Pengaruh Variasi Jenis Daun Pohon Mangga (Mangifera Indica Linn) Terhadap Penurunan Temperatur Ruangan Dengan Menggunakan Proses Coating Pada Atap Galvalum

Asfawi, Mohammad and Dr. Ir. Redi Bintarto, ST., M.Eng.Pract and Ir. Ari Wahjudi, MT. (2024) Pengaruh Variasi Jenis Daun Pohon Mangga (Mangifera Indica Linn) Terhadap Penurunan Temperatur Ruangan Dengan Menggunakan Proses Coating Pada Atap Galvalum. Sarjana thesis, Universitas Brawijaya.

Abstract

Penggunaan baja galvanis sebagai bahan atap bangunan memiliki beberapa kekurangan, salah satunya baja galvanis memiliki nilai konduktivitas termal yang tinggi sehingga dapat meningkatkan temperatur ruangan. Dengan demikian baja galvanis membutuhkan proses coating dengan tujuan dapat menurunkan temperatur ruangan. Proses coating dilakukan menggunakan komposit antara serat daun mangga dan resin epoxy. Penelitian ini bertujuan untuk mngetahui pengaruh variasi jenis daun mangga terhadap penurunan temperatur ruangan dengan proses coating pada atap galvalum. Penelitian ini bertujuan untuk mengeksplorasi dampak penggunaan limbah daun mangga sebagai bahan tambahan pada lapisan komposit atap galvalum terhadap penurunan suhu dalam ruangan. Lapisan tersebut dibuat dengan mencampurkan serat daun mangga dengan resin epoxy menggunakan metode Hand Lay up Coating. Dengan variasi jenis serat daun mangga yang dilakukan pada penelitian ini adalah mangga arumanis (mangifera indica 'arumanis'), mangga manalagi (mangifera indica 'manalagi'), mangga golek (mangifera indica 'golek'), dan mangga kweni (mangifera odorata). Coating pada penelitian ini dibuat dengan komposisi fraksi berat antara serat daun mangga dan epoxy 50%:50%. Pengujian kandungan selulosa menggunakan metode van soest untuk mengetahui kandungan selulosa yang terkandung pada serat daun mangga. Alat uji konduktivitas termal dengan spesimen silinder berukuran diameter 4cm dan tebal 4mm. Kamera digunakan untuk memfoto makro spesimen untuk melihat distribusi persebaran serat daun mangga. Spesimen Uji penurunan temperatur ruangan berukuran 50 cm x 50 cm, spesimen ini akan diletakan dibagian atas alat uji. Uji penurunan temperatur ruangan menggunakan alat berbentuk kubus yang terbuat dari multiplex berukuran 50 cm x 50 cm x 50 cm. Thermocouple diletakan pada box di 4 titik yang berbeda yaitu diatas box, atas permukaan galvalum, bawah permukaan galvalum, dan didalam ruang box. Pengujian dilakukan di Lapangan Rektorat Universitas Brawijaya agar terkena sinar matahari yang optimal dan diuji selama 10 menit. Pada pengujian konduktivitas termal didapatkan nilai terendah pada variasi serat daun mangga kweni yaitu 0,155 W/m.°C dan nilai konduktivitas tertinggi pada variasi serat daun mangga arumanis yaitu 0,525 W/m.°C. Analisis dari foto makroskopik menunjukan bahwa semua variasi komposit serat daun mangga dan epoxy dapat melapisi atap galvalum dengan kerapatan yang sama. Hasil uji penurunan temperatur ruangan didapatkan bahwa serat dengan variasi serat daun mangga kweni memiliki nilai perbedaan temperatur ruangan tertinggi yaitu 2,039°C dan terendah pada variasi serat daun mangga arumanis dengan nilai 0,599°C.

English Abstract

The use of galvanized steel as roofing material has several disadvantages, one of which is that galvanized steel has a high thermal conductivity value, which can increase room temperature. Therefore, galvanized steel requires a coating process aimed at reducing room temperature. The coating process is conducted using a composite of mango leaf fibers and epoxy resin. This study aims to determine the effect of different types of mango leaves on room temperature reduction through the coating process on galvalume roofing. The purpose of this research is to explore the impact of using mango leaf waste as an additive in the composite layer of galvalume roofing on indoor temperature reduction. The layer was created by mixing mango leaf fibers with epoxy resin using the Hand Lay Up Coating method. The variations in mango leaf fibers used in this study are Arumanis mango (Mangifera indica 'Arumanis'), Manalagi mango (Mangifera indica 'Manalagi'), Golek mango (Mangifera indica 'Golek'), and Kweni mango (Mangifera odorata). The coating in this study is made with a weight fraction composition between mango leaf fibers and epoxy of 50%:50%. Cellulose content testing uses the Van Soest method to determine the cellulose content in mango leaf fibers. A thermal conductivity test device with a cylindrical specimen measuring 4 cm in diameter and 4 mm thick is used. A camera is utilized to take macro photographs of the specimens to observe the distribution of mango leaf fibers. The room temperature reduction test specimens measure 50 cm x 50 cm, and these specimens will be placed on top of the test device. The room temperature reduction test uses a cube-shaped device made of multiplex measuring 50 cm x 50 cm x 50 cm. Thermocouples are placed on the box at four different points, namely on top of the box, on the upper surface of the galvalume, below the surface of the galvalume, and inside the box. The testing is conducted at the Rectorate Field of Brawijaya University to ensure optimal exposure to sunlight and tested for 10 minutes. In the thermal conductivity test, the lowest value was obtained for the Kweni mango leaf fiber variation, which is 0.155 W/m.°C, and the highest conductivity value was found in the Arumanis mango leaf fiber variation, which is 0.525 W/m.°C. Analysis of the macroscopic photographs shows that all variations of the mango leaf fiber and epoxy composite can coat the galvalume roofing with the same density. The results of the room temperature reduction test indicate that the Kweni mango leaf fiber variation has the highest room temperature difference value, which is 2.039°C, and the lowest is the Arumanis mango leaf fiber variation with a value of 0.599°C.

Item Type:	Thesis (Sarjana)
Identification Number:	052407
Uncontrolled Keywords:	Atap Galvalum, Serat Daun Mangga, Resin Epoxy, Coating, Konduktivitas Termal, Penurunan Temperatur
Divisions:	Fakultas Teknik > Teknik Mesin
Depositing User:	Unnamed user with username nova
Date Deposited:	03 Dec 2024 06:17
Last Modified:	03 Dec 2024 06:17
URI:	http://repository.ub.ac.id/id/eprint/228848

Text (DALAM MASA EMBARGO) mohammad asfawi.pdf Restricted to Registered users only Download (6MB)

Actions (login required)

View Item