Modifikasi Fotokatalis TiO2 dengan Kurkumin dan SiO2 dari Abu Sekam Padi untuk Penurunan Kadar Pb(II) dalam Air

Bediumasa, Adinda Asa and Dra. Sri Wardhani, M.Si. and Drs. Danar Purwonugroho, M.Si. (2024) Modifikasi Fotokatalis TiO2 dengan Kurkumin dan SiO2 dari Abu Sekam Padi untuk Penurunan Kadar Pb(II) dalam Air. Sarjana thesis, Universitas Brawijaya.

Abstract

Penelitian ini bertujuan untuk mengetahui karakteristik fotokatalis TiO2/Kurkumin-SiO2 menggunakan FTIR, XRD, dan UVVis DRS serta pengaruh penambahan kurkumin dan SiO2 terhadap penurunan kadar Pb(II). Aktivitas fotokatalitik dari fotokatalis TiO2/Kurkumin-SiO2 dilihat berdasarkan pengaruh lama penyinaran dan rasio massa fotokatalis dengan volume limbah dalam mereduksi logam Pb(II) menggunakan sinar tampak dan tanpa penyinaran. SiO2 diekstraksi dari abu sekam padi menggunakan metode pencucian asam dan kurkumin diekstraksi dari bubuk kunyit dengan metode maserasi. Sintesis fotokatalis TiO2-Kurkumin, TiO2-SiO2, dan TiO2/KurkuminSiO2 menggunakan metode impregnasi basah. Uji pengaruh penambahan kurkumin dan SiO2 dilakukan menggunakan sinar UV, sinar tampak, dan tanpa penyinaran selama 2 jam. Uji pengaruh lama penyinaran menggunakan sinar tampak dengan variasi waktu 1, 2, 3, dan 4 jam, sedangkan variasi waktu tanpa penyinaran 1, 2, 3, 4, 5, dan 6 jam. Uji pengaruh rasio massa fotokatalis dengan volume limbah menggunakan rasio 1:2, 2:1, 4:1, 6:1, dan 10:1 mg/mL dengan sinar tampak selama 3 jam dan tanpa penyinaran selama 4 jam. Penambahan kurkumin dan SiO2 dapat menurunkan energi celah pita yang didasarkan pada analisis UV-Vis DRS. Energi celah pita TiO2, TiO2- Kurkumin, dan TiO2/Kurkumin-SiO2 masing-masing 3,6; 2,3; dan 2,0 eV yang terbukti melalui uji aktivitas fotokatalitik pada sinar tampak dapat mereduksi Pb(II) sebesar 96,3%. Lama penyinaran optimum pada sinar tampak selama 3 jam dan tanpa penyinaran selama 4 jam. Rasio massa fotokatalis dengan volume limbah yang optimum pada sinar tampak dan gelap adalah 4:1 mg/mL.

English Abstract

This research aims to determine the characteristics of TiO2/Curcumin-SiO2 photocatalyst using FTIR, XRD, and UV-Vis DRS as well as the effect of the addition of curcumin and SiO2 on the reduction of Pb(II) levels. The photocatalytic activity of the TiO2/Curcumin-SiO2 photocatalyst is seen based on the effect of irradiation duration and the ratio of photocatalyst mass to waste volume in reducing Pb(II) metal using visible light and without irradiation. SiO2 was extracted from rice husk ash using acid leaching method and curcumin was extracted from turmeric powder using maceration method. Synthesis of TiO2-Curcumin, TiO2-SiO2, and TiO2/CurcuminSiO2 photocatalysts used wet impregnation method. Tests of the effect of the addition of curcumin and SiO2 were carried out using UV light, visible light, and without irradiation for 2 hours. Test the effect of the length of irradiation used visible light with a time variation of 1, 2, 3, and 4 hours, while the time variation without irradiation is 1, 2, 3, 4, 5, and 6 hours. Test the effect of the ratio of photocatalyst mass to waste volume used a ratio of 1:2, 2:1, 4:1, 6:1, and 10:1 mg/mL with visible light for 3 hours and without irradiation for 4 hours. The addition of curcumin and SiO2 can reduce the band gap energy based on UV-Vis DRS analysis. The band gap energy of TiO2, TiO2-Curcumin, and TiO2/Curcumin-SiO2 are respectively 3.6; 2.3; and 2.0 eV which is proven through photocatalytic activity tests in visible light can reduce Pb(II) by 96.3%. Optimum irradiation time in visible light is for 3 hours and without irradiation is for 4 hours. The optimum ratio of photocatalyst mass to waste volume in visible light and dark is 4:1 mg/mL.

Item Type:	Thesis (Sarjana)
Identification Number:	0524090202
Uncontrolled Keywords:	photocatalyst, TiO2, curcumin, SiO2, Pb(II)
Divisions:	Fakultas Matematika dan Ilmu Pengetahuan Alam > Kimia
Depositing User:	Unnamed user with username nova
Date Deposited:	27 Aug 2024 06:47
Last Modified:	27 Aug 2024 06:47
URI:	http://repository.ub.ac.id/id/eprint/224688

Text (DALAM MASA EMBARGO) Adinda Asa Bediumasa.pdf Restricted to Registered users only Download (7MB)

Actions (login required)

View Item