Pengaruh Soaking Time pada Penggunaan Geopolimer sebagai Coating Agregat Kasar Daur Ulang terhadap Kuat Tekan dan Cepat Rambat Gelombang Beton,

Fadhillah, Muhammad Risydi and u Dr. Eng. Ir. Eva Arifi, ST., MT. (2024) Pengaruh Soaking Time pada Penggunaan Geopolimer sebagai Coating Agregat Kasar Daur Ulang terhadap Kuat Tekan dan Cepat Rambat Gelombang Beton,. Sarjana thesis, Universitas Brawijaya.

Abstract

Campuran dari agregat yang digabungkan dengan semen dan air akan menghasilkan beton. Kadang-kadang, bahan tambahan diberikan untuk mencapai karakteristik tertentu seperti mempermudah proses pengerjaan, meningkatkan daya tahan, dan mengatur waktu pengerasan. Sudah menjadi rahasia umum bahwa beton adalah salah satu material yang paling sering digunakan dalam proyek konstruksi. Beton lebih sering dipilih dibandingkan material lainnya karena memiliki beberapa keunggulan, seperti memiliki kekuatan yang tinggi, Namun, peningkatan kebutuhan beton telah berdampak negatif terhadap lingkungan dalam beberapa tahun terakhir. Menurut International Journal of Science, setidaknya 8% dari emisi global yang disebabkan oleh aktivitas manusia berasal dari pabrik semen. Oleh karena itu, diperlukan solusi tambahan untuk mengatasi permasalahan kualitas penggunaan RCA. Salah satu solusi adalah penggunaan geopolimer sebagai bahan dasar untuk beton daur ulang. Geopolimer merupakan larutan yang memanfaatan bahan alternatif pengganti semen, seperti fly ash, rice husk ash, dan bahan lainnya yang memiliki kandungan tinggi silika dan aluminium. Dengan proses polimerisasi yang ada di dalam geopolimer, penambahan fly ash sebagai coating pada RCA diharapkan dapat menjawab beberapa permasalahan terkait kualitas yang mempengaruhi penggunaan beton daur ulang. Namun, masih ada banyak masalah yang harus diperhatikan secara teliti sehingga perlu melalui beberapa tahap penelitian diantaranya angka kuat tekan dan Cepat Rambat Gelombang beton. Kuat tekan beton merupakan karakteristik beton yang didapatkan dari perbandingan antara beban runtuh yang dapat diterima dengan luas bidang tekan,

English Abstract

A mixture of aggregates combined with cement and water will produce concrete. Sometimes, additives are added to achieve certain characteristics, such as making the work process easier, increasing durability, and regulating the setting time. It is well known that concrete is one of the most frequently used materials in construction projects. Concrete is often chosen over other materials because it has several advantages, such as high strength. However, the increasing demand for concrete has had a negative impact on the environment in recent years. According to the International Journal of Science, at least 8% of global emissions caused by human activities come from cement factories. Therefore, additional solutions are needed to address the quality issues of using RCA (Recycled Concrete Aggregate). One solution is the use of geopolymer as a base material for recycled concrete. Geopolymer is a solution that utilizes alternative materials to replace cement, such as fly ash, rice husk ash, and other materials that have high silica and aluminum content. With the polymerization process in geopolymer, the addition of fly ash as a coating on RCA is expected to address several issues related to the quality affecting the use of recycled concrete. However, there are still many issues that need to be carefully considered, requiring several stages of research, including the compressive strength and wave velocity of the concrete. The compressive strength of concrete is a characteristic obtained from the comparison between the failure load it can withstand and the area of the compressive field

Item Type:	Thesis (Sarjana)
Identification Number:	052407
Uncontrolled Keywords:	beton, geopolimer, fly ash, kuat tekan, cepat rambat gelombang
Divisions:	Fakultas Teknik > Teknik Sipil
Depositing User:	Unnamed user with username nova
Date Deposited:	05 Dec 2024 06:00
Last Modified:	05 Dec 2024 06:00
URI:	http://repository.ub.ac.id/id/eprint/228997

Text (DALAM MASA EMBARGO) MUHAMMAD RISYDI FADHILLAH.pdf Restricted to Registered users only Download (3MB)

Actions (login required)

View Item