Ir. Dionysius Joseph Djoko Herry Santjojo, M.Phil., Ph.D and Dr. Eng. Masruroh, M.Sc. (2024) Effect Of Exposure Time On Wettability Using Atmospheric Pressure Plasma Jet On Teflon Surface. Sarjana thesis, Universitas Brawijaya.
Abstract
Dalam beberapa dekade terakhir, Teflon (PTFE) telah banyak digunakan dalam berbagai aspek dikarenakan propertinya lah yang membuat unggul. Penelitian ini terutama difokuskan pada bagaimana interaksi permukaan Teflon yang dilakukan perlakuan dengan plasma jet pada tekanan atmosfer (APPJ). Gas argon sebagai gas yang digunakan dalam eksperimen ini dengan tegangan 3,6KV. Spesies plasma yang dihasilkan dapat diamati dengan Spektrometer Emisi Optik (OES). Setelah proses perlakuan, kebasahan (Wettability) permukaan Teflon diukur. Rentang nilai sudut kontak sebelum perlakuan cukup bervariasi, dengan sudut kontak terendah mencapai 35,4° dan termasuk hidrofilik. Dari eksperimen ini dapat disimpulkan bahwa spesies plasma argon merangsang oksigen kemudian berinteraksi dengan ikatan C − H dalam permukaan Teflon, dan perlakuan ini menyebabkan kehilangan sebagian fluorin dan produksi ikatan C = C. Pada permukaan PTFE, radikal dari lingkungan sekitar, seperti oksigen dan uap air di udara, membentuk radikal karbon (-CH) dan memasukkan gugus-gugus yang mengandung oksigen ke permukaan PTFE.
English Abstract
In recent years Teflon (PTFE) has a lot of use occation in many aspect , its property what makes it superior. In this research mainly focused on how interaction of Teflon surface that treated with Atmospheric -pressure plasma jet (APPJ). Argon gases are used in this experiment followed by roughly approximation of voltage around 3,6KV. Plasma species that produced are observed with Optical Emmision Spectrometer. After the treatment process Teflon surface wettability are measured. The result are intriguing, range of contact angle value after treatment is quite variative with 35,4° as the lowest angle contact and it to be hypdrophilic. From this experiment can be concluded that argon plasma species excite oxygen then interacted with C − H bonds in Teflon surface and this treatment lead to partialy loss of fluorine and production of C = C bonds. On the surface radicals from surrounding environment, such as oxygen and water vapor in the air, forming carbon radicals (-CH) and incorporation of oxygen-containing at the PTFE surface
| Item Type: | Thesis (Sarjana) |
|---|---|
| Identification Number: | 0524090237 |
| Uncontrolled Keywords: | Telfon (PTFE), Atmospheric Pressure-Plasma Jet (APPJ), Spesies plasma, Optical Emmision Spectrometer (OES),Perlakuan permukaan, Kebasahan, Sudut kontak. |
| Divisions: | Fakultas Matematika dan Ilmu Pengetahuan Alam > Fisika |
| Depositing User: | Unnamed user with username nova |
| Date Deposited: | 13 Nov 2024 07:08 |
| Last Modified: | 13 Nov 2024 07:08 |
| URI: | http://repository.ub.ac.id/id/eprint/227971 |
![[thumbnail of DALAM MASA EMBARGO]](http://repository.ub.ac.id/style/images/fileicons/text.png) |
Text (DALAM MASA EMBARGO)
ELSA KRISTIAN C..pdf Restricted to Registered users only Download (2MB) |
Actions (login required)
 |
View Item |