Pengaruh Coating Komposit Campuran Epoxy Dan Jenis Bata Ringan AAC Pada Atap Galvanis Terhadap Penurunan Temperatur Ruangan

Fahri, Fauzan and Ir. Redi Bintarto,, ST., M. Eng.Pract and Ir. Tjuk Oerbandono,, M.Sc.CSE (2023) Pengaruh Coating Komposit Campuran Epoxy Dan Jenis Bata Ringan AAC Pada Atap Galvanis Terhadap Penurunan Temperatur Ruangan. Sarjana thesis, Universitas Brawijaya.

Abstract

Penggunaan Baja Galvanis pada atap tentunya memiliki kekurangan, salah satunya pada sifat dasar baja itu sendiri yaitu sifat konduktivitas termal yang besar. Salah satu cara yang dapat dilakukan adalah dengan menambahkan material dengan konduktivitas termal yang lebih rendah. Suhu nyaman bagi orang Indonesia berkisar antara 22,8-25,8ºC. namun kerapkali ditemukan suhu ruangan dapat mencapai 35ºC. Hal ini dapat mengurahi kenyamanan di dalam ruangan dan menyebabkan meningkatnya penggunaan benda elektronik yang membantu untuk menurunkan temperatur ruangan. Dari meningkatnya penggunaan benda elektronik tersebut dapat meningkatkan penggunaan energi. Oleh karena itu insulasi termal sangat penting pada bangunan untuk menekan penggunaan energi. Material yang digunakan dalam penelitian ini adalah serbuk bata ringan AAC. Serbuk bata ringan AAC dipilih karena bata ringan AAC memiliki nilai konduktivitas termal yang rendah, sehingga diharapkan setelah proses pelapisan, konduktivitas termal baja galvanis serta suhu ruangan dapat menurun. Dari keempat jenis tersebut memiliki jumlah si yang berbeda. Pengaruh banyaknya si pada serbuk bata ringan dapat menurunkan nilai konduktivitas thermal pada atap galvanis. Komposisi si pada masing-masing jenis serbuk bata ringan adalah 21% untuk bata ringan Blesscon, 21,1% untuk bata ringan bricon, 22,5% untuk bata ringan citicon, 22,7% untuk bata ringan fastcon. Dari hasil penelitian yang dilakukan didapati bahwa atap galvanis dengan coating serbuk bata ringan fastcon memiliki konduktivitas thermal yang paling rendah sehingga dapat menurunkan temperature ruangan hingga 2,1 ºC

English Abstract

The use of Galvanized Steel for roofs certainly has drawbacks, one of which is the basic properties of the steel itself, namely its high thermal conductivity. One way that can be done is to add a material with a lower thermal conductivity. The comfortable temperature for Indonesians ranges from 22.8-25.8ºC. but often found room temperature can reach 35ºC. This can reduce the comfort in the room and lead to increased use of electronic devices that help to lower the room temperature. From the increased use of electronic objects can increase energy use. Therefore thermal insulation is very important in buildings to reduce energy use. The material used in this research is AAC light brick powder. AAC lightweight brick powder was chosen because AAC lightweight brick has a low thermal conductivity value, so it is expected that after the coating process, the thermal conductivity of galvanized steel and room temperature can decrease. Of the four types, the number of si is different. The effect of the amount of Si on light brick powder can reduce the value of thermal conductivity on galvanized roofs. The si composition of each type of lightweight brick powder is 21% for Blesscon lightweight brick, 21.1% for bricon lightweight brick, 22.5% for Citicon lightweight brick, 22.7% for Fastcon lightweight brick. From the results of the research conducted, it was found that the galvanized roof with fastcon light brick powder coating has the lowest thermal conductivity so that it can reduce the room temperature to 2.1 ºC

Item Type:	Thesis (Sarjana)
Identification Number:	052307
Uncontrolled Keywords:	bata ringan, komposit, galvanis, resin epoxy, penurunan temperatur, coating - Autoclaved Aerated Concrete, composite, galvanized, epoxy resin, temperature decrease, coating.
Divisions:	Fakultas Teknik > Teknik Mesin
Depositing User:	Unnamed user with username pratiwi
Date Deposited:	11 Jan 2024 02:10
Last Modified:	11 Jan 2024 02:10
URI:	http://repository.ub.ac.id/id/eprint/207845

Text (DALAM MASA EMBARGO) FAHRI FAUZAN.pdf Restricted to Registered users only until 31 December 2025. Download (7MB)

Actions (login required)

View Item