Syaifuddin, Abdullah and Dr. Ir. Redi Bintarto, ST., M.Eng.Pract. and Moch. Syamsul Ma’arif, ST., MT. (2024) Pengaruh Variasi Jenis Serat Bambu Pada Pelapisan Komposit Matrix Epoxy Terhadap Tingkat Penurunan Temperatur Ruangan Pada Atap Galvalum. Sarjana thesis, Universitas Brawijaya.
Abstract
Penelitian ini bertujuan untuk mengetahui pengaruh variasi jenis serat bambu sebagai lapisan komposit penyerap panas atap galvalum terhadap penurunan temperatur ruangan. Lapisan komposit pada atap galvalum menggunakan campuran serat bambu dan resin epoxy. Penelitian ini merupakan penelitian experimental nyata yang menggunakan metode Hand Lay Up Coating. Dengan variasi jenis serat bambu yang digunakan yaitu serat bambu apus (Gigantochloa apus), bambu betung (Dendrocalamus asper), bambu ori (Bambusa blumeana), dan bambu wulung (Gigantochloa atroviolacea). Lapisan komposit pada penelitian ini dibuat dengan mengoleskan campuran serat bambu dan resin epoxy menggunakan metode hand lay up coating. Uji penurunan temperatur ruangan menggunakan alat berbentuk kubus yang terbuat dari multiplex berukuran 50 cm x 50 cm x 50 cm. Thermocouple diletakan pada kubus di 4 titik yang berbeda yaitu atas kubus, atas permukaan galvalum, bawah permukaan galvalum, dan di dalam ruang kubus. Pengujian dilakukan di area terbuka supaya terkena sinar matahari dan diuji selama 10 menit. Pada pengujian konduktivitas termal didapat nilai tertinggi pada spesimen galvalum coating serat bambu wulung dengan nilai konduktivitas termalnya 0,244230 W/m.℃ dan nilai konduktivitas termal terendahnya pada spesimen galvalum coating serat bambu apus dengan nilai 0,188406 W/m.℃. Analisis secara visual dari foto makroskopik memperlihatkan bahwa spesimen galvalum coating serat bambu wulung memiliki persebaran serbuk paling baik. Hasil pengujian penurunan temperatur didapatkan bahwa nilai perbedaan temperatur (ΔT) dalam ruangan spesimen galvalum tanpa coating dengan spesimen galvalum coating terbaik adalah spesimen galvalum coating serat bambu apus dengan beda suhu sebesar 1,978°C dan terendah pada spesimen galvalum coating serat bambu wulung dengan beda suhu sebesar 1,735°C.
English Abstract
This study aims to determine the effect of variations in the type of bamboo fiber as a heat-absorbing composite layer of galvalume roof on reducing room temperature. The composite layer on the galvalume roof uses a mixture of bamboo fiber and epoxy resin. This research is a real experimental research that uses the Hand Lay Up Coating method. With a variety of types of bamboo fibers used, namely apus bamboo fiber (Gigantochloa apus), betung bamboo (Dendrocalamus asper), ori bamboo (Bambusa blumeana), and wulung bamboo (Gigantochloa atroviolacea). The composite layer in this study was made by applying a mixture of bamboo fiber and epoxy resin using the hand lay up coating method. The room temperature drop test uses a cube-shaped device made of multiplex measuring 50 cm x 50 cm x 50 cm. Thermocouples are placed on the cube at 4 different points, namely the top of the cube, above the galvalume surface, below the galvalume surface, and inside the cube space. Testing is done in an open area so that it is exposed to sunlight and tested for 10 minutes. In the thermal conductivity test, the highest value was obtained in the galvalume coating specimen of wulung bamboo fiber with a thermal conductivity value of 0,244230 W/m.℃ and the lowest thermal conductivity value in the galvalume coating specimen of apus bamboo fiber with a thermal conductivity value 0,188406 W/m.℃. Analysis by visual from Macroscopic photos show that galvalume specimens coated with wulung bamboo fiber have the best powder distribution. The results of the temperature drop test found that the value of the temperature difference (ΔT) in the room of galvalume specimens without coating with the best galvalume coating specimen is the galvalume coating specimen of apus bamboo fiber with a temperature difference of 1,978°C and the lowest is the galvalume coating specimen of wulung bamboo fiber with a temperature difference of 1,735°C.
| Item Type: | Thesis (Sarjana) |
|---|---|
| Identification Number: | 052407 |
| Uncontrolled Keywords: | Serat Bambu, Komposit, Coating, Atap Galvalum, Konduktivitas Termal, Penurunan Temperatur, Temperatur Ruangan-Bamboo Fiber, Composite, Coating, Galvalume Roof, Thermal Conductivity, Temperature Drop, Room Temperature. |
| Divisions: | Fakultas Teknik > Teknik Mesin |
| Depositing User: | Unnamed user with username nova |
| Date Deposited: | 26 Aug 2024 04:11 |
| Last Modified: | 26 Aug 2024 04:11 |
| URI: | http://repository.ub.ac.id/id/eprint/224446 |
![[thumbnail of DALAM MASA EMBARGO]](http://repository.ub.ac.id/style/images/fileicons/text.png) |
Text (DALAM MASA EMBARGO)
Abdullah Syaifuddin.pdf Restricted to Registered users only Download (14MB) |
Actions (login required)
 |
View Item |