Pengaruh Soaking Time pada Penggunaan Geopolimer sebagai Coating untuk Meningkatkan Kualitas Agregat Kasar Daur Ulang

Wasesa, Dimas Tegar Bayu and Dr. Eng. Ir. Eva Arifi, S.T., M.T., IPM. and Ir. Indra Waluyohadi, ST., MT., M.Sc. (2024) Pengaruh Soaking Time pada Penggunaan Geopolimer sebagai Coating untuk Meningkatkan Kualitas Agregat Kasar Daur Ulang. Sarjana thesis, Universitas Brawijaya.

Abstract

Bahan konstruksi daur ulang, khususnya agregat, telah mendapat perhatian selama beberapa dekade terakhir untuk mengatasi kekurangan agregat dan mendorong beton berkelanjutan dan ramah lingkungan. Namun demikian, penggunaan recycled coarse aggregate (RCA) pada tingkat penggantian penuh dapat menyebabkan penurunan karakteristik segar, mekanis, dan daya tahan dibandingkan dengan beton yang diproduksi dengan bahan Natural Coarse Aggregates (NCA). Untuk dapat meminimalkan dampak negatif kelemahan RCA, penggunaan geopolimer bisa menjadi salah satu jalan keluar. Geopolimer akan digunakan sebagai bahan pelapis permukaan pada RCA, yang diharapkan mampu menekan kelemahan RCA itu sendiri. Geopolimer terbuat dari bahan organik dengan proses polimerisasi. Dalam penelitian ini dibahas pengaruh soaking time pada saat coating agregat kasar daur ulang. Lama waktu perendamaan atau soaking time yang ditentukan yaitu 5 menit dan 10 menit. Agregat kasar daur ulang untuk variasi soaking time 5 menit memiliki hasil yang paling optimal, dimana dibuktikan dengan meningkatnya berat isi dan penurunan nilai penyerapan yang dimiliki RCA sebelum dan setelah dilakukan coating, serta nilai hasil pengujian aggregate crushing value (ACV). Pada agregat kasar daur ulang untuk variasi soaking time 5 menit geopolimer menyerap secara optimal dan mengalami pengeringan yang sempurna, sedangkan untuk waktu 10 menit geopolimer mengalami penyerapan yang berlebih dan dapat pudar saat dilakukan pengujian, hal ini dapat dilihat dari hasil scanning electron microscope (SEM). Penulis menyarankan untuk menggunakan RCA dari sumber beton dengan bahan dan mutu yang sama agar dapat menghasilkan perbandingan yang lebih efektif dan akurat.

English Abstract

Recycled construction materials, especially aggregates, have attracted attention in recent decades to address aggregate shortages and promote sustainable and eco-friendly concrete practices. However, fully replacing Natural Coarse Aggregates (NCA) with recycled coarse aggregate (RCA) can diminish the fresh, mechanical, and durability characteristics c to concrete made with NCA. To mitigate these negative impacts of RCA, the application of geopolymers presents a potential solution. Geopolymers are utilized as surface coatings on RCA, aimed at alleviating RCA's inherent weaknesses. Geopolymers are synthesized from organic natural materials through a polymerization process. This research explores the impact of soaking time during the coating of recycled coarse aggregates, with designated soaking times of 5 minutes and 10 minutes. Recycled coarse aggregate subjected to a 5-minute soaking time demonstrates optimal outcomes, indicated by increased bulk density and reduced water absorption values of RCA before and after coating, as well as results from the aggregate crushing value (ACV) test. Geopolymers exhibit optimal absorption and thorough drying with a 5-minute soaking time, whereas a 10-minute soaking time shows excessive absorption and potential fading during testing, as observed in scanning electron microscope (SEM) analyses. The author suggests using recycled coarse aggregate sourced from concrete materials with identical compositions and quality to ensure more effective and precise comparisons.

Item Type:	Thesis (Sarjana)
Identification Number:	052407
Uncontrolled Keywords:	recycled coarse aggregate, geopolimer, soaking time, aggregate crushing value, scanning electron microscope. -recycled coarse aggregate, geopolymer, soaking time, aggregate crushing value, scanning electron microscope.
Divisions:	Fakultas Teknik > Teknik Sipil
Depositing User:	Unnamed user with username nova
Date Deposited:	27 Aug 2024 06:44
Last Modified:	27 Aug 2024 06:44
URI:	http://repository.ub.ac.id/id/eprint/224628

Text (DALAM MASA EMBARGO) Dimas Tegar Bayu Wasesa.pdf Restricted to Registered users only Download (5MB)

Actions (login required)

View Item