Pengaruh Penggunaan Silica Fume dan Semen Slag sebagai Material Substitusi Semen terhadap Kuat Tekan Beton Recycled Coarse Aggregate dengan Menggunakan Destructive Test dan Non-Destructive Test.

Khoirunisa, Fairuz and Ir. Christin Remayanti N, ST., MT and Dr. Eng. Ir. Indradi Wijatmiko,, ST., M.Eng. (Pract) (2023) Pengaruh Penggunaan Silica Fume dan Semen Slag sebagai Material Substitusi Semen terhadap Kuat Tekan Beton Recycled Coarse Aggregate dengan Menggunakan Destructive Test dan Non-Destructive Test. Sarjana thesis, Universitas Brawijaya.

Abstract

Limbah beton yang terus meningkat dan dibiarkan di lingkungan nantinya akan menyebabkan suatu kerusakan bagi lingkungan, hal tersebut dsebabkan limbah pembangunan dan pembongkaran yang umumnya terdiri dari material inert yang dapat menyebabkan pencemaran air tanah. Selain itu, limbah B3 yang setiap tahunnya terus mengalami peningkatan juga dapat membahayakan Kesehatan dan kelangsungan hidup manusia dan makhluk hidup yang lainnya. Untuk itu diperlukan suatu upaya pemerintah dalam menerapkan konsep Green Construction untuk mendukung tujuan pembangunan berkelanjutan atau Sustainable Development Goals (SDGs). Dimana inovasi yang dapat dilakukan untuk mendukung tercapainya SDGs 2030 adalah penggunaan agregat kasar daur ulang serta limbah B3, seperti Silica Fume dan Semen Slag dalam suatu campuran beton. Penelitian dilakukan dengan menggunakan variasi penggunaan RCA 50% dan 100% terhadap berat agregat kasar alam dengan varisi Silica Fume sebesar 0%, 5%, 10%, dan 15% dan variasi Semen Slag sebesar 0%, 10%, 20%, dan 30% terhadap berat semen. Metode pelaksanaan pembuatan beton dilakukan sama dengan beton biasa dengan proses pengujian slump pada saat beton masih dalam keadaan segar yang kemudian akan dilanjutkan dengan perawatan benda uji selama 7 hari. Pengujian dengan menggunakan metode Non-Desteuctive Test (HT dan UPV) dan Destructive Test (CT) akan dilakukan pada saat beton berumur 28 hari dengan hasil pengujian yang akan diolah dengan menggunakan model formula matematik penelitian terdahulu dan Sonic Rebound (SONREB) untuk mendapatkan kuat tekan perkiraan yang mempunyai tingkat akurasi yang tinggi. Penggunaan Silica Fume dan Semen Slag secara umum dapat meningkatkan nilai rebound number, cepat rambat gelombang, dan kuat tekan pada beton RCA 50% dan beton RCA100%. Akan tetapi, hal tersebut tidak sejalan dengan hasil pengujian Silica Fume pada beton RCA 50% yang mengalami penurunan signifikan pada data hasil pengujian Compressive Sterngth Test sebesar 23%. Setelah data hasil pengujian melalui proses pengolahan data menggunakan model formula matematik dan SONREB didapatkan kesimpulan bahwasannya penggunaan metode SONREB memberikan hasil kuat tekan xii perkiraan yang memiliki tingkat akurasi yang lebih tinggi dibandingan model formula matematik.

English Abstract

The increasing amount of concrete waste left in the environment will eventually cause environmental damage. This is due to the waste generated from construction and demolition, which mostly consists of inert materials that can contaminate groundwater. Additionally, the annually increasing hazardous waste, known as B3 waste, can also pose risks to human health and the survival of other living organisms. Therefore, government efforts are needed to implement the concept of Green Construction to support sustainable development goals (SDGs). One of the innovations that can be done to achieve SDGs 2030 is the use of recycledd coarse aggregates and B3 waste, such as Silica Fume and Slag Cement, in a concrete mixture. The research was conducted by using variations of 50% and 100% Recycledd Coarse Aggregate (RCA) compared to the weight of natural coarse aggregates, with variations of Silica Fume at 0%, 5%, 10%, and 15%, and variations of Slag Cement at 0%, 10%, 20%, and 30% in relation to the weight of cement. The concrete production process followed the same procedure as regular concrete, including slump testing when the concrete was still fresh, followed by curing the specimens for 7 days. Testing was performed using Non-Destructive Test methods (HT and UPV) and Destructive Test (CT) on the 28-day-old concrete, and the test results were processed using mathematical formulas from previous studies and the Sonic Rebound (SONREB) method to obtain estimated compressive strength with high accuracy. In general, the use of Silica Fume and Slag Cement can increase the rebound number, wave velocity, and compressive strength of both 50% RCA concrete and 100% RCA concrete. However, this is not consistent with the test results of Silica Fume on 50% RCA concrete, which showed a significant decrease in compressive strength test data by 23%. After processing the test data using mathematical formulas and SONREB, it was concluded that the SONREB method provides estimated compressive strength results with higher accuracy compared to the mathematical formula model.

Other obstract

-

Item Type: Thesis (Sarjana)
Identification Number: 0523070226
Uncontrolled Keywords: Silica Fume, Semen Slag, Destructive Test, Non-Destructive Test, SONREB
Subjects: 600 Technology (Applied sciences) > 624 Civil engineering
Divisions: Fakultas Teknik > Teknik Sipil
Depositing User: Endang Susworini
Date Deposited: 26 Sep 2023 04:11
Last Modified: 26 Sep 2023 04:11
URI: http://repository.ub.ac.id/id/eprint/203309
[thumbnail of DALAM MASA EMBARGO] Text (DALAM MASA EMBARGO)
Fairuz Khoirunisa.pdf
Restricted to Registered users only until 31 December 2025.
Download (4MB)

Actions (login required)

View Item View Item