Optimasi Kekuatan Tarik Sambungan Las Gesek AA6061 Dengan Variasi Sudut Chamfer Ganda, Waktu Gesek, Dan Gaya Tekan Akhir Menggunakan Box-Behnken Design.

Rizki, Siswanto Adhi and Dr. Eng. Yudy Surya Irawan, ST.,MT and Moch. Syamsul Ma’arif, ST.,MT (2024) Optimasi Kekuatan Tarik Sambungan Las Gesek AA6061 Dengan Variasi Sudut Chamfer Ganda, Waktu Gesek, Dan Gaya Tekan Akhir Menggunakan Box-Behnken Design. Sarjana thesis, Universitas Brawijaya.

Abstract

Saat ini penggunaan aluminium dan logam paduan aluminium didunia industri terus berkembang di era modernisasi karena merupakan elemen dasar untuk membuat suatu yang berguna dalam bidang industri manufaktur, industri otomotif maupun konstruksi bangunan. Salah satu material yang digunakan adalah Alumunium A6061. Alumunium A6061 merupakan alumunium paduan yang mengandung Mg2Si yang memiliki kelemahan dalam proses penyambungannya. Penelitian ini meneliti sifat-sifat las gesek pada material simillar aluminium A6061. Las gesek merupakan metode pengelasan logam dalam keadaan solid state dengan memanfaatkan panas karena adanya gesekan dan pemberian tekanan. Keuntungan menggunakan las gesek adalah dapat melakukan penyambungan dengan efisien waktu dan memiliki kelebihan pada benda silinder. Dalam penelitian ini menggunakan logam Alumunium A6061 dengan tujuan untuk mengoptimalkan dan menganalisis pengaruh sudut chamfer, waktu gesek, dan gaya tekan akhir terhadap kekuatan tarik sambungan las. Rancangan percobaan menggunakan metode box-behnken design dengan foto makrostruktur dan mikrostruktur untuk mengamati luasan daerah pengelasan dan besar butiran yang terbentuk. Hasil pengujian kekuatan tarik sambungan las didapatkan pada spesimen dengan kekuatan tarik tertinggi yaitu pada spesimen maximum dengan nilai 147,16 MPa dengan variasi sudut chamfer 30˚, waktu gesek 7s, dan gaya tekan akhir 28 kN. Pada spesimen optimasi yang memiliki nilai kekuatan tarik 138,27 MPa dengan variasi sudut chamfer 30˚, waktu gesek 5s, dan gaya tekan akhir 28 kN. Kemudia pada spesimen pembanding memiliki kekuatan tarik sebesar 135,01 MPa dengan sudut chamfer 90˚, waktu gesek 5s, dan gaya tekan akhir 28 kN, dan spesimen minimum yang memiliki nilai kekuatan tarik sebesar 56,01 MPa dengan variasi sudut chamfer 60˚, waktu gesek 9s, dan gaya tekan akhir 15,75 kN.

English Abstract

Currently the use of aluminum and aluminum alloy metals in the industrial world continues to grow in the modernization era because it is a basic element to make something useful in the manufacturing industry, automotive industry and building construction. One of the materials used is Aluminum A6061. Aluminum A6061 is an aluminum alloy containing Mg2Si which has weaknesses in the connection process. This study examines the properties of friction welding in aluminum simillar material. Friction welding is a method of welding metals in a solid state state by utilizing heat due to friction and applying pressure. The advantage of using friction welding is that it can perform splicing efficiently in time and has advantages on cylindrical objects. In this study using A6061 Aluminum metal with the aim of optimizing and analyzing the influence of chamfer angle, friction time, and final compressive force on the tensile strength of welded joints. The experimental design used the box-behnken design method with macrostructure and microstructure photos to observe the area of weld zone and the size of the grains formed. The results of the tensile strength test of the welded joint were obtained on the specimen with the highest tensile strength, namely on the maximum specimen with a value of 147.16 MPa with a variation of 30° chamfer angle, 7s friction time, and a final compressive force of 28 kN. In an optimized specimen that has a tensile strength value of 138.27 MPa with a variation in chamfer angle of 30°, friction time of 5s, and final compressive force of 28 kN. Then the comparison specimen has a tensile strength of 135.01 MPa with a chamfer angle of 90°, friction time of 5s, and a final compressive force of 28 kN, and a minimum specimen that has a tensile strength value of 56.01 MPa with variations in chamfer angle of 60°, friction time of 9s, and final compressive force of 15.75 kN.

Item Type:	Thesis (Sarjana)
Identification Number:	0524070044
Uncontrolled Keywords:	Kekuatan Tarik, Alumunium A6061, Pengelasan Gesek, Box-Behnken Design Tensile Strength, Aluminum A6061, Friction Welding, Box-Behnken Design
Divisions:	Fakultas Teknik > Teknik Mesin
Depositing User:	Sugeng Moelyono
Date Deposited:	20 May 2024 08:08
Last Modified:	30 May 2024 03:30
URI:	http://repository.ub.ac.id/id/eprint/219213

Text (DALAM MASA EMBARGO) Siswanto Adhi Rizki.pdf Restricted to Registered users only Download (19MB)

Actions (login required)

View Item