Optimalisasi Parameter Projection Welding Pada Nut M6 Dengan Steelplate Terhadap Kekuatan Pressure Test Menggunakan Metode Taguchi di PT RPA

Ismawan, Faiz Destantyatma and Ir. Sri Widiyawati, ST., MT (2023) Optimalisasi Parameter Projection Welding Pada Nut M6 Dengan Steelplate Terhadap Kekuatan Pressure Test Menggunakan Metode Taguchi di PT RPA. Sarjana thesis, Universitas Brawijaya.

Abstract

Tujuan utama dari suatu perusahaan adalah untuk memperoleh profit / keuntungan untuk tumbuh dan berkembang. Tetapi setiap tahunnya, perusahaan harus menghadapi kenaikan biaya dari beberapa faktor, seperti labor cost (biaya tenaga kerja), material cost (biaya bahan baku), exchange rate impact (perubahan nilai tukar rupiah), dan sebagainya. Jika perusahaan tidak melakukan penghematan / efficiency pada biaya lainnya, maka profit dari perusahaan akan berkurang sehingga perusahaan tidak bisa maju dan berkembang. Jika dibiarkan terus menerus, perusahaan akan mangalami kebangkrutan. Pada penelitian ini dilakukan Desain Eksperimen Taguchi untuk mengoptimalisasi parameter projection welding terhadap kekuatan pressure test pada benda kerja nut M6 dengan steelplate di PT RPA. Parameter tersebut yaitu welding current, air pressure, dan welding time yang masing-masing parameternya memiliki 3 level. Mesin projection welding yang digunakan merupakan mesin las Chuo Spot Welder 50 Kva model S2-6-505 dan mesin pengujian pressure test yang digunakan merupakan Universal Testing Machine (UTM) HT-9501 Series dengan spesimen uji berupa nut M6 berdiameter 6 mm dan steelplate JSH270C dengan tebal sebesar 1,6 mm. Hasil dari Desain Eksperimen Taguchi memperlihatkan bahwa parameter optimal yang disarankan untuk mengoptimalkan nilai kekuatan pressure test merupakan welding current pada setting 11 KA (Level 2) dan air pressure pada setting 0,45 Mpa (Level 2) dengan persen kontribusi welding current sebesar 49,79%, dan air pressure sebesar 36,15%. Perubahan parameter tersebut membuat estimasi biaya produksi per satu pcs menjadi berkurang dari biaya awal sebesar Rp 329,09 menjadi Rp 301,67. Oleh karena itu, estimasi biaya pengelasan produk nut m6 dengan steelplate JSH270C tebal 1,6 mm pada proses projection welding selama setahun dapat dihemat sebesar Rp 197.443.008,00

English Abstract

The main goal of a company is to gain profit / profits to grow and develop. But every year, companies have to face rising costs from several factors, such as labor costs, material costs, exchange rate impacts, and so on. If the company does not make savings/efficiency at other costs, then the profit of the company will decrease so that the company cannot progress and develop. If allowed to continue, the company will experience bankruptcy. In this research, the Taguchi Experimental Design was carried out to optimize the projection welding parameters for the strength of the pressure test on the M6 nut workpiece with steelplate at PT RPA. These parameters are welding current, air pressure, and welding time, each of which has 3 levels. The projection welding machine used is the Chuo Spot Welder 50 Kva welding machine model S2-6-505 and the pressure test testing machine used is the Universal Testing Machine (UTM) H—9501 Series with test specimens in the form of an M6 nut with a diameter of 6 mm and JSH270C steelplate with 1.6mm thick. The results of the Taguchi Experimental Design show that the optimal parameters suggested to optimize the pressure test strength value are welding current at setting 11 KA (Level 2) and air pressure at setting 0.45 Mpa (Level 2) with a percent contribution of welding current of 49.79 %, and air pressure of 36.15%. Changes in these parameters reduced the estimated production cost per one pieces from the initial cost of IDR 329.09 to IDR 301.67. Therefore, the estimated cost of welding a nut m6 product with JSH270C steelplate 1.6 mm thick in the projection welding process for a year can be saved by Rp. 197,443,008.00

Item Type:	Thesis (Sarjana)
Identification Number:	0523070228
Uncontrolled Keywords:	Desain Eksperimen Metode Taguchi, Nut M6, Pressure Test, Resistance Projection Welding, Resistance Welding
Subjects:	600 Technology (Applied sciences) > 670 Manufacturing
Divisions:	Fakultas Teknik > Teknik Industri
Depositing User:	Endang Susworini
Date Deposited:	27 Sep 2023 02:17
Last Modified:	27 Sep 2023 02:17
URI:	http://repository.ub.ac.id/id/eprint/203316

Text (DALAM MASA EMBARGO) Faiz Destantyatma Ismawan.pdf Restricted to Registered users only until 31 December 2025. Download (5MB)

Actions (login required)

View Item