Pengaruh Variasi Tekanan Kompaksi Pada Proses Metalurgi Serbuk Terhadap Ketangguhan Dan Mikrostruktur Paduan Zinc Dan Hidroksiapatit Cangkang Sotong (Sepia sp.)

Firmansyah, Harli Farizki and Ir. Teguh Dwi Widodo,, ST., M.Eng., Ph.D. and Ir. Rudianto Raharjo,, ST., MT. (2023) Pengaruh Variasi Tekanan Kompaksi Pada Proses Metalurgi Serbuk Terhadap Ketangguhan Dan Mikrostruktur Paduan Zinc Dan Hidroksiapatit Cangkang Sotong (Sepia sp.). Sarjana thesis, Universitas Brawijaya.

Abstract

Pengembahangan biomaterial sintesis menjadi perhatian kalangan peneliti pada beberapa tahun terakhir, hal ini dikarenakan telah membantu banyak dalam meningkatkan efisiensi bedah ortopedi. Paduan Zinc dan Hidroksiapatit diteliti dapat digunakan sebagai implan biodegradabe yang aman untuk tubuh manusia, beberapa kelebihan utama dari zinc adalah memliki ketahanan korosi dan biokompatibilitas yang baik untuk regenerasi dan terapi jaringan. Dalam tubuh manusia implan zinc akan mengalami proses degradasi secara alami atau yang biasa disebut implan biodegradable, dimana tidak diperlukan tindakan pembedahan lanjutan untuk pengangkatan implan ketika tulang telah sembuh. Penelitian ini bertujuan untuk mengetahui pengaruh variasi tekanan pada proses kompaksi terhadap ketangguhan dan mikrostruktur pada paduan Zn-HAp. Pada penelitian ini dilakukan sintesis untuk menghasilkan paduan logam Zn-HAp. Variasi tekanan kompaksi yang digunakan adalah 16,67 MPa, 17,65 MPa, 18,63 MPa, 19,61 MPa, 20,59 MPa dalam cetakan berbentuk balok. Penelitian ini menggunakan metode metalurgi serbuk dengan komposisi paduan 70% Zinc dan 30% Hidroksiapatit dan suhu sintering sebesar 380⁰C dengan waktu holding 3 jam. Penelitian ini dilakukan dengan beberapa pengujian diantaranya, uji impact charpy untuk mengetahui nilai ketangguhan dari paduan biodegradable Zn-HAp, pengamatan foto makro dengan menggunakan Canon EOS 5D dengan lensa makro untuk analisis bentuk patahan yang terjadi akibat uji impact, pengamatan SEM EDS dengan merek Hitachi FLEXSEM 1000 untuk mengetahui morfologi permukaan serta persebaran unsur dari paduan Zn-HAp, serta uji densitas untuk mengetahui hasil kualitas dari produk metalurgi serbuk dengan melihat nilai kepadatan rata – rata spesimen paduan Zn-HAp.

English Abstract

The development of synthetic biomaterials has been of interest to researchers in recent years, as it has helped greatly in improving the efficiency of orthopedic surgery. Zinc and hydroxyapatite alloys are investigated to be used as biodegradable implants that are safe for the human body, some of the main advantages of zinc are that it has good corrosion resistance and biocompatibility for tissue regeneration and therapy. In the human body, zinc implants will undergo a natural degradation process or what is commonly called a biodegradable implant, where no further surgery is required to remove the implant when the bone has healed. This study aims to determine the effect of pressure variation in the compacting process on the toughness and microstructure of Zn-HAp alloy. In this study, synthesis was carried out to produce Zn-HAp metal alloy. Compaction pressure variations used are 16.67 MPa, 17.65 MPa, 18.63 MPa, 19.61 MPa, 20.59 MPa in a block-shaped mold. This research used powder metallurgy method with alloy composition of 70% Zinc and 30% Hydroxyapatite and sintering temperature of 380⁰C with holding time of 3 hours. This research was conducted with several tests including, charpy impact test to determine the toughness value of Zn-HAp biodegradable alloy, macro photo observation using Canon EOS 5D with macro lens to analyze the shape of the fracture that occurs due to impact test, SEM EDS observation with Hitachi FLEXSEM 1000 brand to determine the surface morphology and distribution of elements of Zn-HAp alloy, and density test to determine the quality results of powder metallurgy products by looking at the average density value of Zn-HAp alloy specimens

Item Type:	Thesis (Sarjana)
Identification Number:	052307
Uncontrolled Keywords:	Zinc, Hydroxyapatite, Implan biodegradable, Metalurgi Serbuk, Nilai Ketangguhan, Mikrostruktur, Uji Impact, Charpy, Sintesis Hap
Divisions:	Fakultas Teknik > Teknik Mesin
Depositing User:	Unnamed user with username iwan
Date Deposited:	26 Jan 2024 03:47
Last Modified:	26 Jan 2024 03:47
URI:	http://repository.ub.ac.id/id/eprint/214304

Text (DALAM MASA EMBARGO) Harli Farizki Firmansyah.pdf Restricted to Registered users only Download (6MB)

Actions (login required)

View Item