Putri, Hanifa Rahma (2017) Pelapisan Hydrogel SPMA (3-Sulfopropyl Methacrylate Potassium Salt) Pada Permukaan Polipropilen Dengan Metode Grafting Sebagai Upaya Pencegahan Biofouling Mikroalga Spirulina sp. Dan Tetraselmis chuii. Sarjana thesis, Universitas Brawijaya.
Abstract
Biofouling merupakan masalah kompleks yang kerap dihadapi pada berbagai sektor, seperti industri, pelayaran dan filtrasi membran. Biofouling merupakan penumpukan organisme pada suatu substrat, sehingga akan menimbulkan masalah baik secara lingkungan maupun ekonomis. Maka dari itu, diperlukan suatu zat antifouling yag dapat menghambat proses penempelan dari mikroorganisme tersebut. Upaya yang selama ini dilakukan adalah menggunakan bahan kimia, akan tetapi tidak ramah lingkungan. Salah satu zat ramah lingkungan yang dapat dimanfaatkan sebagai antifouling adalah polimer anion hydrogel SPMA (3-Sulfopropyl Methacrylate Potassium Salt). Pada penelitian ini, SPMA akan digrafting pada permukaan polipropilen. Parameter yang diperhatikan diantaranya adalah stabilitas grafting pada kondisi salinitas air laut. Parameter lain adalah banyaknya mikroalga yang menempel di permukaan polipropilen. Hasil yang didapatkan pada penelitian ini dapat membuktikan bahwa SPMA mampu mengurangi fouling yang terjadi akibat mikroalga jenis Spirulina sp. yang memiliki bentuk filamen serta Tetraselmis chuii yang memiliki bentuk oval. Persentase penempelan mikroalga terbesar pada sampel non grafting dari Tetraselmis chuii mencapai 37,49% dan pada sampel grafting sebesar 12,56%. Hasil tersebut menunjukan bahwa Tetraselmis chuii yang memiliki bentuk oval lebih mudah menempel di permukaan sampel dibandingkan dengan Spirulina yang berbentuk filamen.
English Abstract
Biofouling is a serious problem which are often encountered on many sector, like industrial, shipping and membrane filtration. Biofouling is an organism accumulation on substrate surfaces, and it will have an impact on the environment and the economy. So, an antifouling agent may be required to adhere the microorganism. Efforts that have been done is used chemicals, but it is bad for the environment. One of the ecofriendly substance that can be exploited as antifouling is the SPMA (3-Sulfopropyl Methacrylate Potassium Salt) anion hydrogel polymer. In this study, SPMA will grafted in the surface of polypropylene. The parameters to be observed are the stability of grafting under salinity sea water condition. Also see the attachment from microalgae Spirulina sp. and Tetraselmis chuii on polypropylene surfaces. The result obtained in this study can prove that SPMA is able to reduce the fouling that caused from microalgae Spirulina sp. that has a filamentous and Tetraselmis chuii that has an ovale shape. The highest percentage of microalgae attachment from non grafting owned by Tetraselmis chuii samples was 37,49% and from grafting samples, the highest percentage was 12,56%. The result shown the Tetraselmis chuii with an ovale shaped are more easily to adhere on substrate compared with Spirulina sp. that has a filamentous shape.
| Item Type: | Thesis (Sarjana) |
|---|---|
| Identification Number: | SKR/FTP/2017/398/051709245 |
| Uncontrolled Keywords: | Antifouling, Biofouling, Spirulina sp., SPMA, Tetraselmis chuii |
| Subjects: | 600 Technology (Applied sciences) > 630 Agriculture and related technologies |
| Divisions: | Fakultas Teknologi Pertanian > Keteknikan Pertanian |
| Depositing User: | Budi Wahyono Wahyono |
| Date Deposited: | 23 Oct 2017 06:58 |
| Last Modified: | 04 Jan 2022 06:37 |
| URI: | http://repository.ub.ac.id/id/eprint/4202 |
Preview |
Text
Bab I.pdf Download (155kB) | Preview |
Preview |
Text
Bab III.pdf Download (382kB) | Preview |
Preview |
Text
Bab II.pdf Download (573kB) | Preview |
Preview |
Text
Bab IV.pdf Download (2MB) | Preview |
Preview |
Text
DAFTAR PUSTAKA.pdf Download (331kB) | Preview |
Preview |
Text
Bagian Depan.pdf Download (805kB) | Preview |
Preview |
Text
Bab V.pdf Download (8kB) | Preview |
Actions (login required)
 |
View Item |