Pengaruh Penambahan Serat Kulit Jagung Terhadap Tingkat Pengurangan Kebisingan Pelapisan Komposit Matrik Epoksi Pada Atap Galvalum

Sugianto, Dimas Kurniawan and Ir. Redi Bintarto, ST., M.Eng.Pract and Dr. Ir. Achmad As’ad Sonief, MT. (2024) Pengaruh Penambahan Serat Kulit Jagung Terhadap Tingkat Pengurangan Kebisingan Pelapisan Komposit Matrik Epoksi Pada Atap Galvalum. Sarjana thesis, Universitas Brawijaya.

Abstract

Penggunaan baja galvalum yang lumayan marak dibidang industri seperti pada produk atap. Namun, atap galvalum mudah menimbulkan kebisingan ketika terkena gaya dari luar seperti saat terjadi hujan. Kebisingan yang termasukdalam kategori polusi suara memiliki dampak buruk terhadap kenyamanan serta kesehatan bagi yang terdampak. Penelitian ini bertujuan untuk menemukan pengaruh dari penambahan serat Kulit Jagung terhadap tingkat pengurangan kebisingan pelapisan komposit matrik epoksi pada atap galvalum. Pemberian lapisan dengan sifat peredam kebisingan pada atap galvalum akan membantu mengurangi kebisingan yang dihasilkan atap galvalum. Produk pelapisan dapat berupa komposit dengan serat alam sebagai pengisinya untuk membantu pengurangan kebisingan pada atap galvalum. Penelitian ini akan menggunakan sampel dari atap galvalum yang dilapisi dan diuji menggunakan simulasi hujan buatan serta alat uji koefisien peredaman suara. Pelapisan menggunakan metode hand lay-up dengan bahan menggunakan campuran antara serat Kulit Jagung dan resin epoksi dengan komposisi fraksi berat 0%:100%, 20%:80%, 30%:70%, 40%:60%, dan 50%:50%. Hasil analisis pesebaran serat Kulit Jagung pada foto makroskopik didapatkan tingkat persebaran paling tinggi pada fraksi berat 50%:50% dengan tingkat kemerataan 93%. Pada pengujian nilai kebisingan didapatkan nilai terendah pada persentase 50%:50% dengan nilai 74,500 dB. Kemudian pada pengujian koefisien peredaman dilakukan dengan meletakkan spesimen galvalum pada alat uji koefisien peredaman berbentuk persegi panjang dengan ukuran 100 cm x 50 cm x 50 cm yang dilengkapi dengan 2 sound level meter. Dari hasil pengujian koefisien peredaman di dapatkan nilai koefisien peredaman (α) paling kecil pada persentase 20%:80% sebesar 0,3695 cm-1 dan paling besar pada persentase 50%:50% yaitu sebesar 0,6365 cm-1. Dari hasil pengujian disimpulkan bahwa penambahan serat Kulit Jagung akan mempengaruhi tingkat pengurangan kebisingan pada penggunaan atap galvalum.

English Abstract

The use of galvalume steel is quite widespread in the industrial sector, such as roofing products. However, galvalum roofs easily cause noise when exposed to external forces, such as when it rains. Noise which is included in the noise pollution category has a negative impact on the comfort and health of those affected. This research aims to find the effect of adding corn husk fiber on the level of noise reduction of epoxy matrix composite coatings on galvalum roofs. Providing a layer with noise reducing properties on a galvalum roof will help reduce the noise produced by a galvalum roof. The coating product can be a composite with natural fiber as a filler to help reduce noise on galvalum roofs. This research will use samples from galvalum roofs that are coated and tested using artificial rain simulations and soundproofing coefficient test equipment. Coating uses the hand lay-up method with materials using a mixture of Corn Husk fiber and epoxy resin with a weight fraction composition of 0%:100%, 20%:80%, 30%:70%, 40%:60%, and 50%: 50%. The results of the analysis of the distribution of Corn Husk fibers in macroscopic photos showed that the highest level of distribution was in the weight fraction of 50%:50% with an evenness level of 93%. In testing the noise value, the lowest value was obtained at a percentage of 50%:50% with a value of 74,500 dB. Then, the damping coefficient test was carried out by placing the galvalum specimen on a rectangular damping coefficient test equipment measuring 100 cm x 50 cm x 50 cm which was equipped with 2 sound level meters. From the results of the damping coefficient test, it was found that the damping coefficient (α) value was the smallest at a percentage of 20%:80%, amounting to 0.3695 cm-1 and the largest at a percentage of 50%:50%, namely 0.6365 cm-1. From the test results it was concluded that the addition of corn husk fiber would affect the level of noise reduction when using a galvalum roof.

Item Type:	Thesis (Sarjana)
Identification Number:	0524070010
Uncontrolled Keywords:	Serat Kulit Jagung, Matrik Epoksi, Atap Galvalum, Hand Lay-Up, Fraksi Berat, Nilai Kebisingan, Koefisien Peredaman, Corn Husk Fiber, Epoxy Resin, Galvalume Roofs, Hand Lay-Up, Weight Fraction, Noise Value, Sound Absorption Coefficient
Divisions:	Fakultas Teknik > Teknik Mesin
Depositing User:	Unnamed user with email dini@ub.ac.id
Date Deposited:	03 Apr 2024 07:50
Last Modified:	03 Apr 2024 07:50
URI:	http://repository.ub.ac.id/id/eprint/217894

Text (DALAM MASA EMBARGO) DIMAS KURNIAWAN SUGIANTO.pdf Restricted to Registered users only Download (13MB)

Actions (login required)

View Item