Pengaruh Faktor Air Semen (Fas) Terhadap Kuat Lentur Balok Beton Bertulang Dengan Campuran Ground Granulated Blast Furnace Slag (Ggbfs) 30%

Pinontoan, Frisca Presley and Dr. Eng. Ir. Ming Narto Wijaya, S.T., M.T., M.Sc. and Dr. Eng. Lilya Susanti, S.T., M.T (2024) Pengaruh Faktor Air Semen (Fas) Terhadap Kuat Lentur Balok Beton Bertulang Dengan Campuran Ground Granulated Blast Furnace Slag (Ggbfs) 30%. Sarjana thesis, Universitas Brawijaya.

Abstract

Secara umum, beton yang marak digunakan sebagai bahan utama dalam konstruksi infrastuktur terbuat dari campuran semen, air, agregat kasar, dan agregat halus, serta bisa juga ditambahkan dengan zat aditif sesuai dengan kebutuhannya. Air sebagai salah satu bahan campur adukan mortar berperan penting terhadap kekuatan beton dan biasanya disebut juga sebagai faktor air semen (FAS) dalam campuran adukan mortar. Penggunaan zat aditif dalam adukan mortar yang biasanya ditujukan untuk tujuan tertentu pada umumnya merupakan zat yang memiliki sifat pozzolan yaitu bahan yang mengandung senyawa silika maupun silika alumina yang apabila bereaksi dengan air akan membentuk kalsium hidroksida. Pengujian yang dilaksanakan dalam penelitian ini dilakukan terhadap kuat lentur balok beton bertulang berdimensi 0,15m × 0,20m × 1,0m dengan campuran GGBFS sebanyak 30% sebagai pengganti semen PCC (Portland Composite Cement) dengan variasi berupa faktor air semen (FAS) sebesar 0,3 dan 0,4. Mutu benda uji yang ditetapkan pada penelitian ini disesuaikan dengan penelitian sebelumnya, yaitu sebesar 35 MPa. Pada penelitian ini didapatkan hasil berupa penurunan sebesar 3,01% pada benda uji balok beton bertulang dengan FAS 0,4 dan campuran GGBFS sebanyak 30% dibandingkan dengan benda uji dengan nilai FAS sebesar 0,3 dengan kadar GGBFS yang sama dengan nilai rata�rata kuat lentur sebesar 7,378 MPa dan 7,156 MPa pada usia benda uji 28 hari.

English Abstract

In general, concrete used in infrastructure construction is made from a mixture of cement, water, coarse aggregate and fine aggregate, and additives can also be added according to needs. Water as an ingredient in mortar mixtures plays an important role in the strength of concrete and is usually also referred to as the water cement factor (FAS) in mortar mixtures. The use of additives in mortar mixes which are usually intended for certain purposes are generally substances that have pozzolanic properties, namely materials containing silica compounds or silica alumina which, when reacted with water, will form calcium hydroxide. In this research, tests were carried out on the flexural strength of reinforced concrete beams with dimensions of 0,15m × 0,20m × 1,0m with a mixture of 30% GGBFS as a substitute for PCC cement (Portland Composite Cement) with variations in the form of a water cement factor (W/C) of 0,3 and 0,4. The quality used in the test object was adjusted to previous research, namely 35 MPa. In this study, results were obtained in the form of a decrease of 3,01% in reinforced concrete beam specimens with W/C of 0,4 and a GGBFS mixture of 30% compared to specimens with W/C value of 0,3 with a GGBFS content that was the same as the average value of flexural strength are 7,378 MPa and 7,156 MPa at the age of the test specimen of 28 days.

Item Type:	Thesis (Sarjana)
Identification Number:	0524071244
Uncontrolled Keywords:	Ground Granulated Blast Furnace Slag, GGBFS, Balok Beton Bertulang, Faktor Air Semen, FAS, Kuat Lentur, Kuat Tekan.
Divisions:	Fakultas Teknik > Teknik Sipil
Depositing User:	S Sucipto
Date Deposited:	22 Aug 2024 01:34
Last Modified:	22 Aug 2024 01:34
URI:	http://repository.ub.ac.id/id/eprint/228838

Text (DALAM MASA EMBARGO) Frisca Presley Pinontoan.pdf Restricted to Registered users only Download (4MB)

Actions (login required)

View Item