Studi Eksperimen Penambahan Serat Polypropylene Pada Limbah Masker Terhadap Kuat Tekan, Kuat Tarik Belah, Modulus Elastisitas, dan Poisson Ratio Beton Normal

Ramadhani, Gabrielle Pramesti Cahyaning and Ir. Indra Waluyohadi,, ST., MT., M.Sc. and Dr. Eng. Devi Nuralinah,, ST., MT (2023) Studi Eksperimen Penambahan Serat Polypropylene Pada Limbah Masker Terhadap Kuat Tekan, Kuat Tarik Belah, Modulus Elastisitas, dan Poisson Ratio Beton Normal. Sarjana thesis, Universitas Brawijaya.

Abstract

Pandemi Covid-19 membawa banyak dampak terhadap kehidupan dari sektor manapun mulai dari ekonomi, sosial, pendidikan hingga pembangunan. Adanya pandemi ini membuat pemerintah menerapkan beberapa peraturan baru seperti PSBB dan wajibnya penggunaan masker guna mencegah penularan virus corona. Bahkan setelah dua tahun berlalu, masih banyak masyarakat yang tetap menggunakan masker dan masih ada beberapa kegiatan yang mewajibkan menggunakan masker seperti saat akan melakukan penerbangan dengan pesawat terbang. Masker yang digunakan adalah masker medis maupun non medis yang penggunaannya hanya dianjurkan 1x pemakaian. Hal tersebut menyebabkan banyaknya limbah masker yang tertumpuk dan tidak diolah dengan baik. Limbah masker termasuk dalam limbah yang sulit terurai karena mengandung polypropylene di dalamnya. Polypropylene merupakan sebuah polimer termo plastik yang biasa digunakan dalam industri tekstil, perlengkapan laboratorium. Sifatnya yang mirip dengan plastik dan memiliki titik leleh yang tinggi membuat serat ini diinovasi menjadi bahan tambah dalam pembuatan beton. Penambahan serat polypropylene pada limbah serat masker perlu diteliti lebih lanjut. Maka dari itu, dilakukan penelitian mengenai bagaimana pengaruh penambahan serat polypropylene pada limbah masker dengan variasi 0%, 0,5%, 1%, 1,5% dari total volume beton terhadap kuat tekan, kuat tarik belah, modulus elastisitas, dan poisson ratio beton normal. Pada penelitian ini, limbah masker akan di potong menjadi ukuran panjang 5 cm dengan lebar 3 mm, sebelum itu dilakukan pengakuan terlebih dahulu dengan menggunakan larutan kanji. Kemudian potongan limbah masker tersebut di campurkan ke dalam campuran beton dengan metode pencampuran di dalam bekisting setiap 1/3 bagian dan ditumbuk sebanyak 25x agar penyebaran serat lebih merata. Kemudian dilakukan pengujian kuat tekan, kuat tarik belah, modulus elastisitas dan poisson ratio setelah benda uji berumur 28 hari.

English Abstract

The Covid-19 pandemic has had many impacts on the lives of any sector ranging from economy, social, education to development. The existence of this pandemic has made the government implement several new regulations such as PSBB and mandatory use of masks to prevent transmission of the coronavirus. Even after two years have passed, there are still many people who continue to use masks and there are still some activities that require wearing masks such as when going to fly by airplane. The masks used are medical and nonmedical masks whose use is only recommended for 1x use. This causes a lot of mask waste to be piled up and not treated properly. Mask waste is included in waste that is difficult to decompose because it contains polypropylene in it. Polypropylene is a thermo plastic polymer commonly used in the textile industry, laboratory equipment. Its properties are similar to plastic and have a high melting point making this fiber innovated into an added material in making concrete. The addition of polypropylene fiber to mask fiber waste needs further investigation. Therefore, research was conducted on how the effect of adding polypropylene fiber to mask waste with variations of 0%, 0.5%, 1%, 1.5% of the total concrete volume on compressive strength, split tensile strength, modulus of elasticity, and normal concrete poisson ratio. In this study, mask waste will be cut into 5 cm long by 3 mm wide, before that recognition is carried out first using starch solution. Then the pieces of mask waste are mixed into the concrete mixture by mixing method in the formwork every 1/3 part and pounded 25x so that the fiber distribution is more even. Then tests were carried out on compressive strength, split tensile strength, modulus of elasticity and poisson ratio after the specimen was 28 days old.

Item Type:	Thesis (Sarjana)
Identification Number:	052307
Uncontrolled Keywords:	Serat Polypropylene pada Limbah Masker, Kuat Tekan, Kuat Tarik Belah, Modulus Elastisitas, Poisson Ratio
Divisions:	Fakultas Teknik > Teknik Sipil
Depositing User:	Unnamed user with username iwan
Date Deposited:	26 Jan 2024 02:07
Last Modified:	26 Jan 2024 02:07
URI:	http://repository.ub.ac.id/id/eprint/214201

Text (DALAM MASA EMBARGO) GABRIELLE PRAMESTI CAHYANING RAMADHANI.pdf Restricted to Registered users only Download (3MB)

Actions (login required)

View Item