Studi Pengaruh Konsentrasi Pelarut Hidrogen Peroksida (H2O2) Sebagai Oxidizing Agent dan Waktu Leaching terhadap Recovery Tembaga (Cu) pada SIM-Card Handphone Bekas dengan Metode Leaching

Khairina, Prisma Ardaneswari and Ir. Bambang Ismuyanto, M.S., IPM and Ir. Diah Agustina Puspitasari, S.T., M.T., Ph.D (2024) Studi Pengaruh Konsentrasi Pelarut Hidrogen Peroksida (H2O2) Sebagai Oxidizing Agent dan Waktu Leaching terhadap Recovery Tembaga (Cu) pada SIM-Card Handphone Bekas dengan Metode Leaching. Sarjana thesis, Universitas Brawijaya.

Abstract

Di masa kini, kekurangan tembaga akibat konflik geopolitik menjadikan perlunya penelitian untuk metode ekstraksi tembaga dengan sumber selain petambangan..Salah satu potensi sumber daya yang dapat digunakan yakni limbah SIM-Card yang memiliki kandungan Cu melimpah (75,84%). Pada penelitian ini digunakan metode leaching dengan pelarut asam sulfat (H2SO4) dan hidrogen peroksida (H2O2) sebagai agen. Penelitian ini berfokus untuk mengetahui pengaruh variasi konsentrasi H2O2 pada 14%, 14,5%, 15%, 15,5%, 16%, dan waktu pengadukan selama 20, 40, 60 menit. Variabel kontrol yakni 80 mL 2M H2SO4, 20 mL H2O2, rasio S/L 5 gr, dimensi 0,5 cm x 0,5 cm, suhu 50°C, tekanan 1 atm, dan kecepatan pengadukan 200 RPM. Hasil penelitian ini yakni meningkatnya konsentrasi H2O2 dari dari 14% ke 15,5% berpengaruh terhadap peningkatan % recovery Cu dari SIM Card bekas. % Recovery Cu tertinggi diperoleh pada konsentrasi H2O2 15,5% yaitu sebesar 94,15%. Peningkatan konsentrasi H2O2 di atas 15,5% tidak efektif terhadap % recovery Cu. Namun pada H2O2 di atas 15,5%, tidak efektif dalam menaikkan % recovery tembaga. Sedangkan untuk pengaruh waktu pengadukan terhadap % recovery tembaga, terdapat kenaikan konsentrasi tembaga yang signifikan dari 20 menit hingga 60 menit. Saran dari penelitian ini yakni diperlukan studi lebih lanjut mengenai pengaruh interferensi kandungan logam pada SIM Card terhadap proses leaching dan uji UV-Visible Spectrophotometry, serta diperlukan penelitian lanjutan mengenai potensial sel secara aktual.

English Abstract

In the Status Quo, the shortage of copper due to geopolitical conflicts makes it necessary to find new research methods for extracting copper from sources other than mining. One potential resource that can be used is SIM-Card waste which has an abundant Cu content (75.84%). In this research, the leaching method was used with sulfuric acid (H2SO4) and hydrogen peroxide (H2O2) as agents. This research focuses on determining the effect of varying H2O2 concentrations at 14%, 14.5%, 15%, 15.5%, 16%, and stirring times of 20, 40, 60 minutes. The control variables are 80 mL 2M H2SO4, 20 mL H2O2, S/L ratio 5 gr, dimensions 0.5 cm x 0.5 cm, temperature 50°C, pressure 1 atm, and stirring speed 200 RPM. The results of this research are that increasing the concentration of H2O2 from 14% to 15.5% has an effect on increasing the % recovery of Cu from used SIM cards. The highest % Cu recovery was obtained at H2O2 concentration of 15.5%, namely 94.15%. Increasing the H2O2 concentration above 15.5% is not effective on % Cu recovery. However, at H2O2 above 15.5%, it is not effective in increasing the % copper recovery. Meanwhile, regarding the effect of stirring time on the % copper recovery, there was a significant increase in copper concentration from 20 minutes to 60 minutes. The suggestion from this research is that further studies are needed regarding the influence of interference from the metal content of SIM cards on the leaching process and UV-Visible Spectrophotometry tests, and further research is needed regarding actual cell potential.

Item Type:	Thesis (Sarjana)
Identification Number:	0524070146
Uncontrolled Keywords:	Leaching, SIM-Card, Tembaga, Spektrofotometri UV-Vis Leaching, SIM-Card, Tembaga, Spektrofotometri UV-Vis
Divisions:	Fakultas Teknik > Teknik Kimia
Depositing User:	soegeng sugeng
Date Deposited:	20 May 2024 07:03
Last Modified:	20 May 2024 07:03
URI:	http://repository.ub.ac.id/id/eprint/219185

Text (DALAM MASA EMBARGO) Prisma Ardaneswari Khairina.pdf Restricted to Registered users only Download (8MB)

Actions (login required)

View Item