Sintesis Alumunium(III) Oksalat dengan Metode Hidrotermal untuk Adsorpsi Larutan Kromium(VI)

Dharmadyaksa, Anshari and Yuniar Ponco Prananto, S.Si., M.Sc., Ph.D and Prof. Dr. Ir. Adam Wiryawan, M,S, (2024) Sintesis Alumunium(III) Oksalat dengan Metode Hidrotermal untuk Adsorpsi Larutan Kromium(VI). Sarjana thesis, Universitas Brawijaya.

Abstract

Pengembangan material baru dalam penanganan limbah perairan, khususnya Cr(VI) yang efisien dan efektif masih terus dilakukan karena Cr(VI) merupakan spesi kimia yang beracun dan berbahaya untuk lingkungan perairan. Senyawa Al(III) oksalat merupakan salah satu kandidat yang dapat dikembangkan sebagsi adsorben Cr(VI) karena senyawa ini memiliki pori. Penelitian ini bertujuan untuk mensintesis Al(III) oksalat dengan metode hidrotermal, mempelajari pengaruh pH dalam sintesis tersebut, dan menguji kemampuannya dalam mengadsorpsi larutan Cr(VI). Sintesis Al(III) oksalat dilakukan dengan metode hidrotermal dengan rasio mol alumunium(III):oksalat 2:3 pada kondisi 120°C - 6 jam dengan variasi pH 4 dan 7. Karakterisasi produk dilakukan dengan spektroskopi FTIR, dan P-XRD. Studi adsorpsi Cr(VI) dilakukan dengan metode batch dan konsentrasi Cr(VI) ditentukan dengan UV-Vis menggunakan reagen difenilkarbazida. Hasil penelitian menunjukkan bahwa padatan Al(III) oksalat dapat disintesis dengan metode hidrotermal pada kondisi 120°C - 6 jam dan pH 7. Al(III) oksalat yang diperoleh berupa padatan kristalin berwarna putih, dimana analisis FTIR menunjukkan adanya puncak tajam di sekitar 1650, 1400, dan 1300 cm-1 yang mengindikasikan gugus oksalat, dan analisis P-XRD menunjukkan derajat kristalinitas sebesar 18,43%, namun pola difraksi tidak identik dengan pustaka pembanding. Derajat keasaman berpengaruh dalam sintesis hidrotermal Al(III) oksalat, dimana pada kondisi pH asam tidak membentuk padatan kompleks. Produk yang diperoleh tidak dapat digunakan sebagai adsorben Cr(VI), karena padatan larut sempurna ke dalam larutan ketika uji adsorpsi baru berjalan 15 menit. Kadar Cr(VI) yang teradsoprsi adalah 5,9%

English Abstract

The development of new materials in handling aquatic waste, especially Cr(VI) that is efficient and effective is still ongoing because Cr(VI) is a chemical species that is toxic and dangerous for the aquatic environment. Al(III) oxalate compound is one of the candidates that can be developed as Cr(VI) adsorbent because this compound has pores. This research aims to synthesize Al(III) oxalate by hydrothermal method, study the effect of pH in the synthesis, and test its ability to adsorb Cr(VI) in solution. The synthesis of Al(III) oxalate was carried out by hydrothermal method with a mol ratio of aluminum(III):oxalate 2:3 at 120°C - 6 hours with pH variations of 4 and 7. Product characterization was carried out by FTIR spectroscopy, and P-XRD. The adsorption study of Cr(VI) was conducted by batch method and the concentration of Cr(VI) was determined by UV-Vis using diphenylcarbazide reagent. The results showed that Al(III) oxalate solids can be synthesized by hydrothermal method under conditions of 120°C - 6 hours and pH 7. Al(III) oxalate obtained is a white crystalline solid, in which FTIR analysis shows the presence of sharp peaks around 1650, 1400, and 1300 cm-1 which indicate the oxalate groups, and P-XRD analysis shows a degree of crystallinity of 18.43%, but the diffraction pattern is not identical to the comparison compounds. The degree of acidity is influential in the hydrothermal synthesis of Al(III) oxalate, in which at acidic conditions (pH 4), it does not form precipitated complex. The synthesized product cannot be used as a Cr(VI) adsorbent, because the compound dissolves completely into the solution when the adsorption test has only been running for 15 minutes. The adsorbed Cr(VI) content was 5.9%

Item Type:	Thesis (Sarjana)
Identification Number:	052409
Uncontrolled Keywords:	Al(III) oksalat, Cr(VI), hidrotermal, pH, adsorpsi-Al(III) oxalate, Cr(VI), hydrothermal, pH, adsorption
Divisions:	Fakultas Matematika dan Ilmu Pengetahuan Alam > Kimia
Depositing User:	Unnamed user with username nova
Date Deposited:	16 Aug 2024 05:56
Last Modified:	16 Aug 2024 05:56
URI:	http://repository.ub.ac.id/id/eprint/223345

Text (DALAM MASA EMBARGO) Anshari Dharmadyaksa.pdf Restricted to Registered users only Download (3MB)

Actions (login required)

View Item