Immobilisasi Katalis Asam Klorida dengan Polianilin dan Aplikasi dalam Sintesis Alpha-Terpineol

Pratama, Bimantara Ezza and Prof. Dr. Warsito, MS and Dr. Moh. Farid Rahman, S.Si., M.Si. (2024) Immobilisasi Katalis Asam Klorida dengan Polianilin dan Aplikasi dalam Sintesis Alpha-Terpineol. Sarjana thesis, Universitas Brawijaya.

Abstract

Pembuatan katalis padat polianilin (PANI) melibatkan metode polimerisasi oksidatif, dengan asam klorida (HCl) yang digunakan sebagai bahan dopan, dan kalium persulfat (K2S2O8) sebagai bahan inisiasi radikal. Morfologi permukaan katalis HCl doped PANI dilakukan analisis menggunakan SEM-EDX dan menghasilkan bentuk berupa nanofiber/serat nano. Metode sintesis α-terpineol dengan sonikasi menggunakan ultrasonikator. Pengaplikasian imobilisasi katalis HCl doped PANI dalam sintesis α-terpineol dan pengulangan kembali secara triplo katalis HCl doped PANI. Katalis HCl doped PANI menjalani karakterisasi menggunakan SEM-EDX untuk mengetahui morfologi permukaan katalis yang ter-doping asam HCl dan hasil senyawa sintesis α-terpineol menjalani karakterisasi dengan menggunakan GC-MS dan GC-FID untuk mengetahui senyawa α�terpineol yang dihasilkan lebih optimal. Penentuan validitas senyawa α-terpineol dilakukan menggunakan analisis GC-MS dengan variasi penambahan katalis HCl doped PANI 10%; 15%; dan 20% dan dihasilkan senyawa α-terpineol secara berurut adalah 36,97%; 14,86%; dan 29,19%. Dari ketiga hasil tersebut didapatkan kandungan yang lebih efektif terhadap penambahan jumlah katalis adalah pada penambahan katalis HCl doped PANI 10%, kemudian dilakukan pengulangan kembali secara triplo untuk mengetahui efisiensi katalis tersebut. Penentuan senyawa α-terpineol hasil triplo dianalisis menggunakan GC-FID menghasilkan kandungan adalah 36,97%; 0,667%; dan 1,065%. Penambahan katalis HCl doped PANI dan pengulangan kembali katalis dalam proses sintesis α-terpineol belum menghasilkan kandungan α-terpineol yang belum optimal.

English Abstract

The synthesis of solid polyaniline (PANI) catalyst involves oxidative polymerization method, utilizing hydrochloric acid (HCl) as the dopant material, and potassium persulfate (K2S2O8) as the radical initiation agent. Surface morphology analysis of HCl-doped PANI catalyst was performed using SEM-EDX, revealing nanofiber/nanofiber-like structures. The α-terpineol synthesis method involves sonication using an ultrasonicator. Immobilization of the HCl-doped PANI catalyst was applied in α-terpineol synthesis with a triple repetition of the HCl�doped PANI catalyst. The HCl-doped PANI catalyst underwent SEM�EDX characterization to ascertain the surface morphology of the HCl�doped acid-doped catalyst, while the synthesized α-terpineol compound underwent GC-MS and GC-FID characterization to determine the optimal production of α-terpineol compounds. Validation of the α�terpineol compound was performed using GC-MS analysis with varying additions of HCl-doped PANI catalyst at 10%, 15%, and 20%, resulting in α-terpineol compound contents of 36.97%, 14.86%, and 29.19%, respectively. Among these results, the most effective content increase was observed with the addition of 10% HCl-doped PANI catalyst, followed by triple repetition to determine the catalyst efficiency. Analysis of the tripled α-terpineol compound using GC-FID revealed contents of 36.97%, 0.667%, and 1.065%. The addition of HCl-doped PANI catalyst and its repetition in the α-terpineol synthesis process did not yield optimal α-terpineol content.

Item Type:	Thesis (Sarjana)
Identification Number:	052409
Divisions:	Fakultas Matematika dan Ilmu Pengetahuan Alam > Kimia
Depositing User:	Unnamed user with username nova
Date Deposited:	30 Sep 2024 08:35
Last Modified:	30 Sep 2024 08:35
URI:	http://repository.ub.ac.id/id/eprint/225075

Text (DALAM MASA EMBARGO) Bimantara Ezza Pratama.pdf Restricted to Registered users only Download (2MB)

Actions (login required)

View Item