Pramaiswari, Made Adelia and drg. Sinta Candra Wardani, M. Biomed (2023) Potensi mengembang (swelling) Pada Hidrogel Komposit Chitosan-Nanopartikel Demineralized Freeze Dried Bovine Bone Xenograft (DFDBBX-NPs). Sarjana thesis, Universitas Brawijaya.
Abstract
Latar Belakang: Pencabutan gigi dapat menyebabkan perubahan dimensi yang irreversible pada alveolar ridge karena adanya resorpsi tulang. Resopsi tulang dapat dicegah dengan preservasi soket menggunakan bone graft. Partikel DFDBBX digunakan dalam prosedur bone graft karena dapat terdegradasi sepenuhnya memungkinkan regenerasi tulang yang lebih baik dibandingkan dengan DBBM. Tujuan : Mengetahui potensi mengembang (swelling) pada hidrogel komposit chitosan-nanopartikel demineralized freeze dried bovine bone xenograft (DFDBBX-NPs). Metode: Uji swelling yaitu dengan menimbang sampel sebelum direndam dan sesudah di rendam kemudian dihitung dengan rumus swelling ratio. Hasil :Hasil uji ANOVA menunjukkan perbandingan konsentrasi terhadap periode waktu yang berbeda diperoleh rata-rata terbesar pada konsentrasi 1% pada periode waktu 24 jam. Hasil total swelling ratio yang paling efektif saat dipengaruhi oleh periode waktu berbeda terdapat pada konsentrasi 2 wt% pada uji regresi. Kesimpulan: Terdapat perbedaan dari potensi mengembang (swelling) pada hidrogel komposit chitosan-nanopartikel demineralized freeze dried bovine bone xenograft (DFDBBX-NPs) dalam periode waktu yang berbeda (3, 6, 12, 24 jam).
English Abstract
Background: Tooth extraction can cause irreversible dimensional changes in the alveolar ridge due to bone resorption. Bone resorption can be prevented by preserving the socket using bone graft. DFDBBX particles are used in bone graft procedures because they are fully degradable allowing better bone regeneration compared to DBBM. The Purpose: To determine the swelling potential of demineralized freeze dried bovine bone xenograft (DFDBBX-NPs) chitosannanoparticle composite hydrogel. Method: Swelling test is by weighing the sample before soaking and after soaking and then calculating it using the swelling ratio formula. Results: The results of the ANOVA test show that the highest average concentration for different time periods was obtained at a concentration of 1% in the 24 hour time period. The most effective total swelling ratio results when influenced by different time periods were at a concentration of 2% by weight in the regression test. Conclusion: There are differences in the swelling potential of the chitosan-nanoparticle composite hydrogel demineralized freeze dried bovine bone xenograft (DFDBBX-NPs) in different time periods (3, 6, 12, 24 hours).
| Item Type: | Thesis (Sarjana) |
|---|---|
| Identification Number: | 052314 |
| Uncontrolled Keywords: | Bone graft, scaffold, nanopartikel, uji swelling - Bone grafts, scaffolds, nanoparticles, swelling tests |
| Divisions: | Fakultas Kedokteran Gigi > Kedokteran Gigi |
| Depositing User: | Emy Sukartini |
| Date Deposited: | 10 Jan 2024 08:40 |
| Last Modified: | 10 Jan 2024 08:40 |
| URI: | http://repository.ub.ac.id/id/eprint/207606 |
![[thumbnail of Dalam masa EMBARGO]](http://repository.ub.ac.id/style/images/fileicons/text.png) |
Text (Dalam masa EMBARGO)
Made Adelia Pramaiswari.pdf Restricted to Registered users only until 31 December 2025. Download (10MB) |
Actions (login required)
 |
View Item |