PENGARUH KOMPOSISI LAPISAN Ni-Cr PADA BAJA ASME SA 210 C TERHADAP LAJU EROSI SUHU TINGGI”.

Utomo, Slamet Prasetyo and Prof. Ir. Djarot B. Darmadi,, MT., Ph.D and Teguh Dwi Widodo, ST., M.Eng. Ph.D (2023) PENGARUH KOMPOSISI LAPISAN Ni-Cr PADA BAJA ASME SA 210 C TERHADAP LAJU EROSI SUHU TINGGI”. Magister thesis, Universitas Brawijaya.

Abstract

Tujuan dari penelitian ini adalah untuk mengetahui laju erosi temperatur tinggi lapisan NiCr pada baja ASME SA 210 C menggunakan metode combustion oxy fuel thermal spray. Pada boiler Circulating Fluidized Bed (CFB), terjadi sirkulasi fly ash, pasir silika dan udara pada lingkungan bersuhu tinggi yang menyebabkan erosi. Erosi suhu tinggi dapat diminimalkan dengan menggunakan lapisan paduan Ni-Cr dengan metode pembakaran oxy fuel thermal spray. Paduan NiCr terbukti mampu memberikan komposisi lapisan paduan logam yang dapat menahan suhu 600°C dengan kecepatan benturan fly ash 200m/s. Komposisi paduan logam yang telah dipelajari adalah NiCr, NiCrCo, NiCrWc, NiCrWcCo, dan NiCrCoMo. Hasil penelitian ini menunjukkan bahwa paduan logam umumnya melekat pada substrat dan tahan pada temperatur tinggi (600°C). Kekerasan tertinggi diberikan oleh paduan NiCrWcCo yaitu 177,46 HV. Kekerasan terendah terdapat pada komposisi paduan NiCrCo (161,71 HV). Laju erosi suhu tinggi terendah ditemukan pada paduan NiCrWcCo, yaitu -0,00481 gram/menit. Laju erosi yang rendah ini karena paduan NiCrWcCo menghasilkan wetting effect yang baik bagi paduan logam dan memiliki nilai kekerasan yang tinggi.

English Abstract

The purpose of this study was to determine the high temperature erosion rate of the NiCr coating on ASME SA 210 C steel using the combustion oxy fuel thermal spray method. In Circulating Fluidized Bed (CFB) boiler, there is circulation of fly ash, silica sand and air in a high temperature environment which causes erosion. High temperature erosion can be minimized by using Ni-Cr alloy coating sing the combustion oxy fuel thermal spray method. NiCr alloy is proved a able to provider a metal alloy layer composition that can withstand temperatures of 600°C with a fly ash impact speed of 200m/s. The metal alloy compositions that have been studied are NiCr, NiCrCo, NiCrWc, NiCrWcCo, and NiCrCoMo. The results of this study indicates that metal alloys are generally atteche to the substrate and withstand at a high temperatures (600°C). The highest hardness provide by NiCrWcCo alloy which is 177.46 HV. The lowest hardness is found in the composition of the NiCrCo alloy (161.71 HV). The lowest high temperature erosion rate was found in the NiCrWcCo alloy, which was -0.00481 gram/minute. This low erosion rate because the NiCrWcCo alloy produces a good weeting effect for metal alloys and has a high hardness value

Item Type:	Thesis (Magister)
Identification Number:	052307
Divisions:	Fakultas Teknik > Teknik Mesin
Depositing User:	Emy Sukartini
Date Deposited:	22 Jan 2024 02:08
Last Modified:	22 Jan 2024 02:08
URI:	http://repository.ub.ac.id/id/eprint/212844

Text (Dalam masa EMBARGO) Slamet Prasetyo Utomo.pdf Restricted to Registered users only until 31 December 2025. Download (10MB)

Actions (login required)

View Item