB IV.pdf]
Preview
Text
BAB IV.pdf

Download (816kB) | Preview
[thumbnail of BAB V.pdf]
Preview
Text
BAB V.pdf

Download (124kB) | Preview
[thumbnail of Daftar Pustaka.pdf]
Preview
Text
Daftar Pustaka.pdf

Download (317kB) | Preview
[thumbnail of Bagian Depan.pdf]
Preview
Text
Bagian Depan.pdf

Download (631kB) | Preview
[thumbnail of Lampiran.pdf]
Preview
Text
Lampiran.pdf

Download (1MB) | Preview
[thumbnail of PPT seminar hasil.pdf]
Preview
Text
PPT seminar hasil.pdf

Download (3MB) | Preview
[thumbnail of BAB II.pdf]
Preview
Text
BAB II.pdf

Download (619kB) | Preview
[thumbnail of BAB I.pdf]
Preview
Text
BAB I.pdf

Download (22kB) | Preview

Actions (login required)

View Item View Item