Pengaruh Perendaman Yang Dilakukan Pada Komposit Berpenguat Serat Karbon Dan Filler Fly Ash Dalam Larutan HCl 1M Dengan Variasi Temperatur,

Akbar, Hatri Adilah and Dr. Ir. Femiana Gapsari,, ST., MT. and Ari Wahjudi., ST., MT. (2023) Pengaruh Perendaman Yang Dilakukan Pada Komposit Berpenguat Serat Karbon Dan Filler Fly Ash Dalam Larutan HCl 1M Dengan Variasi Temperatur,. Sarjana thesis, Universitas Brawijaya.

Abstract

Penggunaan polimer dan komposit semakin meningkat di semua bidang kehidupan saat ini. Komposit berpenguat serat sering digunakan dalam alat yang membutuhkan bahan yang sifatnya perpaduan dua sifat dasar yaitu kekuatan dan ringan. Perlengkapan otomotif dapat dibuat dari komposit yaitu campuran antara matriks dan serat, matriks berfungsi sebagai pengisi yang mempunyai fraksi volume yang dominan dan serat berfungsi sebagai penahan beban. Sebagian besar komposit banyak digunakan berupa polymer matrix composite (PMC). Sebelum melalui proses-proses pengujian, komposit dibuat berdasarkan komposisi yang telah ditentukan dengan metode vacuum bag. Komposit akan direndam didalam HCl 1M selama 24 jam dalam variasi temperatur 25, 50, dan 75C dengan tujuan untuk mengamati degradasi komposit yang terjadi pada setiap temperatur. Variasi komposit dapat langsung diuji kerakterisasi setalah dikeringkan dari HCl 1M. Selanjutnya serat akan diuji tarik dan SEM pada patahan uji tariknya.

English Abstract

The use of polymers and composites is increasing in all areas of life today. Fiberreinforced composites are often used in tools that require materials with the combined properties of strength and lightness. Automotive equipment can be made from composites, which are a mixture of matrix and fibers, where the matrix acts as a filler with a dominant volume fraction and the fibers act as load-bearing components. Most composites are widely used in the form of polymer matrix composites (PMC). Before undergoing testing processes, composites are made based on a predetermined composition using vacuum bagging methods. The composites are immersed in HCl 1M for 24 hours at various temperatures of 25, 50, and 75°C with the aim of observing the degradation of the composite that occurs at each temperature. The composite variations can be directly characterized after drying from 1M HCl. Furthermore, the fibers will be tested for tensile strength and SEM on the fracture of the tensile test.

Item Type:	Thesis (Sarjana)
Identification Number:	052307
Uncontrolled Keywords:	Komposit, epoxy, serat karbon, fly ash, uji tarik
Depositing User:	Unnamed user with username iwan
Date Deposited:	26 Jan 2024 06:43
Last Modified:	26 Jan 2024 06:43