Analisa Perubahan Arus Las Terhadap Siklus Termal Dan Sifat Mekanik Pengelasan GTAW (Gas Tungsten Arc Welding) Pada Material Similar Plat Stainless Steel 304

Nugraha, I’an Shofwan (2023) Analisa Perubahan Arus Las Terhadap Siklus Termal Dan Sifat Mekanik Pengelasan GTAW (Gas Tungsten Arc Welding) Pada Material Similar Plat Stainless Steel 304. Sarjana thesis, Universitas Brawijaya.

Abstract

Penelitian ini bertujuan untukmengetahui seberapa besar pengaruh perubahan variasi arus pengelasan GTAW (Gas Tungsten Arc Welding) pada sambungan las platStainless Steel304 terhadap siklus termal serta Sifat kekerasan dan kekekuatan tarik. Penelitian ini merupakan penelitianexperimentalnyatapengujian siklus termal, uji kekerasan dan uji tarik. Pada ujiPada pengujian Siklus termal pada pengelasan dilakukan denganmenggunakann tegangan sebesar 200 volt dengan kecepatan laju pengelasan0,1 mm/s. Perbedaan dititik puncak dari beberpa variasi arus,pada variasi arus 35Ampere memiliki titik puncak sebesar 445℃ serta meupakan titik puncak terendah dari pengujian ini. Selainitu pada variasi arus 40Amperememiliki titik puncak sebesar 448℃.Sedangkan pada variasi arus 45Amperememiliki titik puncak yang lebih besar dari beberapa variasi arusyanglainnya yaitu sebesar 458℃. Pada pengujian kekerasanpada titik jarak 0 mm setiap variasi arus memiliki nilai yang berbeda melihat lebih besar variasi arus yang di gunakan akan semarin tinggi nilai kekerasannya. Pada titik 2 mm menghasilkan pada variasi arus 45A lebih kecil dibandingkan dengan variasi arus 40A. Sedangkan pada titik 6 mm menghasilkan variasi arus 35A menghasilan nilai kekerasan yanglebih besar, sedangkan variasi arus 45A menghasilkan kekerasan yang lebih kecil dari variasi arus 35A dan 40A. Pada pengujian tarikhasilnilai tegangan yang paling besar pada variasi arus 45 Amperesebesar490Mpa sedangkan nilai tegangan yang paling kecil terdapat pada variasi arus 35 Amperesebesar482.3Mpa. Nilai regangan yang paling besar pada variasi arus 40 Ampere21.47% , sedangkan nilai tegangan yang paling kecil terdapat pada variasi arus 35 Ampere17.18%. Nilaimodulus elastisitasyang paling besar pada variasi arus 35Ampere 29.08MPa sedangkan nilaimodulus elastisitasyang paling kecil terdapat pada variasi arus 40Ampere25.22MPa.

English Abstract

This study aims to determine how much influence the change in GTAW (Gas Tungsten Arc Welding) welding current variations on 304Stainless Steelplate welding joints on thermal cycles and hardness and tensile strength properties. This research is a real experimental research of thermal cycle testing, hardness test and tensile test. In the test, the thermal cycle test on welding was carried out using a voltage of 200 volts with a welding speed rate of 0.1mm / s. The difference in the peak point of several current variations, in the 35Amperecurrent variation has a peak point of 445 ℃ and is the lowest peak point of this test. In addition, the 40Amperecurrent variation has a peak point of 448 ℃. While the 45Amperecurrent variation has a peak point that isgreater than several other current variations, which is 458 ℃. In tensile testing the results of the largest voltage value in the 45Amperecurrent variation of 490 Mpa while the smallest voltage value is found in the 35Amperecurrent variation of 482.3Mpa. The largest strain value in the 40Amperecurrent variation is 21.47%, while the smallest stress value is found in the 35Amperecurrent variation of 17.18%. The largest elastic modulus value in the 35Amperecurrent variation is 29.08 MPa while the smallest elastic modulus value is found in the 40Amperecurrent variation of 25.22 MPa.

Item Type:	Thesis (Sarjana)
Identification Number:	0523070002
Uncontrolled Keywords:	Stainless Steel 304,GTAW, Kekerasan, Tarik,SiklusTermal, Tegangan,Regangan, Modulus Elastisitas
Divisions:	Fakultas Teknik > Teknik Mesin
Depositing User:	agung
Date Deposited:	09 Jan 2024 03:19
Last Modified:	09 Jan 2024 03:19
URI:	http://repository.ub.ac.id/id/eprint/206381

Text (DALAM MASA EMBARGO) I'AN SHOFWAN NUGRAHA.pdf Restricted to Repository staff only until 31 December 2025. Download (10MB)

Actions (login required)

View Item