Pengaruh Penambahan Acalypha Indica Leaf Powder Pada Proses Epoxy Coating Terhadap Laju Korosi dan Adhesivitas Coating Pada Baja ASTM A36

Shahir, Abdul Malikul and Ir. Teguh Dwi Widodo, ST., M.Eng., Ph.D and Dr. Ir. Rudianto Raharjo, ST., MT (2024) Pengaruh Penambahan Acalypha Indica Leaf Powder Pada Proses Epoxy Coating Terhadap Laju Korosi dan Adhesivitas Coating Pada Baja ASTM A36. Sarjana thesis, Universitas Brawijaya.

Abstract

Kebutuhan saat ini akan ketahanan korosi semakin meningkat menjadikan lapisan epoksi saja tidak dapat bertahan lama di lingkungan yang korosif. Memodifikasi lapisan epoksi dengan penambahan pigmen ke dalam lapisan epoksi dapat meningkatkan ketahanan korosi dan meningkatkan adhesivitas. Oleh sebab itu, pada penelitian ini penulis menggunakan pelapisan epoksi pada Baja A36 dengan menambahkan partikel berupa Acalypha Indica Leaf Powder sebagai pigmen dengan persentase penambahan fraksi berat TP, 1%, 2%, 3%, 4%, dan 5% yang berperan untuk meningkatkan ketahanan korosi dan meningkatkan adhesivitas. Selain itu, pada penelitian ini menggunakan metode eksperimental. Pada penelitian ini dilakukan pengujian laju korosi dengan metode potentiodynamic polarization menggunakan alat potensiostat PalmSens4. Pada pengujian laju korosi terdapat dua perlakuan yang berbeda spesimen, yaitu spesimen direndam dalam NaCl selama 48 jam dan spesimen direndam dalam NaCl dengan disinari UV selama 48 jam. Kemudian, pada pengujian adhesivitas menggunakan alat adhesion tester PosiTest AT-M. Kemudian, hipotesis diperkuat dengan adanya pengujian pendukung seperti pengujian foto mikrostruktur, pengujian wettability, pengujian scanning electron microscope (SEM), pengujian open circuit potential (OCP), pengujian electrochemical impedance spectroscopy (EIS). Hasil penelitian ini dapat ditarik kesimpulan dengan adanya Acalypha Indica Leaf Powder di dalam lapisan epoksi meningkatkan ketahanan korosi dan adhesivitas coating. Hasil pengujian laju korosi dipengaruhi oleh perlakuan spesimen dan persentase penambahan fraksi berat Acalypha Indica Leaf Powder. Pada spesimen OCP variasi 5% yaitu sebesar 0.001 mm/year, sedangkan spesimen TP yaitu sebesar 0.026 mm/year. Pada spesimen UV variasi 5% yaitu sebesar 0.002 mm/year, sedangkan spesimen TP yaitu sebesar 0.030. Hal tersebut juga didukung dengan pengujian open circuit potential (OCP) dan pengujian electrochemical impedance spectroscopy (EIS) bahwa seiring bertambahnya persentase penambahan fraksi berat akan meningkatkan ketahanan korosi yang semakin baik. Hasil pengujian adhesivitas dipengaruhi oleh variasi persentase penambahan fraksi berat Acalypha Indica Leaf Powder, semakin bertambahnya variasi akan meningkatkan adhesi. Pada spesimen 5% yaitu 10,17 MPa sedangkan spesimen TP yaitu 6,69 MPa

English Abstract

The current need for corrosion resistance is increasing, making epoxy coatings alone unable to last long in corrosive environments. Modifying the epoxy coating by adding pigments into the epoxy coating can improve corrosion resistance and increase adhesivity. Therefore, in this study, the authors used epoxy coating on A36 steel by adding particles in the form of Acalypha Indica Leaf Powder as a pigment with a percentage of weight fraction addition of TP, 1%, 2%, 3%, 4%, and 5% which played a role in improving corrosion resistance and increasing adhesivity. In addition, this research uses experimental methods. In this study, corrosion rate testing was carried out using the potentiodynamic polarization method using the PalmSens4 potentiostat tool. In testing the corrosion rate there are two different treatments of specimens, namely specimens immersed in NaCl for 48 hours and specimens immersed in NaCl with UV irradiation for 48 hours. Then, the adhesivity test uses the PosiTest AT-M adhesion tester. Then, the hypothesis is strengthened by supporting tests such as microstructure photo testing, wettability testing, scanning electron microscope (SEM) testing, open circuit potential (OCP) testing, electrochemical impedance spectroscopy (EIS) testing. The results of this study can be concluded that the presence of Acalypha Indica Leaf Powder in the epoxy coating increases corrosion resistance and coating adhesivity. The results of corrosion rate testing are influenced by specimen treatment and the percentage of addition of Acalypha Indica Leaf Powder weight fraction. In the OCP specimen, the 5% variation is 0.001 mm/year, while the TP specimen is 0.026 mm/year. In the UV specimen, the 5% variation is 0.002 mm/year, while the TP specimen is 0.030. It is also supported by open circuit potential (OCP) testing and electrochemical impedance spectroscopy (EIS) testing that as the percentage of weight fraction addition increases, it will increase the better corrosion resistance. The results of the adhesivity test are influenced by the variation in the percentage of the addition of the weight fraction of Acalypha Indica Leaf Powder, the increasing variation will increase adhesion. The 5% specimen is 10.17 MPa while the TP specimen is 6.69 MPa.

Item Type:	Thesis (Sarjana)
Identification Number:	052407
Uncontrolled Keywords:	Acalypha indica leaf powder, lapisan epoksi, adhesivitas, korosi
Divisions:	Fakultas Teknik > Teknik Mesin
Depositing User:	Unnamed user with username nova
Date Deposited:	08 Nov 2024 03:52
Last Modified:	08 Nov 2024 03:52
URI:	http://repository.ub.ac.id/id/eprint/227481