Pengaruh Fraksi Berat Cangkang Telur Ayam Ras Petelur terhadap Penurunan Temperatur Ruangan dengan Proses Coating pada Atap Galvanis.

Ramadani, Octafian Pramana and Ir. Redi Bintarto, ST., M.Eng.Pract. and Moch. Syamsul Ma’arif, ST., MT. (2023) Pengaruh Fraksi Berat Cangkang Telur Ayam Ras Petelur terhadap Penurunan Temperatur Ruangan dengan Proses Coating pada Atap Galvanis. Sarjana thesis, Universitas Brawijaya.

Abstract

Penggunaan baja galvanis sebagai bahan atap bangunan memiliki beberapa kekurangan, salah satunya baja galvanis memiliki nilai konduktivitas termal yang tinggi sehingga dapat meningkatkan temperatur ruangan. Dengan demikian baja galvanis membutuhkan proses coating dengan tujuan dapat menurunkan temperatur ruangan. Proses coating dilakukan menggunakan komposit antara cangkang telur ayam ras petelur dan resin epoxy. Penelitian ini bertujuan untuk mngetahui pengaruh fraksi berat cangkang telur ayam ras petelur terhadap penurunan temperatur ruangan dengan proses coating pada atap galvanis. Penelitian ini merupakan penelitian eksperimen nyata dengan melakukan coating pada plat galvanis menggunakan campuran antara cangkang telur ayam ras petelur dan epoxy dengan komposisi fraksi berat 0%:100%, 20%:80%, 30%:70%, 40%:60% dan 50%:50%. Spesimen plat galvanis nantinya diletakkan di atas alat uji penurunan temperatur berbentuk kubus dengan panjang setiap sisinya 50 cm × 50 cm × 50 cm. Alat uji penurunan temperatur dilengkapi dengan 4 sensor suhu dengan posisi yang berbeda, dimana sensor 1 terletak 20 cm di atas permukaan galvanis, sensor 2 terletak di atas permukaan galvanis, sensor 3 terletak di bagian bawah galvanis dan sensor 4 terletak di bagian dalam ruangan berjarak 10 cm dari dasar alat uji. Pengujian ini dilakukan dengan mencatat temperatur setiap 1 menit sekali selama 10 menit. Pada pengujian konduktivitas termal didapatkan nilai tertinggi pada spesimen dengan fraksi berat 0%:100% dengan nilai 1,59 W/m ℃, sedangkan nilai terendah terdapat pada fraksi berat 50%:50% dengan nilai 0,25 W/m ℃. Hasil analisis pesebaran serbuk cangkang telur pada foto makroskopik didapatkan tingkat kemerataan paling tinggi pada fraksi berat 50%:50% dengan presentase 99,12 %. Kemudian pada pengujian penurunan temperatur didapatkan hasil penurunan temperatur paling rendah pada fraksi berat 0%:100% dengan nilai 0,164 ℃ dan penurunan temperatur paling tinggi terdapat pada fraksi berat 50%:50% dengan nilai 0,962 ℃. Sehingga dapat disimpulkan dengan semakin besar fraksi berat cangkang telur yang digunakan dalam komposit maka penurunan temperatur yang dihasilkan akan semakin besar.

English Abstract

The use of galvanized steel as a building roofing material has several drawbacks, one of which is that galvanized steel has a high thermal conductivity value so that it can increase room temperature. Thus galvanized steel requires a coating process with the aim of lowering the room temperature. The coating process is carried out using a composite between egg shells of laying hens and epoxy resin. This study aims to determine the effect of the weight fraction of eggshell laying hens on decreasing room temperature by coating the galvanized roof. This research is a real experimental research by coating the galvanized plate using a mixture of egg shells of laying hens and epoxy with a weight fraction composition of 0%:100%, 20%:80%, 30%:70%, 40%:60% and 50%:50%. The galvanized plate specimen will then be placed on a cube-shaped temperature drop tester with a side length of 50 cm × 50 cm × 50 cm. The temperature drop tester is equipped with 4 temperature sensors in different positions, where sensor 1 is located 20 cm above the galvanized surface, sensor 2 is located above the galvanized surface, sensor 3 is located at the bottom of the galvanized and sensor 4 is located on the inside of the room 10 cm from the base of the test apparatus. This test is carried out by recording the temperature every 1 minute for 10 minutes. In the thermal conductivity test, the highest value was obtained for the specimen with a weight fraction of 0%:100% with a value of 1.59 W/m ℃, while the lowest value was found in a heavy fraction of 50%:50% with a value of 0.25 W/m ℃. The results of the analysis of the distribution of eggshell powder on macroscopic photos obtained the highest level of evenness in the weight fraction of 50%:50% with a percentage of 99.12%. Then in the temperature reduction test, the lowest temperature decrease was found in the 0%:100% weight fraction with a value of 0.164 ℃ and the highest temperature decrease was in the 50%:50% weight fraction with a value of 0.962 ℃. So it can be concluded that the greater the weight fraction of the eggshell used in the configuration, the lower temperature is.

Item Type:	Thesis (Sarjana)
Identification Number:	052307
Uncontrolled Keywords:	Coating, Cangkang Telur, Atap Galvanis, Fraksi Berat, Penurunan Temperatur, Konduktivitas Termal, Coating, Eggshell, Galvanized Roof, Weight Fraction, Temperature Drop, Thermal Conductivity.
Divisions:	Fakultas Teknik > Teknik Mesin
Depositing User:	Zainul Mustofa
Date Deposited:	17 Jan 2024 02:47
Last Modified:	17 Jan 2024 02:47
URI:	http://repository.ub.ac.id/id/eprint/211281

Text (DALAM MASA EMBARGO) Octafian Pramana Ramadani.pdf Restricted to Registered users only until 31 December 2025. Download (14MB)

Actions (login required)

View Item