Taufik, Achmad and Prof. Dr. Ir. Pratikto, MMT. and Prof. Ir. Agus Suprapto, M.Sc., Ph.D and Dr. Ir. Achmad As’ad Sonief, MT. (2022) Analisis Formability Hot Rolled Plate Steel Terhadap Proses Bending dan Quench – Temper. Doktor thesis, Universitas Brawijaya.
Abstract
Hot Rolled plate Steel (HRPS) merupakan material baja structural komersial yang diproduksi oleh PT Krakatau Steel (persero) dengan nama KSW 500, akan tetapi dalam aplikasinya masih memerlukan perbaikan sifat mekaniknya sehingga berbagai macam perlakuan perlu ditambahkan. Jika dilakukan dengan metode pengerjaan dingin, terjadi perubahan dimensi yang cukup besar dan deformasi plastis yang tidak homogen. Tujuan penelitian ini mempelajari dampak perilaku radius bending terhadap disribusi kekerasan, distribusi butir dan struktur mikro di bidang/sisi tarik dan bidang/sisi tekan setelah quenching dan tempering pada material HRPS sebagai bahan eksperimen. Metode penelitian ini menggunakan variasi radius bending HRP Steel R : 50, 55, 60, 65, 70 mm dan heat treatment dengan temperature 900℃ dan selanjutnya dilakukan pendinginan sangat cepat menggunakan media air (quench), untuk menghilangkan tegangan sisa dilakukan tempering dengan suhu temper 150℃, kemudian dilakukan pendinginan pada suhu kamar 26℃. Untuk mengetahui pengaruhnya terhadap kekerasan dan struktur mikro yang berdampak pada sifat mekanik. Hasil proses bending HRP Steel dan heat treatment menunjukkan bahwa pada radius bending R 70 mm, memberikan pengaruh yang signifikan yaitu ada peningkatan kekerasan dari HRP Steel sebesar 80,95 %. Dari hasil pengamatan struktur mikro membuktikan bahwa dengan radius bending R 70 mm dan proses quenching – tempering terjadi perubahan struktur mikro lebih halus dan rapat, karena fitur butir menjadi pipih. Hal ini dibuktikan dengan distribusi butir pada bidang/sisi tekan sebesar φ 6,068 μm atau 80% dan bidang/sisi tarik φ 3,584 μm atau 40% sehingga kekerasan HRP Steel dapat meningkat sesuai dengan prosedur Intercept (ASTM 112).
English Abstract
Hot Rolled plate Steel (HRPS) is a commercial structural steel material produced by PT Krakatau Steel (Persero) under the name KSW 500, but in its application it still requires improvement of its mechanical properties so that various kinds of treatments need to be added. If carried out using the cold working method, there will be considerable dimensional changes and inhomogeneous plastic deformation. The purpose of this study was to study the impact of radius bending behavior on the distribution of hardness, grain distribution and microstructure in the tensile stress region and the compressive stress region after quenching and tempering the HRPS material as an experimental material. This research method uses variations in the bending radius of HRP Steel R: 50, 55, 60, 65, 70 mm and heat treatment with a temperature of 900℃ and then cooling very quickly using water (quench), to remove residual stress, tempering is carried out at a tempering temperature. 150℃, then cooled at room temperature 26℃. To find out its effect on hardness and microstructure that has an impact on mechanical properties. The results of the bending process of HRP Steel and heat treatment show that at a bending radius of R 70 mm, it has a significant effect, namely there is an increase in the hardness of HRP Steel by 80.95%. From the observation of the microstructure, it is evident that with a bending radius of R 70 mm and the quenching – tempering process, the microstructure changes to a finer and denser one, because the grain features become flat. This is evidenced by the grain distribution on the compression side of 6,068μm or 80% and the tensile side 3,584μm or 40% so that the hardness of HRP Steel can increase according to the Intercept procedure (ASTM 112).
| Item Type: | Thesis (Doktor) |
|---|---|
| Identification Number: | 062207 |
| Uncontrolled Keywords: | Hot Rolled Plate Steel, Kekerasan, Bending, Quench-Temper.-Hot Rolled Plate Steel, Hardness, Bending, Quench-Temper. |
| Divisions: | S2/S3 > Doktor Teknik Mesin, Fakultas Teknik |
| Depositing User: | soegeng sugeng |
| Date Deposited: | 18 Jan 2024 07:06 |
| Last Modified: | 18 Jan 2024 07:06 |
| URI: | http://repository.ub.ac.id/id/eprint/212080 |
![[thumbnail of DALAM MASA EMBARGO]](http://repository.ub.ac.id/style/images/fileicons/text.png) |
Text (DALAM MASA EMBARGO)
Achmad Taufik.pdf Restricted to Registered users only until 31 December 2024. Download (5MB) |
Actions (login required)
 |
View Item |