Pengaruh Variasi Temperatur Substrat Pada High Temperature Erosion Menggunakan Coal Fly Ash Terhadap Laju Erosi Pada Baja ASME SA210.

Putra, Naufal Harda and Teguh Dwi Widodo, ST., M.Eng., Ph.D and Rudianto Raharjo, ST., MT. (2023) Pengaruh Variasi Temperatur Substrat Pada High Temperature Erosion Menggunakan Coal Fly Ash Terhadap Laju Erosi Pada Baja ASME SA210. Sarjana thesis, Universitas Brawijaya.

Abstract

Penggunaan batu bara dalam pembangkitan listrik menjadi kebutuhan yang tinggi bagi kehidupan manusia. Pada boiler berbahan bakar batu bara sering dijupai peristiwa erosi dalam boiler yang menyebabkan kerusakan pada permukaan pipa-pipa yang berada dalam boiler. ASME SA210 Gr C adalah jenis baja yang biasa digunakan dalam pipa-pipa waterwall yang terdapat pada boiler. Dalam penelitian ini akan diamati bagaimana erosion rate yang terjadi pada baja ASME SA210 Gr C dengan kondisi high temperature erosion berdasarkan standar ASTM G211. Variasi temperature substrat yang digunakan adalah 200, 300, 400, 500, 600oC. Dengan perlakuan erosi dilakukan selama 600s sebanyak lima siklus di tiap spesimenya. Tiap variasi temperatur terdapat dua macam spesimen yaitu spesimen erosi dan non erosi. Kedua spesimen akan dicari selisihnya guna untuk mengeliminasi massa dari oxide layer yang terbentuk selama pengujian berlangsung. Hasil penelitian ini menunjukkan bahwa variasi temperature substrat dapat meningkatkan nilai erosion rate yang terjadi pada high temperature erosion. Semakin tinggi temperature substrat maka mekanikal properties dari suatu baja akan menurun yang akan mempermudah terjadinya deformasi, Sehingga ketika permukaan specimen baja di beri perlakukan erosi partikel padat pada kondisi temperature tinggi tersebut material akan mudah untuk di pindahkan dari tempat awalnya. Hal itu akan menyebabkan kehilangan massa pada material yang akan bisa memperbesar perbedaan massa sebelum dan sesudah material diberikan perlakuan erosi. Erosion rate pada suhu substrat 200-500oC akan meningkat secara perlahan, namun pada suhu substrat 600oC akan meningkat secara signifikan, yakni mencapai 1,0141 mg/gr. Angka tersebut meningkat 4046% dibandingkan dengan erosi yang terjadi di variasi temperatur 200oC.

English Abstract

The use of coal in electricity generation is a high demand for human life. In coalfired boilers, there are often erosion events in the boiler that cause damage to the surface of the pipes in the boiler. ASME SA210 Gr C is a type of steel commonly used in waterwall pipes found in boilers. In this study, it will be observed how the erosion rate occurs in ASME SA210 Gr C steel with high temperature erosion conditions based on ASTM G211 standards. The substrate temperature variations used are 200, 300, 400, 500, 600oC. With erosion treatment carried out for 600s as many as five cycles in each specimen. Each temperature variation has two kinds of specimens, namely erosion and non-erosion specimens. Both specimens will be searched for the difference in order to eliminate the mass of the oxide layer formed during the test. The results of this study indicate that variations in substrate temperature can increase the erosion rate value that occurs in high temperature erosion. The higher the substrate temperature, the mechanical properties of a steel will decrease which will facilitate deformation, so that when the surface of the steel specimen is treated with solid particle erosion under high temperature conditions the material will be easy to move from its original place. This will cause mass loss in the material which will be able to increase the mass difference before and after the erosion. Erosion rate at substrate temperature 200-500oC will increase slowly, but at 600oC substrate temperature will increase significantly, reaching 1.0141 mg/gr. This figure increased by 4046% compared to the erosion that occurred in the 200oC temperature variation.

Item Type:	Thesis (Sarjana)
Identification Number:	052307
Uncontrolled Keywords:	High Temperature Erosion, Coal Fly Ash, Erosion Rate, ASME SA210.
Divisions:	Fakultas Teknik > Teknik Mesin
Depositing User:	Zainul Mustofa
Date Deposited:	16 Jan 2024 02:30
Last Modified:	16 Jan 2024 02:30
URI:	http://repository.ub.ac.id/id/eprint/210681

Text (DALAM MASA EMBARGO) Naufal Harda Putra.pdf Restricted to Registered users only until 31 December 2025. Download (10MB)

Actions (login required)

View Item