Studi Pengaruh Tegangan Ac+Dc Pada Proses Plasma Electrolytic Oxidation Terhadap Karakterisrik Permukaan Material Aluminium 6061

Desyami, Kiky Tamara and Dr. Eng. Masruroh, S.Si., M.Si., and Muhammad Prisla Kamil, S.Pd., Ph.D. (2024) Studi Pengaruh Tegangan Ac+Dc Pada Proses Plasma Electrolytic Oxidation Terhadap Karakterisrik Permukaan Material Aluminium 6061. Sarjana thesis, Universitas Brawijaya.

Abstract

Aluminium 6061 (Al 6061) adalah bahan material yang sering digunakan dalam teknik industri seperti mobil, ruang angkasa, dan teknik kelautan. Sifat dari Al 6061 yaitu ringan dan kuat, namun masih rentan terhadap korosi yang terjadi. Oleh karena itu, diperlukan pelapisan guna meningkatkan ketahanan korosi. Dari beberapa metode pelapisan, penggunaan metode Plasma Electrolytic Oxidatioan (PEO) dipilih karena lebih ramah lingkungan dan menghemat waktu pelapisan. Dalam proses PEO memerlukan tegangan yang tinggi, sehingga penelitian ini yaitu menggunakan tegangan gabungan AC+DC untuk mengurangi tegangan yang dibutuhkan selama proses PEO. Tujuan dari penelitian ini yaitu mempelajari pengaruh variasi tegangan gabungan AC+DC pada proses PEO. PEO dilakukan selama 10 menit dengan dua variasi AC dan DC. Beberapa karakterisasi dilakukan dengan menggunakan FESEM-EDX, TMS, XRD, uji sudut kontak, dan uji korosi. Hasil dari pengujian memperlihatkan bahwa variasi tegangan menunjukkan bahwa dapat menurunkan tegangan yang diperlukan untuk menjalankan proses Plasma Electolytic Oxidation (Breakdown Voltage). Dari variasi tegangan yang digunakan dalam penelitian ini, tegangan optimal yaitu AC 20V DC 140V dengan ketahanan korosi terbaik.

English Abstract

Aluminum 6061 (Al 6061) is a material that is often used in industrial engineering such as automobiles, aerospace and marine engineering. The properties of Al 6061 are light and strong, but still susceptible to corrosion. Therefore, coating is needed to increase corrosion resistance. Of the several coating methods, the use of the Plasma Electrolytic Oxidation (PEO) method was chosen because it is more environmentally friendly and saves coating time. The PEO process requires a high voltage, so this research uses a combined AC+DC voltage to reduce the voltage required during the PEO process. The aim of this research is to study the effect of AC+DC combined voltage variations on the PEO process. PEO was carried out for 10 minutes with two variations, AC and DC. Several characterizations were carried out using FESEM-EDX, TMS, XRD, contact angle tests, and corrosion tests. The results of the test show that variations in voltage show that it can reduce the voltage needed to carry out the Plasma Electolytic Oxidation (Breakdown Voltage) process. From the voltage variations used in this research, the optimal voltage is AC 20V DC 140V with the best corrosion resistance.

Item Type:	Thesis (Sarjana)
Identification Number:	052409
Uncontrolled Keywords:	Alumina, Al 6061, Plasma electrolytic oxidation, Tegangan gabungan.
Divisions:	Fakultas Matematika dan Ilmu Pengetahuan Alam > Fisika
Depositing User:	Unnamed user with username nova
Date Deposited:	22 Aug 2024 04:15
Last Modified:	22 Aug 2024 04:15
URI:	http://repository.ub.ac.id/id/eprint/223649

Text (DALAM MASA EMBARGO) Kiky Tamara Desyami.pdf Restricted to Registered users only Download (6MB)

Actions (login required)

View Item