Ramadhani, Adrian Ahmad and Dr. Ir. Redi Bintarto, ST., M.Eng.Pract. and Moch. Syamsul Ma’arif, ST., MT. (2024) Pengaruh Variasi Jenis Daun Filum Arecaceae pada Pelapisan Komposit Matriks Epoksi Terhadap Penurunan Temperatur pada Atap Galvalum. Sarjana thesis, Universitas Brawijaya.
Abstract
Penelitian ini bertujuan untuk mengetahui pengaruh limbah daun tanaman filum arecaceae sebagai lapisan komposit penyerap panas atap galvanis terhadap penurunan temperatur ruangan. Lapisan komposit pada atap galvanis menggunakan campuran serat filum arecaceae dan resin epoxy. Penelitian ini merupakan penelitian experimental nyata yang menggunakan metode Hand Lay Up Coating. Dengan variasi daun filum arecaceae yang digunakan adalah daun enau atau aren (Arenga pinnata), kelapa (Cocos nucifera), salak (Salacca Zalacca) dan palem manila (Adonidia Merrilli). Lapisan komposit pada penelitian ini dibuat dengan mengoleskan campuran serat daun arecaceae dan resin epoxy menggunakan metode hand lay up coating. Pengujian dilakukan dengan menggunakan alat uji menyerupai miniatur rumah berbentuk kubus yang dibuat dengan multipleks ukuran 50 cm x 50 cm x 50 cm dan terdapat ventilasi dengan ukuran 10 cm x 25 cm. Pengujian specimen dilakukan dengan memanfaatkan sinar matahari dimana pada pengujian digunakan 4 sensor termokopel pada titik yang berbeda, yaitu pada 20 cm diatas kotak; diatas atap galvanis; dibawah atap galvanis; dan 10 cm dari dasar kotak. Setiap specimen diuji selama 10 menit. Pada pengujian konduktivitas termal, didapatkan nilai tertinggi yakni serat daun aren dengan nilai konduktivitas termal 0.191W/m℃ dan nilai konduktivitas termal terendahnya pada serat daun salak dengan nilai 0.148 W/m℃. Analisis yang dilakukan menggunakan aplikasi ImageJ menunjukkan bahwa serat daun salak memiliki persebaran serat paling baik. Hasil pengujian penurunan temperature didapatkan bahwa nilai perbedaan temperature dalam ruangan specimen galvalum tanpa coating dengan specimen galvalume coating terbaik dalah serat daun salak dengan perbedaan suhu sebesar 1,177°C dan terendah pada serat daun aren dengan perbedaan suhu sebesar 0,351°C.
English Abstract
This study aims to determine the effect of leaf waste of the Arecaceae phylum as a composite layer that absorbs heat from galvanized roof against decreasing temperature room. The composite layer on the galvanized roof uses a mixture of Arecaceae phylum fibers and epoxy resin. This research is real experimental research that uses methods Hand Lay Up Coating. With variations of the leaf of the Arecaceae phylum used are palm leaves or sugar palm (Arenga pinnata), coconut (Cocos nucifera), salak (Salacca Zalacca) and manila palm (Adonidia Merrilli). The composite layer in this study was made with applying a mixture of arecaceae leaf fibers and epoxy resin using the hand lay method up coating. Testing is carried out using a test tool resembling a miniature house cube-shaped which is made with a multiplex size of 50 cm x 50 cm x 50 cm and there are ventilation with a size of 10 cm x 25 cm. Specimen testing is done by utilizing sunlight where using 4 thermocouple sensors were used at the same point different, namely at 20 cm above the box; on a galvanized roof; under galvanized roof; and 10 cm from the bottom of the box. Each specimen was tested for 10 minutes. In the thermal conductivity test, the highest value was obtained by sugar palm leaf fiber with a thermal conductivity value of 0.191W/m℃ and the lowest thermal conductivity value was salak leaf fiber with a value of 0.148 W/m℃. Analysis carried out using the ImageJ application showed that salak leaf fiber had the best fiber distribution. The results of the temperature reduction test showed that the value of the temperature difference in the room between uncoated galvalume specimens and the best coated galvalume specimens was salak leaf fiber with a temperature difference of 1.177°C and the lowest was sugar palm leaf fiber with a temperature difference of 0.351°C.
| Item Type: | Thesis (Sarjana) |
|---|---|
| Identification Number: | 052407 |
| Uncontrolled Keywords: | Serat Daun Filum Arecaceae, Filum Arecaceae, Komposit, Atap Galvanis, Konduktivitas Termal, Penurunan Temperatur, Temperatur Ruangan-Phylum Arecaceae leaf fibre, Phylum Arecaceae, Galvanic Roof Composite, Thermal Conductivity, Temperature Drop, Room Temperature |
| Divisions: | Fakultas Teknik > Teknik Mesin |
| Depositing User: | Unnamed user with username nova |
| Date Deposited: | 23 Aug 2024 06:22 |
| Last Modified: | 23 Aug 2024 06:22 |
| URI: | http://repository.ub.ac.id/id/eprint/224470 |
![[thumbnail of DALAM MASA EMBARGO]](http://repository.ub.ac.id/style/images/fileicons/text.png) |
Text (DALAM MASA EMBARGO)
ADRIAN AHMAD RAMADHANI.pdf Restricted to Registered users only Download (13MB) |
Actions (login required)
 |
View Item |