Pengaruh Penggunaan RCA yang telah diperbaiki oleh Bakteri Micrococcus luteus dengan Penambahan Kadar Glukosa terhadap Kuat Tekan dan Modulus Elastisitas Beton

Prasetyo, Bimo Putra Tri and Dr. Eng. Ir. Eva Arifi, S.T., M.T., IPM. and Ir. Indra Waluyohadi, ST., MT., M.Sc., IPM (2024) Pengaruh Penggunaan RCA yang telah diperbaiki oleh Bakteri Micrococcus luteus dengan Penambahan Kadar Glukosa terhadap Kuat Tekan dan Modulus Elastisitas Beton. Sarjana thesis, Universitas Brawijaya.

Abstract

Meningkatkan pembangunan infrastruktur untuk mendukung kemajuan ekonomi menyebabkan peningkatan permintaan akan beton sebagai bahan konstruksi. Meningkatnya penggunaan beton mengakibatkan limbah beton yang makin bertambah. Penggunaan kembali limbah beton sebagai Recycled Coarse Aggregate (RCA) telah menjadi solusi yang berkelanjutan dalam industri konstruksi. Meskipun demikian, kualitas RCA memengaruhi kualitas beton yang dihasilkan, sehingga diperlukan metode perbaikan seperti metode biodeposisi untuk meningkatkan kualitasnya. Metode biodeposisi merupakan kemampuan bakteri micrococcus luteus untuk menghasilkan pengendapan CaCO3. Kadar glukosa yang dipakai dalam studi ini, yaitu 0,1%; 0,2%; dan 0,3%. Penambahan kadar glukosa juga dipakai sebagai sumber karbon dipakai untuk menginduksi bakteri dalam menghasilkan eksopolisakarida. Kemudian, pengujian kuat tekan dan modulus elastisitas dilaksanakan ketika umur beton mencapai 28 hari dengan memakai compression testing machine (CTM) dan extensometer. Beton dengan variasi RCA-0,1% yang merupakan RCA yang telah diperbaiki dengan penambahan kadar glukosa sebanyak 0,1% memiliki hasil kuat tekan dan modulus elastisitas yang lebih tinggi dibandingkan dengan beton variasi lain. Hal ini menunjukkan jika makin tinggi kadar glukosa yang ditambah di larutan bakteri maka akan makin mengurangi nilai kuat tekan beton. Penambahan kadar glukosa yang makin tinggi juga akan mengganggu proses dari pengendapan kalsium karbonat karena akan meningkatkan kadar eksopolisakarida yang akan mengikat ikatan ion kalsium. Penulis menyaranakan untuk menggunakan RCA dari kondisi dan sumber yang sama agar data yang dihasilkan lebih akurat serta menambahkan pembahasan mengenai analisis biaya untuk membandingkan efisiensi dengan penggunaan agregat kasar alami.

English Abstract

The increasing development of infrastructure to support economic progress has led to a rising demand for concrete as a construction material. This increased use of concrete results in a growing amount of concrete waste. Reusing concrete waste as Recycled Coarse Aggregate (RCA) has become a sustainable solution in the construction industry. However, the quality of RCA significantly affects the quality of the resulting concrete, necessitating improvement methods such as bio-deposition to enhance its quality. Biodeposition involves the ability of the Micrococcus luteus bacteria to CaCO3 precipitate. Glucose concentrations used in this study were 0.1%, 0.2%, and 0.3%. The addition of glucose also serves as a carbon source to induce bacteria to produce exopolysaccharides. Compressive strength and elastic modulus tests were conducted at 28 days using a compression testing machine (CTM) and an extensometer. Concrete with RCA-0.1%, which had been treated with a 0.1% glucose solution, exhibited higher compressive strength and modulus of elasticity compared to other concrete variations. This indicates that higher glucose concentrations added to the bacterial solution reduce the compressive strength of the concrete. Increasing glucose concentrations also disrupt the calcium carbonate deposition process by elevating exopolysaccharide levels that bind calcium ions. The author recommends using RCA from consistent conditions and sources to ensure accurate data and suggests including cost analysis to compare efficiency with natural coarse aggregates.

Item Type:	Thesis (Sarjana)
Identification Number:	052407
Uncontrolled Keywords:	recycled coarse aggregate, bakteri micrococcus luteus, glukosa, presipitasi kalsium karbonat, kuat tekan, modulus elastisitas-recycled coarse aggregate, micrococcus luteus bacteria, glucose, calcium carbonate precipitation, compressive strength, elastic modulus
Divisions:	Fakultas Teknik > Teknik Sipil
Depositing User:	Unnamed user with username nova
Date Deposited:	27 Aug 2024 06:37
Last Modified:	27 Aug 2024 06:37
URI:	http://repository.ub.ac.id/id/eprint/224593

Text (DALAM MASA EMBARGO) Bimo Prasetyo.pdf Restricted to Registered users only Download (2MB)

Actions (login required)

View Item