Pengaruh Penambahan 50% Zeolit Terhadap Karakteristik Char Hasil Pirolisis Kayu Mahoni Pada Temperatur Pirolisis 350-800oC

Sokhib, Muhammad (2017) Pengaruh Penambahan 50% Zeolit Terhadap Karakteristik Char Hasil Pirolisis Kayu Mahoni Pada Temperatur Pirolisis 350-800oC. Sarjana thesis, Universitas Brawijaya.

Abstract

Pirolisis merupakan proses dekomposisi termal biomassa dengan sedikit oksigen, sehingga ikatan rantai panjang hidrokarbon yang tadinya lebih kompleks mengalami pemecahan menjadi ikatan molekul yang lebih sederhana dalam bentuk char, tar, dan gas. Tujuan penelitian ini adalah untuk mengidentifikasi karakteristik char hasil pirolisis serbuk kayu mahoni dengan penambahan zeolit sebesar 50 %, seberapa besar pengaruh variasi temperatur dan juga zeolit pada karakteristik char. Dalam penelitian ini menggunakan variasi pirolisis biomassa tanpa zeolit dan biomassa dengan penambahan 50% zeolit dan masing-masing sampel dipirolisis pada temperatur 350°C, 500°C dan 800°C. Proses pirolisis ini dilakukan selama tiga jam dengan sedikit kadar oksigen dengan bahan baku serbuk kayu mahoni sebanyak 200 gram dengan ukuran mesh 20 dan serbuk zeolite 200 gram serta kadar air < 2%. Hasil penelitian menunjukkan dengan meningkatnya temperatur maka char yang terbentuk akan menurun hingga variasi temperatur 800°C, berbeda dengan hasil char pirolisis tanpa menggunakan zeolit yang proses dekomposisinya kurang efektif dimana hasil produk masih kurang dalam hal kualitas dengan produk utama hanya char dan menghasilkan sedikit tar dan gas. Char yang dihasilkan pada setiap temperatur mayoritas tersusun atas unsur karbon. Penelitian juga menunjukkan bahwa penggunaan zeolit akan menghasilkan char dengan rantai karbon lebih sederhana dibandingkan dengan kandungan char pada pirolisis tanpa menggunakan zeolit. Selain itu prosentase kandungan karbon akan terus meningkat seiring meningkatnya temperatur. Sedangkan kandungan unsur oksigen akan menurun terhadap peningkatan temperatur pemanasan pirolisis.

English Abstract

Pyrolysis is a thermochemical decomposition of organic material at elevated temperatures in a little amount of oxygen, thus the long and complex chain of hydrocarbon molecule compounds cracked into simpler molecular bonds and shorter hydrocarbon chain in the form of char, tar, and gasses. The purpose of this study is to identify the effect of temperature variation to the characteristics of char made from pyrolyzed mahogany wood powder with an addition of 50 % zeolite. In this study, the variation is the kind of organic material, organic material without zeolite and organic material with 50% zeolite. Each of kind organic material have temperature variation set to 350°C, 500°C and 800°C. Pyrolysis process was conducted for three hours without oxygen with mahogany wood raw material powder 200 grams with 20 mesh size, zeolite powder 200 grams and water content less than 2%. The results showed with the increasing of temperature, the mass and volume of char will decrease continuously until the temperature of 800°C, in contrast to the results of pyrolysis with 50% zeolite more effective than pyrolysis without zeolite because the main product in pyrolysis without zeolite is char but less of tar and gasses. The characteristics of char at each temperature have the majority of carbons. In addition the use of zeolite will produce char with shorter carbon chain than the char in the pyrolysis without the use of zeolites. Then, the carbon percentage will increase with the increasing of temperature. But, the oxygen percentage will decrease with the increasing of temperature.

Item Type:	Thesis (Sarjana)
Identification Number:	SKR/FT/2017/453/051705354
Subjects:	600 Technology (Applied sciences) > 676 Pulp and paper technology > 676.1 Pulp
Divisions:	Fakultas Teknik > Teknik Mesin
Depositing User:	Budi Wahyono Wahyono
Date Deposited:	07 Sep 2017 06:53
Last Modified:	12 Dec 2020 16:38
URI:	http://repository.ub.ac.id/id/eprint/2226

	Text BAGIAN DEPAN.pdf Restricted to Repository staff only Download (1MB)
	Text BAB 1.pdf Restricted to Repository staff only Download (96kB)
	Text BAB 2.pdf Restricted to Repository staff only Download (1MB)
	Text BAB 3.pdf Restricted to Repository staff only Download (413kB)
	Text BAB 4.pdf Restricted to Repository staff only Download (708kB)
	Text BAB 5.pdf Restricted to Repository staff only Download (87kB)
	Text 9 Daftar Pustaka.pdf Restricted to Repository staff only Download (155kB)

Actions (login required)

View Item