Shidqi, Faisal and Drs. Ir. Moch. Dhofir, M.T and Tri Nurwati,,, S.T, M.T (2023) Pengaruh Lapisan Hidrofobik pada Permukaan Isolator Polietilen Berbentuk Sirip terhadap Tingkat Arus Bocor dan Tegangan Flashover dalam Kondisi Basah dan Kering,. Sarjana thesis, Universitas Brawijaya.
Abstract
Penelitian ini membahas tentang pengaruh lapisan hidrofobik pada permukaan isolator polietilen terhadap arus bocor dan tegangan flashover dengan variasi jumlah sirip. Pada penelitian ini akan diuraikan pengaruh dari lapisan hidrofobik terhadap distribusi medan listrik, tingkat arus bocor, dan tegangan flashover dalam kondisi kering dan basah. Material penyusun isolator yang digunakan adalah polietilen, dengan tiga variasi jumlah sirip yaitu 1 sirip, 2 sirip, dan 3 sirip. Jarak antar elektroda dan jarak rambat dari isolator dibuat sama, dengan pembuatan dimensi yang memperhatikan standar IEC. Metode penelitian yang digunakan adalah dengan mengambil data arus bocor dan tegangan flashover secara langsung di Laboratorium Teknik Tegangan Tinggi Universitas Brawijaya, serta dilakukan simulasi distribusi medan listrik pada masing-masing variasi isolator menggunakan software FEMM 4.2. Pengujian dilakukan dengan menggunakan tegangan tinggi AC, dengan variasi tegangan uji 2, 4, 6, 8, 10, 12 dan 14 kV. Pada pengujian kondisi basah, digunakan tiga variasi debit pembasahan, yaitu 10, 30, dan 60 mL/s yang mengacu pada tren curah hujan di Indonesia. Pada penelitian ini didapatkan bahwa dengan adanya lapisan hidrofobik pada permukaan isolator dan semakin banyak jumlah sirip isolator dengan jarak rambat dan jarak vertikal yang sama akan membuat distribusi medan maksimum dan arus bocornya semakin kecil, sedangkan tingkat homogenitas dan tegangan flashover akan semakin besar. Semakin besar arus bocornya maka tegangan flashover akan semakin kecil. Pada isolator dengan lapisan hidrofobik nilai arus bocor dan tegangan flashover dapat diperbaiki.
English Abstract
This research aims at how a hydrophobic coating on the surface of polyethylene insulators affects leakage currents and flashover voltages as the number of fins changes. The effect of hydrophobic coating on electric field distribution, leakage current level, and flashover voltage in dry and wet conditions will be described in this study. The insulator material is polyethylene, and there are three variations in the number of fins: one, two, and three. By using dimensions that adhere to IEC standards, the distance between the electrodes and the creepage distance from the insulator made the same. The research method used is to collect leakage current and flashover voltage data directly at the High Voltage Engineering Laboratory, University of Brawijaya, and then use FEMM 4.2 software to simulate the electric field distribution on each variation of insulator. High voltage AC was used for the tests, with test voltages ranging from 2, 4, 6, 8, 10, 12, and 14 kV. In the wet condition test, three wetting discharge variations were used, namely 10, 30, and 60 mL/s, which correspond to the trend of rainfall in Indonesia. In this study, it was discovered that the presence of a hydrophobic layer on the surface of the insulator, as well as the greater number of insulator fins with the same creepage distance and vertical distance, reduces the maximum field distribution and leakage current while increasing the level of homogeneity and flashover voltage. The higher the leakage current, the lower the flashover voltage. The leakage current and flashover voltage values of an insulator with a hydrophobic coating can improve.
Other obstract
-
| Item Type: | Thesis (Sarjana) |
|---|---|
| Identification Number: | 0523070227 |
| Uncontrolled Keywords: | isolator, arus bocor, flashover, hidrofobik, polietilen. |
| Subjects: | 600 Technology (Applied sciences) > 621 Applied physics > 621.3 Electrical, magnetic, optical, communications, computer engineering; electronics, lighting > 621.38 Electronics, communications engineering > 621.381 Electronics |
| Divisions: | Fakultas Teknik > Teknik Elektro |
| Depositing User: | Endang Susworini |
| Date Deposited: | 26 Sep 2023 04:24 |
| Last Modified: | 26 Sep 2023 04:24 |
| URI: | http://repository.ub.ac.id/id/eprint/203310 |
![[thumbnail of DALAM MASA EMBARGO]](http://repository.ub.ac.id/style/images/fileicons/text.png) |
Text (DALAM MASA EMBARGO)
Faisal Shidqi.pdf Restricted to Registered users only until 31 December 2025. Download (5MB) |
Actions (login required)
 |
View Item |