Kinerja Formulasi Phase Change Material (PCM) Berbahan Dasar Parafin White Oil

Tarik, Ahmad Rayyan and Rini Yulianingsih, STP., MT., Ph. D and Prof. Dr. Eng. Nurkholis Hamidi, S.T., M. Eng. (2024) Kinerja Formulasi Phase Change Material (PCM) Berbahan Dasar Parafin White Oil. Sarjana thesis, Universitas Brawijaya.

Abstract

PCM merupakan material yang memanfaatkan perubahan fasa ketika menyerap (charging) serta melepaskan (discharging) kalor, tetapi struktur maupun susunan kimia tidak berubah. PCM atau phase change material dapat digunakan untuk menyimpan energi dalam bentuk panas kalor. Tujuan penelitian ini yaitu menganalisis perlakuan campuran aquades, span 80, dan parafin terhadap kestabilan, karakteristik fisik, thermal dan uji kinerja pada Phase Change Material (PCM). Penelitian ini menggunakan metode eksperimental dengan melihat pengaruh campuran aquades, parafin white oil, dan span 80 terhadap karakteristik Phase Change Material (PCM). Penelitian ini menggunakan 9 variasi persentase parafin white oil, dan span 80 pada Phase Change Material (PCM). Dari variasi tersebut, data yang diujikan dapat dibandingkan masing-masing karakteristiknya. Pada penelitian ini, menggunakan metode eksperimental dengan melihat pengaruh campuran aquades, parafin white oil, dan span 80 terhadap karakteristik Phase Change Material (PCM). Karakteristik PCM yang diamati pada penelitian ini adalah titik beku, titik lebur, derajat supercooling, panas spesifik, viskositas, creaming index, dan kinerja. Didapatkan hasil dari penelitian titik beku tertinggi ada pada sampel dengan kandungan minyak parafin yang kecil dengan nilai sebesar -15.03 ℃. Selanjutnya untuk titik lebur tertinggi ada pada sampel dengan kandungan minyak parafin yang besar dengan nilai sebesar 5.67 ℃. Selanjutnya pada pengukuran densitas nilai tertinggi terdapat pada sampel dengan kandungan aquades tertinggi dengan nilai sebesar 0.868 g/ml3. Pada pengujian creaming index nilai terbesar ada pada sampel dengan kandungan minyak yang tinggi dengan nilai sebesar 67.79%. Pada pengukuran viskositas nilai terbesar terdapat padasampel yang mengandung minyak sedikit dengan nilai sebesar 97.81 mPa.s. Selanjutnya pada pengujian panas spesifik nilai tertinggi terdapat pada sampel dengan kandungan minyak yang sedikit dengan nilai sebesar 10080 J/Kg.K dan 15120 J/Kg.K. Berdasarkan hasil pengujian kinerja PCM pada freezer didapatkan bahwa sampel M60S3 tidak dapat menghemat daya yang digunakan freezer dengan nilai sebesar - 630.023,68 Joule

English Abstract

PCM is a material that utilizes phase changes when absorbing (charging) and releasing (discharging) heat, but the structure or chemical composition does not change. PCM or phase change material can be used to store energy in the form of heat. The aim of this research is to analyze the treatment of a mixture of distilled water, span 80, and paraffin on stability, physical, thermal characteristics and performance tests on Phase Change Material (PCM). This research uses an experimental method by looking at the effect of a mixture of distilled water, paraffin white oil, and span 80 on the characteristics of Phase Change Material (PCM). This research used 9 variations in the percentage of white paraffin oil, and a span of 80 in Phase Change Material (PCM). From these variations, the data tested can be compared for each characteristic. In this research, we used an experimental method by looking at the effect of a mixture of distilled water, paraffin white oil, and span 80 on the characteristics of Phase Change Material (PCM). The PCM characteristics observed in this research were freezing point, melting point, degree of supercooling, specific heat, viscosity, creaming index, and performance. The research results showed that the highest freezing point was in samples with a small paraffin oil content with a value of -15.03 ℃. Furthermore, the highest melting point was in the sample with a large paraffin oil content with a value of 5.67 ℃. Furthermore, in density measurements, the highest value was found in the sample with the highest distilled water content with a value of 0.868 g/ml3. In the creaming index test, the largest value was in the sample with high oil content with a value of 67.79%. In viscosity measurements, the largest value was found in samples containing little oil with a value of 97.81 mPa.s. Furthermore, in the specific heat test the highest values were found in samples with a small oil content with values of 10080 J/Kg.K and 15120 J/Kg.K. Based on the results of PCM performance testing on the freezer, it was found that the M60S3 sample could not save the power used by the freezer with a value of - 630.023,68 Joules

Item Type:	Thesis (Sarjana)
Identification Number:	0524100240
Uncontrolled Keywords:	Phase Change Material, Cold Storage, span 80, Parafin white oil, Aquades-Phase Change Material, Span 80, White Oil Paraffin, Aquades
Divisions:	Fakultas Teknologi Pertanian > Keteknikan Pertanian
Depositing User:	soegeng sugeng
Date Deposited:	18 Nov 2024 04:20
Last Modified:	18 Nov 2024 04:20
URI:	http://repository.ub.ac.id/id/eprint/228820

Text (DALAM MASA EMBARGO) Ahmad Rayyan Tarik.pdf Restricted to Registered users only Download (4MB)

Actions (login required)

View Item