Pengaruh Variasi Suhu Pada Proses Sintering Terhadap Kekerasan Dan Mikrostruktur Paduan Magnesium Dan Hydroxyapatite.

Nararita, Rachma Gusti and Teguh Dwi Widodo, ST., M.Eng., Ph.D. and Rudianto Raharjo, ST., MT. (2023) Pengaruh Variasi Suhu Pada Proses Sintering Terhadap Kekerasan Dan Mikrostruktur Paduan Magnesium Dan Hydroxyapatite. Sarjana thesis, Universitas Brawijaya.

Abstract

Pengembahangan biomaterial sintesis menjadi perhatian kalangan peneliti pada beberapa tahun terakhir, hal ini dikarenakan telah membantu banyak dalam meningkatkan efisiensi bedah ortopedi. Paduan Magnesium dan Hidroksiapatit diteliti dapat digunakan sebagai implan biodegradabe yang aman untuk tubuh manusia, beberapa kelebihan utama dari magnesium adalah sifat mekanik yang menyerupai tulang dan biokompabilitasnya yang baik. Dalam tubuh manusia implan magnesium akan mengalami proses degradasi secara alami atau yang biasa disebut implan biodegradable, dimana tidak diperlukan tindakan pembedahan lanjutan untuk pengangkatan implan ketika tulang telah sembuh . Penelitian ini bertujuan untuk mengetahui pengaruh variasi temperatur pada proses sintering terhadap sifat mekanik dan mikrostruktur pada paduan Mg-HAp. Pada penelitian ini dilakukan sintesis untuk menghasilkan paduan logam Mg-HAp. Variasi temperatur sintering yang digunakan adalah 480⁰C, 490⁰C, 500⁰C, 510⁰C, dan 520⁰C dengan waktu holding 30 menit. Penelitian ini menggunakan metode metalurgi serbuk dengan komposisi paduan 90% Magnesium dan 10% Hidroksiapatit dan tekanan kompaksi sebesar 12 Mpa dalam cetakan berbentuk silinder. Penelitian ini dilakukan dengan beberapa pengujian diantaranya, uji kekerasan untuk mengetahui karakteristik sifat mekanik paduan biodegradable Mg-HAp, uji foto makro untuk analisis bentuk persebaran unsur dan pengamatan permukaan spesimen, uji SEM untuk mengetahui morfologi permukaan dan uji densitas untuk mengetahui hasil kualitas dari produk metalurgi serbuk dengan melihat nilai kepadatan rata – rata spesimen paduan Mg-HAp. Dari hasil uji Kekerasan menunjukkan proses sintering dengan temperatur 500⁰C mempunyai nilai kekerasan terbaik dengan nilai sebesar 51,56 HV. Hasil uji densitas menunjukkan nilai terbaik yaitu sebesar 1,8718 g/cm3 pada spesimen dengan temperatur 500⁰C pada proses sintering.

English Abstract

The development of synthetic biomaterials has become a concern among researchers in recent years, this is because it has helped a lot in increasing the efficiency of orthopedic surgery. The alloy of Magnesium and Hydroxyapatite studied can be used as a biodegradable implant that is safe for the human body. Some of the main advantages of magnesium are its mechanical properties of resembling bone and its good biocompatibility. In the human body, magnesium implants will experience a natural degradation process or what is commonly called biodegradable implants, where no further surgery is required to remove the implant when the bone has healed. This study aims to determine the effect of temperature variations in the sintering process on the mechanical and microstructural properties of the Mg-HAp alloy. In this research, synthesis was carried out to produce Mg-HAp metal alloy. Variations of sintering temperature used were 480⁰C, 490⁰C, 500⁰C, 510⁰C and 520⁰C with a holding time of 30 minutes. This study used a powder metallurgy method with an alloy composition of 90% Magnesium and 10% Hydroxyapatite and a compaction pressure of 12 MPa in a cylindrical mold. This research was carried out with several tests including, hardness test to determine the mechanical properties of biodegradable Mg-HAp alloy, macro photo test to analyze the shape of the element distribution and observation of the surface of the specimen, SEM test to determine the surface morphology and density test to determine the quality results of metallurgical products. powder by looking at the average density value of the Mg-HAp alloy specimens. The results of the hardness test showed that the sintering process at 500⁰C had the best hardness value with a value of 51.56 HV. The results of the density test showed that the best value was 1.8718 g/cm3 for the specimen at 500⁰C during the sintering process.

Item Type:	Thesis (Sarjana)
Identification Number:	052307
Uncontrolled Keywords:	Magnesium, Hydroxyapatite, Implan biodegradable, Metalurgi Serbuk, Nilai Kekerasan, Mikrostruktur, Magnesium, Hydroxyapatite, Biodegradable Implant, Powder Metallurgy, Hardness Value, Microstructure.
Divisions:	Fakultas Teknik > Teknik Mesin
Depositing User:	Zainul Mustofa
Date Deposited:	18 Jan 2024 02:37
Last Modified:	18 Jan 2024 02:37
URI:	http://repository.ub.ac.id/id/eprint/211840

Text (DALAM MASA EMBARGO) Rachma Gusti Nararita.pdf Restricted to Registered users only until 31 December 2025. Download (4MB)

Actions (login required)

View Item