Pengaruh Variasi Penataan Serat Daun Sisal Pada Proses Coating Atap Galvalum Terhadap Tingkat Penurunan Temperatur Ruangan.

Bhakti, Sadam Kresna and Redi Bintarto, ST., M.Eng.Pract. and Moch. Syamsul Ma’arif, ST., MT. (2023) Pengaruh Variasi Penataan Serat Daun Sisal Pada Proses Coating Atap Galvalum Terhadap Tingkat Penurunan Temperatur Ruangan. Sarjana thesis, Universitas Brawijaya.

Abstract

Temperatur bangunan yang meningkat akibat dari radiasi sinar matahari yang masuk dapat menyebabkan ketidaknyamanan bagi penghuni bangunan. Kondisi seperti itu membuat penghuni bangunan menggunakan air conditioner (AC). Cara yang paling murah memperoleh kenyamanan termal pada penggunaan atap sebuah bangunan yang tentunya sangat berpengaruh terhadap penurunan suhu dan kenyamanan termal dalam ruangan, terutama dalam hal penggunaan material. Salah satu contoh material yang banyak digunakan untuk penggunaan atap bangunan saat ini adalah galvalum. Tetapi menggunakan galvalum memiliki kekurangan karena atap berbahan baja galvalum tentu akan lebih banyak menyerap panas. Untuk itu maka atap galvalum perlu dilapisi agar tidak menyerap panas berlebihan dengan di coating. Coating merupakan teknik pelapisan suatu bahan material di bagian permukaannya untuk melindungi dari pengaruh lingkungan. Dengan ini maka dapat diciptakan suatu insulator termal yang digabungkan dengan atap galvalum untuk membantu penurunan suhu ruangan. Penelitian ini bertujuan untuk mengetahui pengaruh dari variasi penataan serat daun sisal (Agave Sisalana) Uni directional, Bi directional, Random Directional dan Multi Directional sebagai komposit coating terhadap penurunan suhu pada atap galvalum. Pada penelitian ini dilakukan pengujian dengan menggunakan alat uji konduktivitas termal dengan spesimen silindris ukuran diameter 4 cm dan tebal 4 mm. Mesin XRF tipe Miniap 4 digunakan untuk mengetahui komposisi yang terkandung pada serat daun sisal. Foto makroskopis menggunakan kamera digunakan untuk melihat kemerataan dan kerapatan serat daun sisal. Pengujian penurunan temperatur dilakukan dengan meletakkan spesimen menutupi box miniatur ruangan yang memiliki ukuran 50 cm x 50 cm yang telah diletakkan sensor thermocouple pada 4 titik yang menghasilkan temperatur lingkungan, temperatur atap galvalum permukaan atas dan bawah serta temperatur ruangan. Dari data pengujian didapatkan nilai konduktivitas termal dari tertinggi ke terendah yaitu; Uni Directional, Bi Directional, Random Directional dan Multi Directional dengan nilai 0,325925926 ;0,272290048 ;0,26666667 ;0,23058705 W/m.°C. Berdasarkan nilai diatas dapat dilihat bahwa variasi penataan serat daun sisal berpengaruh terhadap penurunan nilai dari konduktivitas termal dimana semakin banyak arah penataan serat maka serat menjadi semakin merata dan rapat sehingga mengakibatkan semakin rendahnya temperatur ruangan. Galvalum dengan coating serat daun sisal dengan variasi penataan multi directional bertindak sebagai pelindung dari bagian atas ruangan yang berkontak langsung dengan matahari sehingga panas yang diteruskan ke dalam ruangan mengalami penurunan yang lebih baik dibandingkan seluruh spesimen lainnya dengan perbedaan temperatur antara galvalum atas dan bawah yaitu 11,111°C.

English Abstract

Building temperature increases as a result of incoming solar radiation can cause inconvenience to building occupants. Such conditions make building occupants use air conditioners (AC). The cheapest way to obtain thermal comfort is by using the roof of a building which of course greatly affects the decrease in temperature and thermal comfort in the room, especially in terms of material use. One example of a material that is widely used for roofing buildings today is galvalum. But using galvalume has drawbacks because a roof made of galvalume steel will certainly absorb more heat. For this reason, the galvalum roof needs to be coated so that it does not absorb excessive heat by coating it. Coating is a technique of coating a material on its surface to protect it from environmental influences. With this, a thermal insulator can be created which is combined with a galvalum roof to help reduce room temperature. This study aims to determine the effect of variations in the arrangement of Uni-directional, Bi-directional, Random Directional and Multi Directional sisal (Agave Sisalana) fiber leaves as a composite layer on the temperature reduction on galvalum roofs. In this study, testing was carried out using a thermal conductivity tester with cylindrical specimens with a diameter of 4 cm and a thickness of 4 mm. Miniap 4 type XRF machine is used to determine the composition contained in the sisal leaf fiber. Macroscopic photos using a camera are used to see the evenness and density of sisal leaf fibers. The temperature drop test was carried out by placing a miniature box cover specimen in a room that had a size of 50 cm x 50cm which had thermocouple sensors placed at 4 points which produced the ambient temperature, the top and bottom surface galvalum roof temperature and the room temperature. From the test data, the thermal conductivity values were obtained from the highest to the lowest, namely; Uni Directional, Bi Directional, Random Directional and Multi Directional with values 0.325925926 ;0.272290048 ;0.26666667 ;0.23058705 W/m.°C. Based on the values above, it can be seen that variations in the arrangement of sisal leaf fibers affect the decrease in the value of thermal conductivity where the more directions the arrangement of the fibers, the more evenly distributed and denser the fibers become, resulting in a lower room temperature. as a protector from the top of the room that is in direct contact with the sun so that the heat that is transmitted into the room decreases better than all other specimens with a temperature difference between the top and bottom galvalum of 11.111°C.

Item Type:	Thesis (Sarjana)
Identification Number:	0523070375
Uncontrolled Keywords:	galvalum, serat daun sisal, resin epoxy, coating, variasi penataan, komposit, konduktivitas termal, penurunan temperatur
Subjects:	600 Technology (Applied sciences) > 621 Applied physics > 621.8 Machine engineering
Divisions:	Fakultas Teknik > Teknik Mesin
Depositing User:	Endang Susworini
Date Deposited:	09 Oct 2023 04:26
Last Modified:	09 Oct 2023 04:26
URI:	http://repository.ub.ac.id/id/eprint/203724

Text (DALAM MASA EMBARGO) SADAM KRESNA BHAKTI.pdf Restricted to Registered users only until 31 December 2025. Download (9MB)

Actions (login required)

View Item