Pengaruh Variasi Jenis Serat Daun Filum Poaceae Pada Pelapisan Komposit Matrix Epoxy Terhadap Tingkat Penurunan Temperatur Ruangan Pada Atap Galvalum

Firnanda, Tian Putra and Dr. Ir. Redi Bintarto, ST., M.Eng.Pract and Moch. Syamsul Ma’arif, ST., MT. (2024) Pengaruh Variasi Jenis Serat Daun Filum Poaceae Pada Pelapisan Komposit Matrix Epoxy Terhadap Tingkat Penurunan Temperatur Ruangan Pada Atap Galvalum. Sarjana thesis, Universitas Brawijaya.

Abstract

Penelitian ini bertujuan untuk mengeksplorasi dampak penggunaan limbah daun tanaman filum poaceae sebagai bahan tambahan pada lapisan komposit atap galvanis terhadap penurunan suhu dalam ruangan. Lapisan komposit tersebut dibuat dengan mencampurkan serat filum poaceae dengan resin epoxy, menggunakan metode Hand Lay Up Coating. Penelitian ini merupakan studi eksperimental yang menggunakan metode Hand Lay Up Coating, dengan variasi jenis daun poaceae seperti tebu, jagung, bambu, dan padi. Lapisan komposit dibuat dengan cara mengoleskan campuran serat daun poaceae dan resin epoxy menggunakan metode hand lay up coating. Pengujian dilakukan pada sebuah model miniatur rumah berbentuk kubus dari multipleks dengan ukuran 50 cm x 50 cm x 50 cm, dilengkapi dengan ventilasi berukuran 10 cm x 25 cm. Specimen diuji menggunakan sinar matahari, dengan empat sensor termokopel ditempatkan pada posisi yang berbeda 20 cm di atas kotak, di atas atap galvanis, di bawah atap galvanis, dan 10 cm dari dasar kotak. Masing-masing specimen diuji selama 10 menit. Pada pengujian konduktivitas termal, ditemukan bahwa serat daun tebu memiliki nilai tertinggi dengan konduktivitas termal sebesar 0.163 W/m℃, sementara nilai terendahnya tercatat pada serat daun bambu dengan konduktivitas termal 0.223 W/m℃. Analisis menggunakan aplikasi ImageJ menunjukkan bahwa distribusi serat daun tebu adalah yang terbaik. Hasil pengujian penurunan suhu dalam ruangan menunjukkan bahwa perbedaan suhu antara specimen galvalum tanpa lapisan tambahan dan specimen galvalume dengan lapisan terbaik, yaitu serat daun tebu, adalah sebesar 1,86°C, sedangkan perbedaan terendahnya tercatat pada serat daun bambu sebesar 1,25°C.

English Abstract

This research aims to explore the impact of using leaf waste from the Phylum Poaceae plant as an additional material in galvanized roof composite layers on reducing indoor temperature. The composite layer is made by mixing Phylum Poaceae fibers with epoxy resin, using the Hand Lay Up Coating method. This research is an experimental study using the Hand Lay Up Coating method, with various types of poaceae leaves such as sugar cane, corn, bamboo and rice. The composite layer is made by applying a mixture of Poaceae leaf fibers and epoxy resin using the hand lay up coating method. The test was carried out on a miniature model of a cube-shaped house from multiplex with dimensions of 50 cm x 50 cm x 50 cm, equipped with ventilation measuring 10 cm x 25 cm. Specimens were tested using sunlight, with four thermocouple sensors placed in different positions 20 cm above the box, above the galvanized roof, below the galvanized roof, and 10 cm from the bottom of the box. Each specimen was tested for 10 minutes. In the thermal conductivity test, it was found that sugarcane leaf fiber had the highest value with a thermal conductivity of 0.163 W/m℃, while the lowest value was recorded for bamboo leaf fiber with a thermal conductivity of 0.223 W/m℃. Analysis using the ImageJ application shows that the distribution of sugarcane leaf fiber is the best. The results of the indoor temperature reduction test showed that the temperature difference between galvalume specimens without additional layers and galvalume specimens with the best coating, namely sugarcane leaf fiber, was 1.86°C, while the lowest difference was recorded for bamboo leaf fiber at 1.25°C.

Item Type:	Thesis (Sarjana)
Identification Number:	052407
Uncontrolled Keywords:	Serat Daun Filum Poaceae, Filum Poaceae, Komposit, Atap Galvanis, Konduktivitas Termal, Penurunan Temperatur, Temperatur Ruangan-Phylum Poaceae leaf fibre, Phylum Poaceae, Galvanic Roof Composite, Thermal Conductivity, Temperature Drop, Room Temperature
Divisions:	Fakultas Teknik > Teknik Mesin
Depositing User:	Unnamed user with username nova
Date Deposited:	30 Sep 2024 08:34
Last Modified:	30 Sep 2024 08:34
URI:	http://repository.ub.ac.id/id/eprint/225042

Text (DALAM MASA EMBARGO) TIAN PUTRA FIRNANDA.pdf Restricted to Registered users only Download (11MB)

Actions (login required)

View Item