Karakterisasi Zinc Oxide Nano-partikel yang disintesis Secara Green Synthesis oleh Ekstrak Daun Physalis Angulata Linn serta Zinc Nitrate Hexahydrate (Uji Spektrofotometri dengan UV-Vis)”

Adhuri, Amyra Rachmi and drg. Delvi Fitrani, M. Kes. (2023) Karakterisasi Zinc Oxide Nano-partikel yang disintesis Secara Green Synthesis oleh Ekstrak Daun Physalis Angulata Linn serta Zinc Nitrate Hexahydrate (Uji Spektrofotometri dengan UV-Vis)”. Sarjana thesis, Universitas Brawijaya.

Abstract

Zinc oxide eugenol (ZOE) walau dikenal sebagai bahan sementasi sementara dengan manfaatnya yang paling banyak ternyata dapat menghasilkan reaksi toksik pada pulpa. Selain itu, ZOE juga lemah dalam kekuatan mekanik dan kekakuan. Maka dari itu, zinc oxide nano partikel (ZnONPs) diharapkan dapat menjadi solusinya. Zinc oxide nano-partikel dapat disintesis secara green synthesis dengan manfaat yang paling banyak karena mudah, murah dan aman. Penelitian ini menggunakan ekstrak daun Physalis angulata Linn karena kandungan fitokimianya berperan aktif sebagai reduktor dan capping agent sehingga memicu pembentukan nano-partikel yang relatif stabil. Untuk menghasilkan dengan kondisi optimum, proses biosintesis ZnONPs ini dapat dipengaruhi oleh konsentrasi ekstrak tumbuhan dan zinc precursor. Penelitian ini menguji lima macam sample menggunakan ekstrak daun Physalis angulata Linn konsentrasi 100%, 50% dan 25% dan precursor zinc nitrate hexahydrate konsentrasi 0,1 M, 0,05 M dan 0,01 M. Kelima sample ini diuji dengan spektrofotometri UV-Vis dan terbukti bahwa ekstrak daun Physalis angulata Linn berpengaruh terhadap ukuran ZnONPs dan precursor zinc nitrate hexaydrate konsentrasi 0,05 M dan 0,01 M memiliki puncak absorbansi dan intesitas yang sama tetapi ZnONPs dengan konsentrasi zinc nitrate hexahydrate 0,1 M adalah berbeda

English Abstract

Zinc oxide eugenol (ZOE) although known as a tempororay cementation material with the most benefits can actually produce a toxic reaction in the pulp. In addition, ZOE is also weak in mechanical strength and rigidity. Therefore, zinc oxide nanoparticles (ZnONPs) are expected to be the solution. Zinc oxide nano-particles can be synthesized by green synthesis with the most benefits because it is easy, cheap and safe. This study used Physalis angulata Linn leaf extract because its phytochemical content plays an active role as a reducing agent and capping agent, thus triggering the formation of relatively stable nano-particles. To produce with optimum conditions, the ZnONPs biosynthesis process can be influenced by the concentration of plant extracts and zinc precursors. This study tested five kinds of samples using Physalis angulata Linn leaf extract concentrations of 100%, 50% and 25% and precursor zinc nitrate hexahydrate concentrations of 0.1 M, 0.05 M and 0.01 M. These five samples were tested by UV-spectrophotometry. It was proven that Physalis angulata Linn leaf extract had an effect on the size of ZnONPs and zinc nitrate hexaydrate precursors with concentrations of 0.05 M and 0.01 M had the same absorbance and intensity peaks but ZnONPs with a concentration of 0.1 M zinc nitrate hexahydrate were different.

Item Type:	Thesis (Sarjana)
Identification Number:	052314
Uncontrolled Keywords:	Zinc Oxide Nano-partikel, Esktrak Daun Physalis Angulata Linn, Precursor Zinc Nitrate Hexahydrate - Zinc Oxide Nanoparticles, Leaf Extract of Physalis angulata Linn, Precursor Zinc Hexahydrate
Divisions:	Fakultas Kedokteran Gigi > Kedokteran Gigi
Depositing User:	Emy Sukartini
Date Deposited:	09 Jan 2024 07:26
Last Modified:	10 Jan 2024 01:18
URI:	http://repository.ub.ac.id/id/eprint/206493

Text (Dalam masa EMBARGO) AMYRA RACHMI ADHURI.pdf Restricted to Registered users only until 31 December 2025. Download (2MB)

Actions (login required)

View Item