Karakterisasi Struktur Kristal, Morfologi, dan Energi Gap Nanopartikel ZnO dengan Konsentrasi Dopan Al+Mn Menggunakan Sintesis Metode Kopresipitasi

Yahmin, Ihsan Ramadian and Dr. Heru Harsono, M.Si., and Drs. Ach. Agus Dardiri, M.Si., (2024) Karakterisasi Struktur Kristal, Morfologi, dan Energi Gap Nanopartikel ZnO dengan Konsentrasi Dopan Al+Mn Menggunakan Sintesis Metode Kopresipitasi. Sarjana thesis, Universitas Brawijaya.

Abstract

Nanopartikel Seng Oksida (ZnO) adalah semikonduktor yang menjadi topik menarik dalam penelitian serta pengaplikasiannya. Sintesis nanopartikel Seng Oksida (ZnO) sendiri banyak dilakukan dan banyak metode yang digunakan, salah satunya kopresipitasi yang merubah material bulk menjadi skala nano dengan proses pengendapan. Zn(0,98-x)Al(0,02)Mn(x)O (x = 0, 3, 6, dan 9%) disintesis dengan penambahan Aluminium (Al) dan Mangan (Mn) melalui metode kopresipitasi. Karakterisasi dilakukan meliputi pengukuran XRD, SEM-EDX, dan UV-Vis. Diketahui bahwa fase kristal adalah hexagonal dengan struktur kristal zincite di sampel 0% dan 3% kandungan Mn serta berubah menjadi kristal simonkolleite pada sampel 6% dan 9% kandungan Mn. Hasil ukuran kristal memiliki rentang sebesar 24,095–54,680 nm yang meningkat beriringan dengan bertambahnya konsentrasi kandungan Mn. Bentuk morfologi kristal dengan SEM-EDX adalah kepingan segi enam yang diuji pada sampel 6% kandungan Mn. Karakterisasi dengan UV-Vis didapatkan bahwa celah pita optik menurun dari 3,314–2,417 eV, meningkat pada sampel 3% kandungan Mn dan dan menurun kembali.

English Abstract

Zinc Oxide (ZnO) nanoparticles are semiconductors that are an interesting topic in research and applications. Zinc Oxide (ZnO) synthesis nanoparticles is widely carried out, and many methods are used, one of which is coprecipitation. Coprecipitation changes the bulk material to nanoscale by a precipitation process. Zn(0.98x)Al(0.02)Mn(x)O (x = 0, 3, 6, and 9%) was synthesized by adding Aluminum (Al) and Manganese (Mn) by the coprecipitation method. Characterization was carried out including XRD, SEM-EDX, and UV-Vis measurements. It is known that the crystal phase is hexagonal with a zincite crystal structure in samples of 0% and 3% Mn content and changes to simonkolleite crystals in samples of 6% and 9% Mn content. The resulting crystal size has a range of 24.095–54.680 nm, which increases with increasing Mn concentration. The crystal morphology using SEM-EDX is a pentagonal chip that was tested on a sample with 6% Mn content. Characterization using UV-Vis showed that the optical band gap decreased from 3,314–2,417 eV, increased in samples with 3% Mn content, and decreased again.

Item Type:	Thesis (Sarjana)
Identification Number:	052409
Uncontrolled Keywords:	Nanopartikel, Kopresipitasi, XRD, Morfologi, dan Energi Celah Pita.-Nanoparticles, Coprecipitation, XRD, Morphology, and Band Gap Energy.
Divisions:	Fakultas Matematika dan Ilmu Pengetahuan Alam > Fisika
Depositing User:	Unnamed user with username nova
Date Deposited:	09 Sep 2024 06:47
Last Modified:	09 Sep 2024 06:47
URI:	http://repository.ub.ac.id/id/eprint/225142

Text (DALAM MASA EMBARGO) IHSAN RAMADIAN YAHMIN.pdf Restricted to Registered users only Download (5MB)

Actions (login required)

View Item