Zakaria, Muhamad Zulfikar and Dr. Eng. Ir. Eva Arifi, S.T., M.T. and Dr. Eng. Devi Nuralinah, S.T., M.T. (2024) Pengaruh Limbah Cangkang Kerang Hijau (Perna viridis) yang Dikalsinasi terhadap Kuat Tekan pada Mortar. Sarjana thesis, Universitas Brawijaya.
Abstract
Indonesia aktif meningkatkan kualitas negaranya dengan berbagai langkah, termasuk pertumbuhan ekonomi, penanggulangan pengangguran, pengentasan kemiskinan, dan peningkatan kesejahteraan masyarakat. Infrastruktur dianggap memiliki peran strategis dalam mendukung roda kegiatan ekonomi dan masyarakat. Pemerintah fokus pada dua prioritas terkait infrastruktur di tahun 2023: mempercepat pembangunan infrastruktur nasional dan mendorong pertumbuhan sentra ekonomi baru, termasuk Ibu Kota Nusantara (IKN). Pembangunan infrastruktur, seperti jalan, jembatan, gedung, dan perumahan, membutuhkan bahan konstruksi, dengan beton sebagai material utama. Namun, penggunaan beton secara masif juga berdampak pada produksi semen, yang mengandalkan agregat seperti batu kapur. Penambangan yang terus berlanjut menyebabkan berkurangnya sumber daya alam pembetonan. Alternatif potensial adalah menggunakan cangkang kerang hijau sebagai bahan substitusi dalam campuran beton, mengingat tingginya produksi dan kandungan senyawa CaCO3 pada cangkang tersebut. Meski demikian, perlu diperhatikan bahwa penggunaannya memerlukan proses kalsinasi untuk mengatasi tingginya kandungan CaCO3 yang dapat mempengaruhi daya ikat beton. Penelitian ini bertujuan untuk menjawab pertanyaan yang muncul seiring dengan pembahasan sebelumnya. Dalam konteks penggunaan cangkang kerang hijau (Perna viridis) sebagai substitusi dalam semen, fokus utama penelitian adalah mengidentifikasi pengaruhnya terhadap kuat tekan mortar. Dengan pertumbuhan produksi cangkang kerang hijau yang signifikan, potensi pemanfaatannya sebagai bahan substitusi dalam campuran beton menjadi lebih menarik. Pengaruh substansi tersebut terhadap karakteristik kuat tekan mortar menjadi pokok perhatian, mengingat tingginya kandungan senyawa CaCO3 pada cangkang kerang hijau yang dapat memengaruhi daya ikat beton. Dengan demikian, penelitian ini diharapkan dapat memberikan kontribusi dalam mencapai tujuan pemerintah untuk meningkatkan kualitas negara melalui pengembangan sektor ekonomi dan infrastruktur. ix ix Berdasarkan hasil penelitian pengaruh subtitusi cangkang kerang hijau yang telah dikalsinasi terhadap sebagian semen, ditemukan bahwa limbah cangkang kerang hijau di desa Banyuurip memiliki kandungan sekitar 98,150% kalsium oksida (CaO) setelah uji X-ray Flourescene. Kalsium oksida ini ternyata dapat digunakan sebagai subtitusi pada semen dan berperan penting dalam kuat tekan semen. Uji kuat tekan dilakukan pada tiga variasi campuran cangkang kerang hijau dengan kontrol, menunjukkan bahwa persentase cangkang kerang hijau, mempengaruhi kuat tekan mortar pada umur 28 hari. Hal ini disebabkan oleh kurangnya kandungan silika (SiO2) dalam cangkang kerang hijau, yang merupakan komponen penting dalam pembentukan kalsium hidroksida (Ca(OH)2) yang berkontribusi pada kuat tekan mortar.
English Abstract
Indonesia is actively improving the quality of its nation through various measures, including economic growth, addressing unemployment, poverty alleviation, and improving the welfare of society. Infrastructure is considered to play a strategic role in supporting economic and societal activities. The government is focusing on two infrastructure-related priorities in 2023: accelerating the development of national infrastructure and promoting the growth of new economic centers, including the Nusantara Capital (IKN). Infrastructure development, such as roads, bridges, buildings, and housing, requires construction materials, with concrete being the primary material. However, the extensive use of concrete also impacts cement production, which relies on aggregates like limestone. Ongoing mining leads to a depletion of natural cementation resources. A potential alternative is using green shellfish shells as a substitution material in concrete mixes, given their high production and CaCO3 compound content. However, it should be noted that their use requires a calcination process to address the high CaCO3 content that can affect concrete binding. This research aims to answer the arising from the previous discussion. In the context of using green shellfish shells (Perna viridis) as a substitute in cement, the main focus of the research is to identify their influence on the compressive strength of mortar. With the significant growth in green shellfish shell production, its potential use as a substitution material in concrete mixes becomes more appealing. The impact of this substance on the compressive strength characteristics of mortar is a key concern, considering the high CaCO3 content in green shellfish shells that can affect concrete binding. Thus, this research is expected to contribute to achieving the government's goal of improving the nation's quality through the development of the economic and infrastructure sectors. xi xi Based on the research results regarding the influence of calcined green shell substitution on a portion of cement, it was found that green shell waste in the Banyuurip village contains approximately 98.150% calcium oxide (CaO) after X-ray Fluorescence testing. This calcium oxide can be used as a substitute in cement and plays a crucial role in the compressive strength of cement. Compressive strength tests were conducted on three variations of green shell mixes with control, indicating that the percentage of green shell content affects the compressive strength of mortar at 28 days. This is due to the lack of silica (SiO2) content in green shell, which is an essential component in the formation of calcium hydroxide (Ca(OH)2) contributing to mortar compressive strength.
| Item Type: | Thesis (Sarjana) |
|---|---|
| Identification Number: | 0524070059 |
| Uncontrolled Keywords: | Cangkang Kerang Hijau, subtitusi semen, kuat tekan, Pembangunan berkelanjutan. |
| Divisions: | Fakultas Teknik > Teknik Sipil |
| Depositing User: | Endang Susworini |
| Date Deposited: | 19 Feb 2024 08:04 |
| Last Modified: | 19 Feb 2024 08:04 |
| URI: | http://repository.ub.ac.id/id/eprint/215582 |
![[thumbnail of DALAM MASA EMBARGO]](http://repository.ub.ac.id/style/images/fileicons/text.png) |
Text (DALAM MASA EMBARGO)
Muhamad Zulfikar Zakaria.pdf Restricted to Registered users only Download (4MB) |
Actions (login required)
 |
View Item |