Pengaruh Perendaman CD-R dengan Ethanol terhadap Produksi Hidrogen pada Proses Elektrolisis Air.

Hidayat, Muhammad Aidil Akbar and Dr. Purnami, ST., MT. and Winarto, ST., MT., Ph.D. (2023) Pengaruh Perendaman CD-R dengan Ethanol terhadap Produksi Hidrogen pada Proses Elektrolisis Air. Sarjana thesis, Universitas Brawijaya.

Abstract

Hidrogen merupakan energi baru terbarukan yang tersedia melimpah di alam, memiliki sifat bebas karbon serta kandungan energi yang tinggi. Dari sekian banyak metode, didapatkan bahwa metode elektrolisis air merupakan metode yang paling sesuai dalam memproduksi hidrogen dikarenakan harga perangkat yang murah, ramah lingkungan, dan akan menghasilkan tingkat kemurnian hidrogen yang tinggi. Namun, beban energi dalam proses elektrolisis masih tergolong rendah daripada proses lainnya. Sehingga menyebabkan penambahan energi pada elektrolisis akan menyebabkan biaya yang besar. Salah satu solusi untuk mengatasi permasalahan tersebut adalah dengan memvariasikan katalis yang digunakan dalam proses elektrolisis air. Media penyimpanan informasi lama yang dikenal dengan Compact Disc Recordable (CD-R) yang sudah ditinggalkan seiring dengan perkembangan zaman, mengandung bahan - bahan elektronik organik yang dapat dimanfaatkan kembali saat ini. Oleh karena itu pada penelitian ini digunakan katalis berupa bahan organik dari lapisan CD-R yang lapisan terluarnya dihilangkan dengan dilakukannya perendaman dengan ethanol. CD-R memiliki beberapa lapisan diantaranya lapisan polikarbonat, lapisan pewarna sianin dan lapisan Perak (Ag). Pada penelitian ini, CD-R direndam dengan ethanol selama 0 menit (tidak direndam), 10 menit, 30 menit, 1 jam, dan 2 jam. Semakin lama perendaman CD-R dengan ethanol, lapisan pada CD-R semakin banyak yang terkelupas. Hal tersebut dapat dilihat pada pengujian SEM, EDS, dan XRR yang telah dilakukan. Selain itu, lama perendaman CD-R dengan ethanol juga akan meningkatkan produksi hidrogen akibat lapisan pewarna sianin dan lapisan Ag pada CD-R semakin mudah berinteraksi dengan larutan elektrolit saat terjadinya proses elektrolisis.

English Abstract

Hydrogen is a renewable energy that is abundantly available in nature, has carbon-free properties and high energy content. On the other hand, it was found that the water electrolysis method is the most suitable one over many methods for producing hydrogen. It is because the price of the equipment is cheap, friendly-environmental, and it would produce a high level of hydrogen purity. However, the energy load in the electrolysis process is still relatively lower over any process, thus it causes the addition of energy in electrolysis then it would cost a lot. One solution to overcome this problem is to vary the catalyst that is used in the water electrolysis process. Old information storage media as known as Compact Disc Recordable (CD-R) that has been abandoned because of the time, contains organic materials that can be reused nowadays. Therefore, in this study, a catalyst was used in the form of organic from the CD-R layer that the outermost layer was removed by immersion in ethanol. CD-R has several layers including a layer of polycarbonate, cyanine dye, and silver (Ag). In this study, CD-R was soaked in for 0 minutes (not being soaked), 10 minutes, 30 minutes, 1 hour, 2 hours. As long as CD-R being soaked in the ethanol, it would make the layers on the CD-R peel off. This can be seen in the SEM, EDS, and XRR tests that have been carried out. In addition, the duration of immersing the CD-R with the ethanol would also increase the hydrogen production due to the cyanine dye layer and the Ag layer on the CD-R more easily interacting with electrolyte solution during the electrolysis process.

Item Type:	Thesis (Sarjana)
Identification Number:	052307
Uncontrolled Keywords:	Hidrogen, Elektrolisis, CD-R, Ethanol, Hydrogen, Electrolysis, CD-R, Ethanol.
Divisions:	Fakultas Teknik > Teknik Mesin
Depositing User:	Zainul Mustofa
Date Deposited:	10 Jan 2024 06:32
Last Modified:	10 Jan 2024 06:32
URI:	http://repository.ub.ac.id/id/eprint/207423

Text (DALAM MASA EMBARGO) Muhammad Aidil Akbar Hidayat.pdf Restricted to Registered users only until 31 December 2025. Download (24MB)

Actions (login required)

View Item