Pengaruh Pelapisan FeNiCr dan FeNiCrMo Dengan Metode HVOF Pada Substrat Baja Astm A516-70 Terhadap Laju Erosi Temperatur Tinggi

Galih Bintoro,, Yulian and Dr. Femiana Gapsari,, ST., MT and Dr.Agus Sukarto Wismogroho, M.Eng. (2022) Pengaruh Pelapisan FeNiCr dan FeNiCrMo Dengan Metode HVOF Pada Substrat Baja Astm A516-70 Terhadap Laju Erosi Temperatur Tinggi. Sarjana thesis, Universitas Brawijaya.

Abstract

RINGKASAN Yulian Galih Bintoro, Jurusan Teknik Mesin, Fakultas Teknik, Universitas Brawijaya, April 2022, Pengaruh Pelapisan FeNiCr dan FeNiCrMo Dengan Metode HVOF Pada Substrat Baja Astm A516-70 Terhadap Laju Erosi Temperatur Tinggi. Dosen Pembimbing Femiana Gapsari dan Agus Sukarto Wismogroho Kadar CO2 pada udara di dunia terus meningkat, hal itu salah satunya disebabkan oleh pembangkit listrik bertenaga batubara, salah satu solusi untuk mengurangi emisi CO2 adalah menambahkan biomasa, jenis boiler yang dapat membakar biomasa salah satunya adalah boiler PCB, namun pada boiler jenis ini memiliki kekurangan yaitu terjadi di fenomena erosi dan oksidasi temperature tinggi. pengaplikasian coating diharapkan dapat memperlama kerusakan akibat fenomena tersebut. Tujuan dilakukan penelitian ini adalah mengetahui karakteristik coating HFOV FeNiCr dan FeNiCrMo yang diaplikasikan pada substrat baja astm A516 grade 70 dengan tujuan mecari karakteristik material terbaik untuk kondisi boiler yang terjadi pada kondisi erosi temperatur tinggi . Erosi sendiri merupakan proses dimana logam yang terbentur pada bagian permukaan, oleh benda yang berupa padatan atau cairan . pada boiler material yang berperan sebagai peng erosi adalah Flay Ash Material Fe, Ni, Cr, dan Mo, masing masing dihaluskan kemudian dicampur menggunakan Planetary Ball Mill kemudian dilakukan proses HVOF pada permukaan substrat baja ASTM A516 grade 70 dengan lebar spesimen 20mmx20mmx5mm. Pengujian erosi dilakukan dengan cara mengoksidasi spesimen selama 100 jam dan pengujian erosi tanpa oksida. Karakterisasi material menggunakan Scanning Electrone Microscope (SEM) didapatkan nilai ketebalan lapisan tertinggi FeNiCr 389.02μm, nilai posoritas tertinggi FeNiCr 1814 μm2, Enegy Dispresive Pectroscopy (EDS) dilakukan untuk mengetahui persebaran unsur pada coating. Pengamatan Optical Microscope (OM) dilakukan dengan tujuan mengamati hasil setelah terjadinya erosi pada permukaan dan cross section.Data pertambahan masa akibat oksidasi tertinggi 0,00136 mg/A, Pengujian pull off dilakukan untuk mengetahua tingkat kereakatan antara oksida dengan coating dan mengetahui kerekatan coating dengan substrat data pengujian tarik tertinggi lapisan FeNiCrMo 17,4 N/mm2 , data pengujian kekerasan dilakukan dengan tujuan mengetahui sifat mekanik kekerasan lapisan coating dan lapisan oksida yang terbentuk, nilai kekerasan tertinggi merupakan nilai kekerasan oksida coating FeNiCrMo dengan nilai kekerasan didapat 301,07 HV. Kata Kunci : Erosi, Paduan FeNiCr, FeNiCrMo, ASTM A516-70, Oxide, HVOF, Kekasaran Permukaan, Adhesiv.

English Abstract

SUMMARY Yulian Galih Bintoro, Department of Mechanical Engineering, Faculty of Engineering, Universitas Brawijaya, April 2022, Effect of FeNiCr and FeNiCrMo Coatings Using the HVOF Method on Astm A516-70 Steel Substrate on High-Temperature Erosion Rates. Supervisors Femiana Gapsari and Agus Sukarto Wismogroho CO2 levels in the air in the world continue to increase, one of which is caused by coal-fired power plants, one solution to reduce CO2 emissions is to add biomass, one type of boiler that can burn biomass is PCB boiler, but this type of boiler has drawbacks. which occurs in the phenomenon of erosion and oxidation at high temperatures. coating application is expected to prolong the damage caused by this phenomenon. The purpose of this study was to determine the characteristics of the FeNiCr and FeNiCrMo HFOV coatings applied to the ASTM A516 grade 70 steel substrate with the aim of finding the best material characteristics for boiler conditions that occur at high temperature erosion conditions. Erosion itself is a process where metal is hit on the surface, by objects in the form of solids or liquids. in the boiler the material that acts as an eroding agent is Flay Ash The Fe, Ni, Cr, and Mo materials were grinded and then mixed using a Planetary Ball Mill then the HVOF process was carried out on the surface of ASTM A516 grade 70 steel substrate with a specimen width of 20mmx20mmx5mm. Erosion testing was carried out by oxidizing the specimen for 100 hours and erosion testing without oxide. Material characterization using Scanning Electrone Microscope (SEM) obtained the highest layer thickness value of FeNiCr 389.02μm, the highest porosity value of FeNiCr 1814 m2, Enegy Dispresive Pectroscopy (EDS) was performed to determine the distribution of elements in the coating. Optical Microscope (OM) observations were carried out with the aim of observing the results after the erosion on the surface and cross section. The highest tensile test data for the FeNiCrMo layer is 17.4 N/mm2 , the hardness test data is carried out with the aim of knowing the mechanical properties of the coating layer hardness and the formed oxide layer, the highest hardness value is the FeNiCrMo coating oxide hardness value with a hardness value of 301.07 HV. Key words : Erosion, FeNiCr alloy, FeNiCrMo alloy, ASTM A516-70, Oxide, HVOF, Surface Roughness, Adhesiv

Item Type:	Thesis (Sarjana)
Identification Number:	052307
Uncontrolled Keywords:	Erosi, Paduan FeNiCr, FeNiCrMo, ASTM A516-70, Oxide, HVOF, Kekasaran Permukaan, Adhesiv.
Divisions:	Fakultas Teknik > Teknik Mesin
Depositing User:	Unnamed user with username saputro
Date Deposited:	22 Jan 2024 04:41
Last Modified:	22 Jan 2024 04:41
URI:	http://repository.ub.ac.id/id/eprint/213021

Text (DALAM MASA EMBARGO) YULIAN GALIH BINTORO.pdf Restricted to Registered users only until 31 December 2024. Download (6MB)