Pengaruh Waktu Hard Anodizing Terhadap Laju Korosi dan Sifat Wettability Pada Lapisan Anodik Recycle Aluminium.

Miranda, Safira and Ir. Rudianto Raharjo, ST., MT. and Ir. Teguh Dwi Widodo, ST., M.Eng., Ph.D. (2023) Pengaruh Waktu Hard Anodizing Terhadap Laju Korosi dan Sifat Wettability Pada Lapisan Anodik Recycle Aluminium. Sarjana thesis, Universitas Brawijaya.

Abstract

Aluminium dan paduannya banyak digunakan diberbagai industri karena sifat-sifat yang dimilikinya. Salah satunya yaitu memiliki ketahanan korosi yang relatif lebih baik jika dibandingkan dengan aluminium murni. Aluminium dan paduannya terlindungi dari korosi oleh lapisan oksida alami yang terbentuk saat aluminium terpapar atmosfer. Namun kemampuan lapisan tersebut untuk melindungi substratnya sangat kecil karena tipisnya lapisan. Hard nodizing merupakan salah satu perlakuan permukaan dimana anoda aluminium diproses secara elektrokimia untuk menghasilkan lapisan anodik yang dapat melindungi substrat dibawahnya. Larutan elektrolit yang umum digunakan dalam proses anodizing adalah asam sulfat Hal ini dikarenakan lapisan anodik yang dihasilkan lebih kuat dan lebih tebal. Namun penggunaan asam sulfat memiliki dampak yang buruk terhadap lingkungan atau pun penggunanya karena bersifat korosif atau merusak. Untuk mengatasi masalah tersebut banyak peneliti yang melakukan percobaan anodizing menggunakan asam organik yang berasal dari buah-buahan yang memiliki rasa asam. Penggunaan larutan campuran asam organik dan anorganik dapat mengurangi laju disolusi pertumbuhan lapisan, meningkatan efisiensi pembentukan lapisan dan meningkatkan karakteristik lapisan.

English Abstract

Aluminum and its alloys are widely used in various industries because of their properties. One of them is that it has relatively better corrosion resistance when compared to pure aluminum. Aluminum and its alloys are protected from corrosion by a natural oxide layer that forms when aluminum is exposed to the atmosphere. However, the ability of the layer to protect the substrate is very small due to the thinness of the layer. Hard nodizing is one of the surface treatments where the aluminum anode is electrochemically processed to produce an anodic layer that can protect the substrate below. The electrolyte solution commonly used in the anodizing process is sulfuric acid because the anodic layer produced is stronger and thicker. However, the use of sulfuric acid has a bad impact on the environment or its users because it is corrosive or destructive. To overcome this problem, many researchers have conducted anodizing experiments using organic acids derived from fruits that have a sour taste. The use of a mixed solution of organic and inorganic acids can reduce the dissolution rate of coating growth, increase the efficiency of coating formation and improve coating characteristics.

Item Type:	Thesis (Sarjana)
Identification Number:	052307
Uncontrolled Keywords:	Hard Anodizing, Belimbing Wuluh, Recycle Aluminium, Laju Korosi, Ketebalan Lapisan Anodik, Wettability, EIS, Hard Anodizing, Bilimbi, Aluminum Recycled, Corrosion Rate, The Thickness of The Anodic Layer, Wettability, EIS.
Divisions:	Fakultas Teknik > Teknik Mesin
Depositing User:	Zainul Mustofa
Date Deposited:	22 Jan 2024 07:13
Last Modified:	22 Jan 2024 07:16
URI:	http://repository.ub.ac.id/id/eprint/213081

Text (DALAM MASA EMBARGO) Safira Miranda.pdf Restricted to Registered users only until 31 December 2025. Download (10MB)

Actions (login required)

View Item