Abstract
Penggunaan bahan bakar minyak untuk moda transportasi terus mengalami peningkatan seiring dengan penurunan ekplorasi dan produksi minyak bumi. Indonesia menyumbang 57 % CPO dunia, yang mana saat ini Indonesia merupakan salah satu eksportir terbesar minyak kelapa sawit. Upaya untuk meningkatkan kinerja biofuel adalah melalui reaksi perengkahan menggunakan katalis atau biasa disebut perengkahan katalitik. Reaksi perengkahan katalitik adalah reaksi di mana molekul hidrokarbon besar pecah menjadi molekul hidrokarbon yang lebih kecil menggunakan katalis. Salah satu material yang berpotensi digunakan sebagai katalis adalah zeolit. Pada Penelitian kali ini dilakukan secara eksperimental secara langsung. Penelitian ini dilakukan perengkahan katalitik menggunakan H-Zeolite sebagai katalis dan palm oil methyl ester, dengan suhu reaksi 50 ºC, 75 ºC, 100 ºC, 125 ºC, 150 ºC. Proses penelitian melewati beberapa proses antara lain aktivasi zeolit menggunakan HCl yang dilakukan unutk menambah keasaman zeolit guna meningkatkan kemampuannya sebagai pendonor proton Browsted-Lowry, Pemanasan dengan waktu penahanan selama 30 menit, kemudian dianalisa sifat fisiknya meliputi densitas, viskositas, flashpoint, nilai kalor. Hasil perengkahan katalitik POME menggunakan katalis zeolit teraktivasi membentuk rantai pendek dari rantai panjang metil ester C-CH3 menjadi C-C pada gelombang 771,58 cm-1, absorbansi yang diserap juga menunjukkan semakin banyaknya rantai C-C yang dihasilkan akibat perengkahan katalitik. Karakteristik fisik mengalami perubahan seiring bertambahnya suhu. Nilai densitas, viskositas, dan flashpoint mengalami penurunan.
English Abstract
The use of fuel oil for transportation modes continues to increase in line with the decline in petroleum exploration and production. Indonesia contributes 57% of the world's CPO, which is currently one of the largest exporters of palm oil. Efforts to improve biofuel performance are through cracking reactions using catalysts or commonly called catalytic cracking. A catalytic cracking reaction is one in which large hydrocarbon molecules break down into smaller hydrocarbon molecules using a catalyst. One material that has the potential to be used as a catalyst is zeolite. This research was conducted experimentally directly. This research was carried out catalytic cracking using H-Zeolite as catalyst and palm oil methyl ester, with reaction temperatures of 50 ºC, 75 ºC, 100 ºC, 125 ºC, 150 ºC. The research process went through several processes, including zeolite activation using HCl which was carried out to increase the acidity of zeolite to increase its ability as a Browsted-Lowry proton donor , Heating with a holding time of 30 minutes, then analyzed its physical properties including density, viscosity, flashpoint, calorific value. The results of POME catalytic cracking using activated zeolite catalysts form short chains from long chains of methyl ester C-CH3 to C-C at waves 771.58 cm-1, the absorbed absorbance also shows the increasing number of C-C chains produced due to catalytic cracking. Physical characteristics change with increasing temperature. Density, viscosity, and flashpoint values decrease.
Other obstract
-
| Item Type: | Thesis (Sarjana) |
|---|---|
| Identification Number: | 0523070172 |
| Uncontrolled Keywords: | Perengkahan, Karakteristik Bahan bakar, POME, Minyak Sawit, Zeolit. |
| Subjects: | 600 Technology (Applied sciences) > 621 Applied physics > 621.8 Machine engineering |
| Divisions: | Fakultas Teknik > Teknik Mesin |
| Depositing User: | Endang Susworini |
| Date Deposited: | 22 Sep 2023 01:09 |
| Last Modified: | 22 Sep 2023 01:09 |
| URI: | http://repository.ub.ac.id/id/eprint/203136 |
![[thumbnail of DALAM MASA EMBARGO]](http://repository.ub.ac.id/style/images/fileicons/text.png) |
Text (DALAM MASA EMBARGO)
Amelia Syamsiananisa.pdf Restricted to Registered users only until 31 December 2025. Download (11MB) |
Actions (login required)
 |
View Item |